Three-component composite yarn and yarn forming method thereof

A composite yarn, three-component technology, applied in the field of fabric fibers, can solve the problems of low versatility of fabrics, no double elastic modulus, etc., and achieve the effect of improving fluffy effect and improving tightness.

Inactive Publication Date: 2011-01-12
JIAXING UNIV
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a dual modulus triple that can not only meet the requirements of small deformation, but also meet the requirements of large deformation, and improve the tightness, shape retention and comfort of clothing. Component composite yarn to overcome the problem that the existing composite yarn does not have a double modulus of elasticity, so that the fabrics made are not very versatile for clothing making

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Three-component composite yarn and yarn forming method thereof
  • Three-component composite yarn and yarn forming method thereof
  • Three-component composite yarn and yarn forming method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0020] Example Manufacture of Composite Yarn

[0021] Combined with ZL02104397.3, on the FA506 ring spinning machine, the staple fiber strands as the outsourcing fibers are fed to the cradle drafting mechanism through the bell mouth of the machine for drafting, and the network yarns (PET DTY77dtex / 36f+PU 44dtex / 1f) is drawn out from the filament unwinding device, filament tension control device and filament positioning guide device, and then fed into the nip of the front roller from the rear of the front roller. twisting zone. Before entering the composite twisting zone, the tension of the filament is controlled by a specific tension device, so that the tension value of the filament is kept stable and within a reasonable range during spinning; at the same time, the filament is controlled by a positioning guide device to be aligned with the center of the staple fiber. Entering the twisting triangle area ensures the coaxial composite twisting of staple fiber strands and filamen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides three-component composite yarn which is formed by combined machining of 5%-30% of inner-layer core yarn and 70%-95% of outer-layer chopped fiber based on weight ratio via a ring spinning frame, wherein, the inner-layer core yarn of the composite yarn is formed by air texturing and machining of polyester filament yarn or polyamide filament yarn and polyurethane. The composite yarn of the invention has double modulus of elasticity and can improve generality of materials on garment after being made into fabrics, thus meeting the requirement for the modulus of elasticity in case of small deformation as well as the requirements for the modulus of elasticity and shape recovery ratio in case of large deformation, and improving close-fitting property, shape retention property and comfort while wearing clothes.

Description

technical field [0001] The invention relates to a fabric fiber, in particular to a three-component composite yarn and a yarn forming method. Background technique [0002] Composite yarns made of a variety of fibers have been used in the current textile industry, and there are many types. According to the various fiber types that make up the composite yarn, these composite yarns can be roughly divided into: composite yarns composed of short fibers and short fibers, composite yarns composed of chemical fiber filaments and short fibers, and composite yarns composed of chemical fiber filaments and chemical fiber filaments. Three categories of yarn. At present, more composite yarns are generally made of chemical fiber filaments as the core yarn, and a composite yarn with a unique structure formed by outsourcing various short fibers. The commonly used chemical fiber filaments for its core yarn include polyester filaments, nylon filaments, spandex filaments, etc. Outsourced shor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/36D02G3/04D02G3/32
Inventor 薛元
Owner JIAXING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap