Automotive glass antifogging agent and preparation method thereof

A technology of automobile glass and anti-fog agent, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of poor anti-fog effect, poor anti-fog effect, short anti-fog time, etc., and achieve excellent anti-fog function , Enhanced stain resistance and wide application range

Inactive Publication Date: 2011-01-26
梁承忠
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used glass anti-fog agents are generally composed of surfactants, alcohol solvents or ether solvents. The anti-fog time is generally 1-2 days, and the anti-fog time is short. In addition, the anti-fog effect is not very good. , when encountering heavy fog or severe cold weather, the anti-fog effect will be poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Automotive glass antifogging agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Prepare 100kg of automobile glass antifogging agent, the consumption of each raw material is as follows:

[0028] Methyl trifluoropropyl silicone oil 2kg,

[0029] Volatile perfluorinated oil 2kg,

[0030] Oleic acid 2kg,

[0031] 1,5 pentanediol 2kg,

[0032] Tween-80 2kg,

[0033] The balance is water.

[0034] The preparation method is as follows:

[0035] (1) Dissolve 2kg Tween-80 in 90kg water and stir until it becomes a uniform liquid;

[0036] (2) Mix 2kg volatile perfluorinated oil, 2kg oleic acid and 2kg methyltrifluoropropyl silicone oil, and stir until it becomes a uniform liquid;

[0037] (3) Slowly pour the liquid in step (2) into the liquid in step (1), and stir until it becomes a uniform liquid;

[0038] (4) Pour 2kg of 1,5-pentanediol into the liquid in step (3), and stir evenly to obtain the anti-fogging agent for automobile glass.

Embodiment 2

[0040] Prepare 100kg of automobile glass antifogging agent, the consumption of each raw material is as follows:

[0041] Methyl trifluoropropyl silicone oil 5kg,

[0042] Volatile perfluorinated oil 5kg,

[0043] Oleic acid 5kg,

[0044] 1,5 pentanediol 5kg,

[0045] Tween-80 5kg,

[0046] The balance is water.

[0047] The preparation method is as follows:

[0048] (1) Dissolve 5kg Tween-80 in 75kg water and stir until it becomes a uniform liquid;

[0049] (2) Mix 5kg volatile perfluorinated oil, 5kg oleic acid and 5kg methyltrifluoropropyl silicone oil, and stir until it becomes a uniform liquid;

[0050] (3) Slowly pour the liquid in step (2) into the liquid in step (1), and stir until it becomes a uniform liquid;

[0051] (4) Pour 5kg of 1,5-pentanediol into the liquid in step (3), and stir evenly to obtain the anti-fogging agent for automobile glass.

[0052] The anti-fogging agent of the present invention can be directly sprayed on the automobile glass, and then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of glass antifogging agents, in particular to an automotive glass antifogging agent and a preparation method thereof. The automotive glass antifogging agent consists of the following raw materials in percentage by weight: 2 to 5 percent of methyl trifluoropropyl silicon oil, 2 to 5 percent of volatile perfluoro-oil, 2 to 5 percent of oleic acid, 2 to 5 percent of 1,5-pentanediol, 2 to 5 percent of tween-80, and the balance of water. The automotive glass antifogging agent is prepared by the following steps of: (1) dissolving the tween-80 in the water, and stirring the mixture; (2) mixing the volatile perfluoro-oil, the oleic acid and the methyl trifluoropropyl silicon oil together, and uniformly stirring the mixture; (3) pouring the liquid of the step (2) into the liquid of the step (1), and uniformly stirring the mixture; (4) pouring the 1,5-pentanediol into the liquid of the step (3), and uniformly stirring the mixture. The introduction of fluorine ensures that the antifogging agent has excellent hydrophobicity and an antifogging function, the antifogging time is prolonged, and the antifogging effect is improved; furthermore, the automotive glass antifogging agent has no side effect on human bodies, and has the functions of preventing rain, cleaning glass and protecting a wiper after the automotive glass antifogging agent is coated on external glass and a back view mirror of an automobile.

Description

technical field [0001] The invention relates to the field of antifogging agents for glass, in particular to an antifogging agent for automobile glass, and also relates to a preparation method of the antifogging agent. Background technique [0002] One of the headaches for car owners in winter is that the glass inside the car is often covered by fog, which seriously hinders driving safety. The currently used glass anti-fog agents are generally composed of surfactants, alcohol solvents or ether solvents. The anti-fog time is generally 1-2 days, and the anti-fog time is short. In addition, the anti-fog effect is not very good. , When encountering heavy fog or severe cold weather, the anti-fog effect will be poor. Contents of the invention [0003] In order to overcome the deficiencies in the above technologies, the present invention provides an antifogging agent for automobile glass with good antifogging effect and long antifogging time. [0004] The invention also provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K3/18
Inventor 李竹君
Owner 梁承忠
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com