Polypropylene (PP) spun-bonded nonwoven fabric fully-degradable composite material and preparation method thereof

A technology of spun-bonded non-woven fabrics and composite materials, applied in the direction of single-component polyolefin artificial filaments, etc., can solve the problems of non-compliance with environmental protection requirements, poor performance such as burst resistance, and inability to achieve full degradation. Good spinnability, good surface gloss, good coloring performance

Inactive Publication Date: 2013-09-11
佛山市衡龙科技有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing technology, the composite material combined with PP spunbonded non-woven fabric cannot be fully degraded, does not meet the requirements of environmental protection, and has poor tensile, tearing, bursting and other properties, which is difficult to meet people's production needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] A kind of PP spunbond non-woven fully degradable composite material of the present invention, it is mainly made of cornstarch, polyvinyl alcohol, glycerin and organic montmorillonite, the weight ratio of cornstarch, polyvinyl alcohol, glycerin and organic montmorillonite (55-65): (15-25): (13-18): (3-8); wherein, the weight ratio of corn starch, polyvinyl alcohol, glycerin and organic montmorillonite is preferably 60:20:15: 5. The particle size of heavy calcium carbonate is 2500 mesh, and the particle size of corn starch is 2000 mesh.

[0023] PP spunbonded non-woven fully degradable composite material, its process steps are as follows:

[0024] 1. First, mix the cornstarch in a horizontal high-speed mixer for 30 minutes at medium speed to achieve the effect of mixing and drying, and the water content is <2%;

[0025] 2. Add polyvinyl alcohol, mix at high speed for 10 minutes, and distribute and mix the components evenly;

[0026] 3. The mixed material is transported...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene (PP) spun-bonded nonwoven fabric fully-degradable composite material and a preparation method thereof. The PP spun-bonded nonwoven fabric fully-degradable composite material is characterized by being mainly prepared from corn starch, polyvinyl alcohol, glycerol and organic montmorillonite according to a weight ratio of (55-65):(15-25):(13-18):(3-8). The PP spun-bonded nonwoven fabric fully-degradable composite material has the advantages of good filtration performance, good spinnability, no slurry dropping, good colorability, uniform lapping, normal gram weight, good tensile strength and flexibility, good surface luster and good popularization value.

Description

technical field [0001] The invention relates to the technical field of PP spun-bonded non-woven fabrics, and more specifically relates to a PP spun-bonded non-woven fabric composite material and a process. Background technique [0002] The quality and performance of meltblown nonwovens depends on the correct selection of polypropylene raw material (melt index) and the optimization of processing conditions. At present, meltblown manufacturers mainly use high-melting polypropylene raw materials, but they lack the necessary flexibility to adapt to different market demands, and there is also the pressure of high costs. In this case, high-quality melt-blown non-woven fabrics can be produced by using low-melt index spun-bonded polypropylene raw materials (MFI=20-50), combined with plastic additives using "chain breaking technology", for Meltblown manufacturers provide more flexible operating space. At present, PP spunbonded non-woven fabrics are made of PP polypropylene raw mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L3/02C08L29/04C08K13/06C08K9/04C08K3/34C08K5/053B29B9/06D01F6/46D01F1/10
Inventor 冯建强
Owner 佛山市衡龙科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap