Method for preparing high-purity fused silica by recovering waste quartz crucible

A quartz crucible and fused silica technology, which is applied in the field of fused silica material preparation, can solve the problems of difficulty in guaranteeing the purity of fused silica, different grades of raw quartz ore, and large differences in impurity content, and is beneficial to the protection and solution of land resources. Pollution and emission problems, the effect of realizing recycling

Inactive Publication Date: 2012-07-11
徐州协鑫太阳能材料有限公司
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the grades of raw quartz ore vary greatly across the country, and the impurity content ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The method for recovering waste quartz crucibles to produce high-purity fused silica in this embodiment includes steps such as crushing and classification, pickling to remove impurities, water washing and drying, and amorphization treatment. The specific methods of each step are as follows.

[0026] Broken classification:

[0027] Using scrap crucibles manufactured by quartz crucibles and / or used by polysilicon ingot casting enterprises as raw materials, mechanical crushing and vibration screening are carried out to make blocks of 1-50 mm.

[0028] Pickling and impurity removal:

[0029] The block is pickled with mixed acid, the concentration of the mixed acid is 1-25% (weight ratio), the weight ratio of the block to the mixed acid is 1:1-5, and the pickling time is 4-200 hours.

[0030] Preferably, the mixed acid is a binary mixed acid of oxalic acid and hydrochloric acid or a ternary mixed acid of hydrofluoric acid, oxalic acid and hydrochloric acid; The weight rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing high-purity fused silica by recovering waste quartz crucible, which comprises steps of smash classification, scouring edulcoration, washing stoving and amorphization treatment and the like. The high-purity fused silica meeting use requirements of the quartz crucible can be obtained through that fact that purification edulcoration and the amorphization treatment are carried out on quartz crucible waste, so that excessive depending on quartz raw ore can be obviously remitted, cyclic utilization of quartz sands can be achieved, the method is applicable to protection of territorial resources, greatly reduces cost of manufacture of quartz ceramic crucible, simultaneously solves contamination and discharge problems of solid waste of quartz crucible production and using enterprises.

Description

【Technical field】 [0001] The invention relates to a method for preparing fused silica material, in particular to a method for recovering waste quartz crucibles to prepare high-purity fused silica. 【Background technique】 [0002] In recent years, with the continuous attention and development of environmental protection energy, solar energy as a green energy has been widely valued by countries all over the world, and has been widely developed and utilized. develop. Fused quartz ceramic crucible is a container used to load polysilicon raw materials in the process of solar polysilicon ingot casting, and melt and crystallize it at a high temperature of 1550°C to produce polysilicon ingots. It must work continuously for more than 50 hours at one time, and the whole process cannot be broken. , the crucible components can not cause pollution to the silicon material, and it is an irreplaceable key consumable part in the production process of polysilicon ingots. With the expansion o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03B5/16C03C6/04
Inventor 何钊煊王金波孙前颂
Owner 徐州协鑫太阳能材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap