Olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same

An olefin deoxidizer, olefin technology, applied in the direction of chemical change purification/separation, organic chemistry, etc., can solve the problems of low deoxidation capacity and short service life, and achieve high deoxidation capacity, high mechanical crushing strength, and emission reduction. Effect

Active Publication Date: 2014-11-05
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The purpose of the present invention is to provide a new olefin deoxidizer, its preparation method and application, and an olefin deoxygenation method in order to overcome the defects of low deoxidation capacity and short service life of the existing olefin deoxidizer at room temperature (25° C.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] On the one hand, the invention provides a kind of preparation method of olefin deoxidizer, described method comprises the following steps:

[0024] (1) Manganese source, nano TiO 2 Mix with the binder to obtain a mixture, respectively, Mn 3 o 4 , Nanoscale TiO 2 and binder, based on 100 parts by weight of the manganese source, nanoscale TiO 2 The dosage is 58-100 parts by weight, the binder is 1.5-25 parts by weight, and the manganese source is Mn 3 o 4 And / or can get Mn after roasting 3 o 4 manganese compounds;

[0025] (2) The mixture obtained in step (1) is impregnated with an equal volume of aqueous solution of a silver compound, then kneaded and molded, and Mn 3 o 4 and Ag 2 In terms of O, based on 100 parts by weight of the manganese source, the aqueous solution of the compound of silver is 8-35 parts by weight, and the compound of silver can be decomposed to obtain Ag after roasting. 2 O water-soluble silver compounds;

[0026] (3) aging the product f...

Embodiment 1

[0059] This example is used to illustrate the preparation method of the olefin deoxidizer provided by the present invention.

[0060] MnCO with an average particle size of 35 μm 3, with an average particle size of 9.8nm and a specific surface area of ​​160m 2 / g anatase TiO 2 , and the cement with an average particle size of 35 μm is mixed evenly. MnCO 3 、TiO 2 and the amount of cement so that the Mn 3 o 4 、TiO 2 and cement meter, based on 1000g of MnCO 3 ,TiO 2 650g, cement 200g, add AgNO 3 solution for equal volume impregnation, AgNO 3 The concentration and amount of the solution make the Mn 3 o 4 and Ag 2 O meter, based on 1000g of MnCO 3 , AgNO 3 The solution is 300g, fully kneaded, and prepared into strips with a diameter of Φ3mm and a length of 5mm with an extruder, and then placed in a sealed place for 48h, then dried at 120°C for 10h, and then roasted at 480°C for 5h to prepare an olefin deoxidizer. The deoxygenation capacity, deoxidation depth and mech...

Embodiment 2

[0062] This example is used to illustrate the preparation method of the olefin deoxidizer provided by the present invention.

[0063] MnCO with an average particle size of 20 μm 3 , with an average particle size of 5nm and a specific surface area of ​​200m 2 / g anatase TiO 2 , and the cement with an average particle size of 20 μm is mixed evenly. MnCO 3 、TiO 2 and the amount of cement so that the Mn 3 o 4 、TiO 2 and cement meter, based on 1000g of MnCO 3 ,TiO 2 580g of cement, 150g of cement, put the blended material evenly into the sugar coating machine, spray AgNO 3 solution for equal volume impregnation, AgNO 3 The concentration and amount of the solution make the Mn 3 o 4 and Ag 2 O meter, based on 1000g of MnCO 3 , AgNO 3 The solution is 350g, rolled into a spherical shape of Φ3mm, and then placed in a sealed place for 60h, then dried at 140°C for 8h, and then calcined at 500°C for 2h to prepare an olefin deoxidizer. The deoxygenation capacity, deoxidation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an olefin deoxygenation agent, its preparation method, and olefin deoxygenation method using the same. The preparation method includes (by weight parts) (1) mixing manganese source (as Mn3O4) 100, titania nanoparticle 58-100 and binder 1.5-25 to obtain a mixture; (2) kneading the mixture and a silver compound (as Ag2O) aqueous solution 8-35, and forming; (3) aging and drying; and (4) calcining. The inventive olefin deoxygenation agent has high room-temperature deoxygenation capacity up to 24.8 mL / g, high mechanical crushing strength up to 89 N / cm, deoxygenation depth smaller than 0.01 ppm, low reduction temperature, and wide applicability in industrial production.

Description

technical field [0001] The invention relates to a preparation method of an olefin deoxidizer, an olefin deoxidizer prepared by the preparation method, an application of the olefin deoxidizer and an olefin deoxygenation method. Background technique [0002] Olefins are important basic organic chemical raw materials. Among them, ethylene and propylene are the main raw materials for the production of polymer materials. With the rapid development of polyethylene and polypropylene technology, various new high-efficiency polyethylene, polypropylene catalysts and metallocene catalysts have been applied to industrial production. In order to avoid poisoning and deactivation of such high-efficiency polyolefin catalysts and improve product quality, there are strict restrictions on the impurity content of ethylene and propylene raw materials used for polymerization. According to the national standard for ethylene and propylene raw materials, the oxygen content in qualified polymer gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C7/148C07C11/04C07C11/06
Inventor 吕顺丰李彤黄凤兴刘博王世亮秦燕璜张秀英
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More