Glaze material of high temperature fast firing crystal glaze archaized brick and preparation process thereof

A preparation process, technology of antique bricks, applied in the field of crystalline glaze, can solve the problems of restricting commercial production, complex process conditions, high cost, etc., and achieve the effects of reducing firing costs, strong operability, and fewer types

Active Publication Date: 2014-03-12
FOSHAN DOWSTONG TECH
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the development of crystalline glazed antique bricks of architectural ceramics is still rare. The main reason is that the traditional crystalline glaze has defects such as complex process conditions and high costs, which limit its commercial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glaze material of high temperature fast firing crystal glaze archaized brick and preparation process thereof
  • Glaze material of high temperature fast firing crystal glaze archaized brick and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] A preparation process of crystalline glaze antique brick, comprising the following steps:

[0034] 1) Preparation of crystal-based glaze: mix the raw materials of crystal-based glaze in proportion; add binder and debonding agent, mix well to obtain a mixture; add water to the mixture, ball mill it into a glaze slurry, and obtain a crystal-based glaze;

[0035] 2) Preparation of the crystallization agent: mix the raw materials of the crystallization agent in proportion, burn them into a frit, and break the frit to obtain the crystallization agent;

[0036] 3) Glazing: apply the crystalline base glaze on the surface of the brick, and then apply the crystallization agent on the crystalline base glaze;

[0037] 4) Firing: firing in a kiln, firing at 1150-1230°C for 50-60 minutes, to obtain crystal glazed antique bricks with crystal flower artistic effect;

[0038] Wherein, the glaze used is the above-mentioned glaze.

[0039] Preferably, the amount of the binder is 0.2-0....

Embodiment 1

[0049] (1) Preparation of crystalline base glaze

[0050] 1) Weigh raw materials of crystalline base glaze: 30 parts of albite, 20 parts of quartz, 10 parts of titanium dioxide, 30 parts of wollastonite, 5 parts of kaolin, 25 parts of zinc oxide, 1 part of copper oxide, and mix well;

[0051] 2) Add its mass 0.25% CMC and 0.3% sodium tripolyphosphate in the raw material, mix to obtain the mixture;

[0052] 3) Add 50-70% of the mass of water to the mixture, ball mill it into a glaze slurry, control the fineness of the glaze slurry to 325 mesh, and obtain a crystal-based glaze suitable for crystal formation and growth.

[0053] (2) Preparation of crystallization agent

[0054] 1) Weigh raw materials of crystallization agent: 22 parts of albite, 20 parts of quartz, 20 parts of titanium dioxide, 10 parts of lithium carbonate, 10 parts of boric acid, 2 parts of soda ash, 8 parts of zirconium silicate, 8 parts of zinc oxide, and 2 parts of limestone , pulverized and mixed;

[0055]...

Embodiment 2

[0064] (1) Preparation of crystalline base glaze

[0065] 1) Weigh raw materials of crystalline base glaze: 24 parts of albite, 20 parts of quartz, 5 parts of titanium dioxide, 20 parts of wollastonite, 10 parts of kaolin, 20 parts of zinc oxide, 2 parts of cobalt oxide, and mix well;

[0066] 2) Add its mass 0.2% CMC and 0.3% sodium tripolyphosphate in the mixed raw material, mix to obtain the mixed material;

[0067] 3) Add 50-70% of the mass of water into the mixture, ball mill it into a glaze slurry, control the fineness of the glaze slurry to 325 mesh, and obtain a crystal-based glaze suitable for crystal formation and growth.

[0068] (2) Preparation of crystallization agent

[0069] 1) Weigh raw materials of crystallization agent: 15 parts of albite, 20 parts of quartz, 22 parts of titanium dioxide, 5 parts of zirconium silicate, 8 parts of zinc oxide, 10 parts of lithium carbonate, 5 parts of boric acid, 2 parts of soda ash, and 2 parts of limestone , 2 parts of coba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glaze material of a high temperature fast firing crystal glaze archaized brick and preparation process thereof. Raw material types of crystal glaze are few and wide in sources. A preparation method of the crystal glaze archaized brick is simple, traditional crystal glaze complex process and specific firing rules are broken through, the crystal glaze archaized brick can be obtained through once firing, operability is good, energy is saved, environment is protected, and firing cost is reduced. By adjusting proportion of glaze material components and colorants and the process method, crystal glaze with different colors and crystal flowers in different sizes are obtained through firing, glaze is light, a few needle holes exist occasionally, and firing yield reaches more than 92%.

Description

Technical field [0001] The invention is a crystalline glaze field, which specializes in a glaze and preparation process of high -temperature fast -burning crystalline glaze antique bricks. Background technique [0002] Crystal glaze is a very decorative artistic glaze. It enjoys a wide reputation with its unique artistic style and has the favor of consumers.In recent years, many ceramic producing areas in my country have successfully carried out the trial production of crystal glaze. The crystal glaze decoration has been widely tried on furnishing porcelain, daily utensils, and wall tiles, and has achieved gratifying results.However, the development of antique bricks of Ceramics Crystal glaze is still rare, mainly due to the complexity and high cost of traditional crystalline glaze, which limits its commercial production. [0003] The crystal range of the crystal glaze is very narrow, and the condition of firing is harsh. It is necessary to strictly control the heating speed and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86
Inventor 余水林曾青蓉
Owner FOSHAN DOWSTONG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More