Al-Fe-Ga-RE aluminum alloy, and preparation method and power cable thereof

A power cable and aluminum alloy technology, applied in the field of alloys, can solve problems such as poor fatigue resistance, quality problems, poor comprehensive performance of aluminum alloy power cables, etc.

Active Publication Date: 2013-03-20
ANHUI JOY SENSE CABLE
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The aluminum alloy conductor materials in the prior art are relatively excellent in electrical properties, corrosion resistance and mechanical properties, etc., but are still relatively poor in fatigue resistance, which is prone to quality problems and affects the service life or band of the aluminum alloy material. Therefore, the overall performance of aluminum alloy power cables is still poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al-Fe-Ga-RE aluminum alloy, and preparation method and power cable thereof
  • Al-Fe-Ga-RE aluminum alloy, and preparation method and power cable thereof
  • Al-Fe-Ga-RE aluminum alloy, and preparation method and power cable thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The present invention also provides a method for preparing an Al-Fe-Ga-RE aluminum alloy, comprising the following steps:

[0052] a) Cast the raw materials of the following composition to obtain an aluminum alloy ingot: 0.01~1.6wt% Fe, 0.001~0.3wt% Cu, 0.001~0.3wt% Mg, 0.001~0.3wt% Co, 0.001~0.2 wt% Be, 0.001~0.3wt% Ca, 0.001~0.2wt% Zn, 0.001~0.3wt% Sr, 0.001~0.3wt% Zr, 0.002~0.25wt% Li, 0.001~0.2wt% Na, 0.002~0.25wt% K, 0.001~0.2wt% Ti, 0.001~0.15wt% V, 0.001~0.12wt% Cr, 0.001~0.12wt% Mn, 0.001~0.15wt% Ni , 0.001~0.2wt% of Ga, 0.01~3.0wt% of RE, greater than zero and less than or equal to 0.2wt% of Si, greater than zero and less than or equal to 0.8wt% of B and the balance of aluminum;

[0053] b) performing homogenization treatment on the aluminum alloy ingot, and rolling the homogenized aluminum alloy ingot to obtain an aluminum alloy rod;

[0054] c) subjecting the aluminum alloy rod obtained in step b) to batch annealing treatment;

[0055] d) performing aging ...

Embodiment 1

[0065] (1) Put the aluminum ingot into the furnace, heat it to melt and keep it warm at 720°C. The melting process is completed in a sealed environment; first add Fe, Cu, Mg, Co, Be, Ca, Zn, Sr, Zr, Si , B, Li, Na, K, Ti, V, Cr, Mn, Ni and Ga pure metals, stir evenly, then add rare earth RE and stir for 20 minutes until fully stirred evenly, and let stand for 30 minutes; then furnace the above alloy melt Internal refining; add refining agent to the alloy melt, stir evenly, and then let it stand for 30 minutes. The melt refining is operated in a sealed environment; After degassing and slag removal, enter the casting machine for casting to obtain aluminum alloy ingots. The ingot composition is listed in Table 1;

[0066] (2) Heat up the aluminum alloy ingot obtained in step (1) at a rate of 5°C / min to 450°C, hold it for 6 hours, and then roll it into a rod;

[0067] (3) Anneal the rod material obtained in step (2) under an inert atmosphere, heat it to 280°C and keep it for 2 ho...

Embodiment 2

[0071] (1) Put the aluminum ingot into the furnace, heat it to melt and keep it warm at 740°C. The melting process is completed in a sealed environment; first add Al-Fe, Al-Cu, Al-Mg, Al-Co, Al-Be , Al-Ca, Al-Zn, Zn-Sr, Al-Zr, Al-Si, Al-B, Al-Li, Al-Na, Al-K, Al-Ti, Al-V, Al-Cr, Al - Mn, Al-Ni and Al-Ga master alloys, stir well, then add rare earth RE and stir for 20 minutes until fully stirred evenly, and keep it for 30 minutes; then refine the above alloy melt in the furnace; add refining to the alloy melt and stir evenly, and then keep it for 30 minutes. The melt refining is operated in a sealed environment; Enter the casting machine for casting to obtain an aluminum alloy ingot, and the ingot composition is listed in Table 1;

[0072] (2) Heat up the aluminum alloy ingot obtained in step (1) at a rate of 3°C / min to 550°C, hold it for 16 hours and then roll it into a rod;

[0073] (3) Anneal the rod material obtained in step (2) under an inert atmosphere, heat it to 360°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thermal resistanceaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides an Al-Fe-Ga-RE aluminum alloy, and a preparation method of the Al-Fe-Ga-RE aluminum alloy. The method comprises the steps that: (a) an aluminum alloy ingot is cast; (b) the aluminum alloy ingot is subjected to a homogenization treatment; and the obtained aluminum alloy ingot is rolled, such that an aluminum alloy rod material is obtained; (c) the aluminum alloy rod material obtained in the step (b) is subjected to a batch-type annealing treatment; and (d) the aluminum alloy rod material obtained in the step (c) is subjected to an aging treatment, such that aluminum alloy is obtained. The invention also provides a power cable. According to the invention, through the selection and control over added elements and the adoption of a reasonable preparation process, the obtained aluminum alloy is provided with good comprehensive performance.

Description

technical field [0001] The invention relates to the field of alloy technology, in particular to an Al-Fe-Ga-RE aluminum alloy, a preparation method thereof and a power cable. Background technique [0002] Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and is widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. With the rapid development of science and technology and industrial economy, the demand for aluminum alloys is increasing, and the research on aluminum alloys is also in-depth. The wide application of aluminum alloys has promoted the development of aluminum alloys in the power industry, and at the same time the development of the power industry has expanded the application fields of aluminum alloys. [0003] A power cable is a resource used to transmit and distribute electrical energy, and its basic structure consists of four parts: a core, an insulating layer, a shieldi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C21/02C22C21/08C22C21/10C22C21/18C22F1/04C22F1/043C22F1/047C22F1/05C22F1/053C22F1/057H01B1/02H01B9/02H01B13/00
Inventor 林泽民
Owner ANHUI JOY SENSE CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com