The production process of cupro blended fabric

A technology of blended fabric and production process, applied in the field of textile and clothing, can solve problems such as poor resistance and achieve the effect of good wearing comfort

Active Publication Date: 2015-11-04
江苏成龙服饰科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor resistance of cupro fiber to oxidants such as chlorine bleach and hydrogen peroxide, the fabrics blended with cupro fiber and other fibers have certain difficulties in the subsequent pretreatment, dyeing and finishing processes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment one: a kind of production technology of cupro-ammonia blended fabric comprises the following process steps:

[0015] (1) Cupro ammonia fiber, carbon fiber and cotton fiber are blended to obtain cupro ammonia blended fabric, and the mass ratio of cupro ammonia fiber, carbon fiber and cotton fiber is 40:1.5:58.5

[0016] (2) Washing: Wash the cupro-ammonia blended fabric in a washing machine with a liquor ratio of 1:30 and add a neutral detergent. The amount of detergent used is 3g per liter of water, the water temperature is 60°C, and the washing time is 1 hour. ;

[0017] (3) Scouring: Soak the washed cupro-ammonia blended fabric in water with a liquor ratio of 1:10, and add a neutral scouring agent solution with a concentration of 30% by mass at 5g per liter of water for 0.5 hours , the scouring temperature is 65°C;

[0018] (4) Dyeing: Put the refined cupro ammonia blended fabric into the dyeing machine, the bath ratio of the dye solution is 1:10, add 1g ...

Embodiment 2

[0019] Embodiment two: a kind of production technology of cupro-ammonia blended fabric comprises the following process steps:

[0020] (1) Cupro ammonia fiber, carbon fiber and cotton fiber are blended to obtain cupro ammonia blended fabric, and the mass ratio of cupro ammonia fiber, carbon fiber and cotton fiber is 60:3:58.5;

[0021] (2) Washing: Wash the cupro-ammonia blended gray fabric in a washing machine with a liquor ratio of 1:50 and add a neutral detergent. The amount of detergent used is 5g per liter of water, the water temperature is 65°C, and the washing time is 0.5 hours ;

[0022] (3) Scouring: Soak the washed cupro-ammonia blended gray fabric in water with a liquor ratio of 1:15, and add a neutral scouring agent solution with a concentration of 35% by mass at a rate of 10g per liter of water for 1 hour , the scouring temperature is 70°C;

[0023] (4) Dyeing: Put the scoured cupro ammonia blended fabric into the dyeing machine, the bath ratio of the dye soluti...

Embodiment 3

[0024] Embodiment three: a kind of production technology of cupro-ammonia blended fabric, comprises the following process steps:

[0025] (1) Cupro ammonia fiber, carbon fiber and cotton fiber are blended to obtain cupro ammonia blended fabric, and the mass ratio of cupro ammonia fiber, carbon fiber and cotton fiber is 50:2:50;

[0026] (2) Washing: wash the cupro-ammonia blended fabric in a washing machine with a bath ratio of 1:40, and add a neutral detergent. The amount of cleaning agent is 4g per liter of water, the water temperature is 62°C, and the washing time is 0.6 hours ;

[0027] (3) Scouring: Soak the washed cupro-ammonia blended fabric in water with a liquor ratio of 1:12, and add a neutral scouring agent solution with a concentration of 32% by mass, the amount added is 8g per liter of water, and the treatment is 0.6 hours , the scouring temperature is 66°C;

[0028] (4) Dyeing: Put the refined cupro-ammonia blended fabric into the dyeing machine, the bath ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production process of copper ammonia blend fabric. The production method of copper ammonia blend fabric includes the following craft steps: (1) blending copper ammonia blending grey fabric, carbon fibers and cotton fibers to obtain copper ammonia blend fabric; (2) washing the copper ammonia blending grey fabric in a water washer with a bath ratio of 1 to 30-50 and adding neutral cleaning agents and the temperature is 60 to 65 DEG C; (3) sinking the copper ammonia blend raw fabric which is washed by water in the water with a bate rate of 1 to 10-15, adding neutral refining agent solution with a addition of 5 to 10 grams per liter water, and processing 0.5 to 1 hour with a refining temperature of 65 to 70 DEG C; (4) placing the copper ammonia blend raw fabric which is refined into a dyeing machine and adding softener and levelling agent; (5) rinsing, drying and obtaining the copper ammonia blend fabric. The production method of copper ammonia blend fabric is manufactured by copper ammonia fibers, carbon fibers and cotton fibers does not damage antibiosis performance and meanwhile possesses good comfort.

Description

technical field [0001] The invention relates to a fabric, in particular to a production process of a cupro-ammonia blended fabric, belonging to the technical field of textiles and garments. Background technique [0002] Cupro fiber is a kind of regenerated cellulose fiber. It is made by dissolving natural cellulose raw materials such as cotton linters in a concentrated ammonia solution of copper hydroxide or alkaline copper salt to prepare a spinning solution. Cellulose molecular compounds are decomposed to regenerate cellulose, and the resulting hydrated cellulose can be post-processed to obtain cupro ammonia fiber. The cross-section of cupro ammonia fiber is round, without sheath-core structure, the fiber can withstand a high degree of elongation, and the monofilament produced is relatively thin, so the fabric feels soft, soft and lustrous, with a real silk feel. Due to the poor resistance of cupro fiber to oxidizing agents such as chlorine bleach and hydrogen peroxide, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06B3/10
Inventor 黄振龙
Owner 江苏成龙服饰科技有限公司