Titanium alloy wire production method

A titanium alloy wire and production method technology, applied in the direction of wire drawing dies, etc., can solve the problems of not easy to expose, easy to scratch the surface of the wire, and low yield rate, so as to ensure the dimensional accuracy and surface quality, improve the working site environment, The effect of reducing production costs

Active Publication Date: 2015-07-08
BAOJI TITANIUM IND CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Titanium alloy has unique physical and chemical properties. When titanium alloy wire is hot-drawn, the surface is coated with a layer of graphite emulsion and then heated at 500°C to 800°C before drawing. Not only the production cost is high, but the dimensional accuracy is poor. Moreover, the surface defects of the wire coated with graphite milk are not easy to be exposed, which affects the quality of the finished wire material. At the same time, due to the use of graphite milk for lubrication, the working environment of the hot drawing of titanium alloy wire cannot be effectively improved.
In addition, the cemented carbide mold used, the surface of the wire is easily scratched during drawing, the yield rate is low, and the product quality needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium alloy wire production method
  • Titanium alloy wire production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] combined with figure 1 , 2 An embodiment of the present invention is described: a production method of φ0.5mm TC4 titanium alloy wire.

[0020] Step 1: First, anneal the Φ6.5mm titanium alloy wire billet at an annealing temperature of 750°C to 800°C for 1 hour, then place the annealed Φ6.5mm titanium alloy wire billet on the rack; place the Φ5.7mm, Φ5 The wire drawing dies with a diameter of .0mm are installed in the fourth and fifth mold boxes of the linear wire drawing machine, and calcium-based wire drawing powder or sodium-based wire drawing powder is added into the mold box as a lubricant;

[0021] Step 2: Lead out the Φ6.5mm titanium alloy wire blank through the fourth and fifth wire drawing dies (Φ5.7mm→Φ5.0mm) for continuous cold drawing to make Φ5.0mm titanium alloy wire blank I, and make The titanium alloy wire blank I is annealed; the annealing temperature is 720°C-750°C, and the time is 45-50 minutes; the line speed of the cold drawing is 3 m / min.

[0022...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a titanium alloy wire production method. A titanium alloy wire is prepared by carrying out multi-die continuous cold-drawing on a titanium alloy wire blank by using a polycrystalline wire drawing die or high-crystalline wire drawing die, wherein calcium-based wire drawing powder or sodium-based wire drawing powder is used as a lubricating agent. By using the titanium alloy wire production method, the size precision and the surface quality of a finished product of the titanium alloy wire are ensured, the production efficiency is increased, and the environment of a working site is improved.

Description

technical field [0001] The invention belongs to the technical field of titanium alloy wire processing, and in particular relates to a production method of titanium alloy wire. Background technique [0002] Titanium alloy has unique physical and chemical properties. When titanium alloy wire is hot-drawn, the surface is coated with a layer of graphite emulsion and then heated at 500°C to 800°C before drawing. Not only the production cost is high, but the dimensional accuracy is poor. Moreover, the surface defects of the wire coated with graphite milk are not easy to be exposed, which affects the quality of the finished wire product. At the same time, due to the use of graphite milk for lubrication, the environment of the hot drawing work site of titanium alloy wire cannot be effectively improved. In addition, the cemented carbide mold used makes the wire surface easily scratched during drawing, the yield rate is low, and the product quality needs to be improved. Contents of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C9/02B21C3/02B21C1/04
Inventor 姜斌邵军范珂王鼎春屈征蒋纪新陶海林胥秀霞
Owner BAOJI TITANIUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com