Tempering technology of G18CrMo2-6 steel

A technology of process and process parameters, which is applied in the direction of manufacturing tools, heat treatment equipment, heat treatment process control, etc., can solve the problems of uneven performance, carbide particle growth, etc., and achieve scientific design results, small carbides, and good impact toughness. Effect
CN103436686AActive Publication Date: 2013-12-11INST OF METAL RESEARCH - CHINESE ACAD OF SCI +1
3 Cites 4 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Publication Date
2013-12-11

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention belongs to the field of steel heat treatment, and more specifically relates to a tempering technology of G18CrMo2-6 steel. The tempering technology is capable of solving a problem that impact toughness of G18CrMo2-6 steel is poor, and changes under different tempering treatment conditions. The tempering technology comprises following specific steps: 1) the G18CrMo2-6 steel after normalizing heat treatment is heated to a temperature smaller than Ac1 at a certain heating speed, and is subjected to tempering treatment after different heat preservation periods; and then charpy V-notch impact test is performed so as to obtain test data; 2) the test data is input into a tempering parameter formula for calculation, and a tempering parameter-impact value corresponding curve is drawn; and 3) a reasonable heat treatment technology is determined based on the optimum value in the tempering parameter curve. According to the tempering technology, the heat treatment technology is determined based on the tempering parameter formula of G18CrMo2-6 steel, so that design errors are avoided, the design of the tempering technology is more reasonable, and designed results are scientific and standard.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the field of iron and steel heat treatment, specifically a tempering process for G18CrMo2-6 steel. When formulating the tempering heat treatment process, the method for determining the tempering heating rate, holding temperature, holding time, and cooling rate is used to make the G18CrMo2-6 steel The impact toughness is the best in different processes. Background technique

[0002] G18CrMo2-6 steel is a structural steel with high strength, high plasticity and high toughness. It is one of the commonly used steels for pressure vessels. It is widely used in the manufacture of boilers, steam turbines and gas turbine castings in thermal power plants, such as steam turbine main steam valves and cylinders. , partitions and boiler valve casings, etc.

[0003] G18CrMo2-6 steel has low carbon content, low alloy content, and poor hardenability. After austenitization, the structure obtained under normalizing conditions is ferrite + bainit...