900MPa high-strength welding wire for mining machine and application method

A high-strength, welding wire technology, applied in welding media, welding equipment, welding equipment, etc., can solve the problem of high price, and achieve the effect of reducing price, reducing manufacturing cost, and reducing ductile-brittle transition temperature

Inactive Publication Date: 2014-01-08
山东索力得焊材股份有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, with the improvement of coal mining quality and the increase of coal seam height, the demand for large-scale hydraulic supports (over 7 meters in height) is increasing, and the corresponding high-strength steel plates and high-strength welding wires are also in urgent need of development. Currently, 800MPa High-strength plates Q890, Q900, etc. above grade, the welding wires corresponding to the above-mentioned high-strength plates are mostly imported from abroad, and the price is also very expensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 900MPa high-strength welding wire for mining machine and application method
  • 900MPa high-strength welding wire for mining machine and application method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A kind of 900MPa high-strength welding wire for mining machinery, its composition and mass percentage are as follows:

[0022]

[0023] Below in conjunction with specific examples, the balance is iron and unavoidable impurities.

[0024] 1 2 3 4 5 6 7 8 9 C 0.060 0.110 0.100 0.062 0.070 0.105 0.089 0.090 0.080 Si 0.60 0.90 0.70 0.80 0.65 0.76 0.85 0.78 0.85 mn 1.40 2.00 1.45 1.90 1.85 1.50 1.48 1.78 1.85 Ni 1.40 2.00 1.70 1.00 1.80 1.90 1.56 1.79 1.85 Cr 0.30 0.80 0.70 0.32 0.75 0.45 0.34 0.45 0.50 Mo 0.10 0.40 0.35 0.28 0.24 0.27 0.38 0.15 0.20 Ti 0.16 0.09 0.087 0.086 0.11 0.09 0.15 0.08 0.09 S 0.02 0.010 0.014 0.005 0.007 0.009 0.015 0.012 0.017 P 0.02 0.010 0.020 0.008 0.010 0.013 0.015 0.007 0.004

[0025] The welding wire of the above-mentioned embodiment was welded in 80%Ar+20%CO Argon-rich gas protection, and tested....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a 900MPa high-strength welding wire for a mining machine and an application method. The 900MPa high-strength welding wire is suitable for welding Q890 plates, Q900 plates and other high-strength plates. The gas shielded welding wire comprises the following chemical components, by mass, including 0.06-0.11% of C, 0.60-0.90% of Si, 1.40-2.00% of Mn, 1.4-2.0% of Ni, 0.30-0.80% of Cr, 0.10-0.40% of Mo, less than or equal to 0.20% of Ti, less than or equal to 0.020% of S, and less than or equal to 0.020% of P with balance being Fe and inevitable impurities. The 900MPa high-strength welding wire is used for welding under the protection of gas rich in argon, that is Ar + 20% of CO2, thereby having high strength and low-temperature toughness.

Description

technical field [0001] The invention relates to a high-strength welding wire suitable for welding Q890, Q900 and other high-strength plates and a use method, in particular to a 900MPa high-strength welding wire for mining machinery and a use method. Background technique [0002] With the rapid development of the coal mining industry, higher requirements are put forward for the reliability of coal mining machinery (such as high-strength hydraulic supports). [0003] At present, coal mining machinery mainly includes support equipment, mining equipment, transportation equipment, etc., and the support equipment includes shield support, support shield support, top-coal caving support, etc., which are all powered by high-pressure liquid. A coal mining face equipment that supports and controls the roof, which is composed of elements and some metal components, has the characteristics of high strength, fast moving speed, good support performance, safety and reliability, so in the pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/30B23K9/16
CPCB23K35/3053B23K9/173
Inventor 关常勇曲传颂王德柱
Owner 山东索力得焊材股份有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com