Preparation method of vortex spinning brocade yarn

A technology of vortex spinning and viscose fiber, which is applied in the direction of yarn, textiles and papermaking, and can solve the problems of restricting product development, fiber types and air-conditioning environment requirements, and affecting spinning efficiency, etc.

Active Publication Date: 2016-01-06
绍兴国周针织科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since vortex spinning yarns are generally pure viscose yarns and polyester-viscose blended yarns, the proportion of colored cotton or pure polyester yarns, pure cotton yarns and other wool yarns should not be too high, such as pure cotton Generally, the proportion of spinning should not exceed 40%, otherwise the spinning efficiency will be affected due to poor spinnability; at the same time, air-jet vortex spinning uses high-speed compressed air to form yarns, and the speed is more than 20 times that of traditional spinning, generally up to 380 meters per minute, so the influence of temperature and humidity is particularly sensitive, the viscose type is controlled at 50-60%, and the polyester-viscose blended type is controlled at 40-45%, so the requirements for the type of fiber and the air-conditioning environment are relatively strict, which limits product development. further development of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of vortex spinning brocade yarn
  • Preparation method of vortex spinning brocade yarn
  • Preparation method of vortex spinning brocade yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation method of vortex spinning colored cotton yarn of the present invention, concrete steps are as follows:

[0020] (1) Material selection: Colored viscose fiber and flat polyester in red, yellow and blue colors are selected. The proportion of colored viscose fiber added is 70%, and the proportion of added flat polyester of each color is the same, 10%.

[0021] (2) Premixed strips: Mix the raw materials in step (1) into four mixed strips, two viscose fiber strips and one polyester strip to form a colored premixed strip. The specific mixing method is: first mix flat polyester with colored The viscose fiber is pre-mixed, that is, the colored viscose fiber and flat polyester are placed in the grid of the disc of the cotton mixing device (that is, the disc grabbing machine, FA002), and then sent to the carding machine after opening , enter the drawing frame through the carding machine for pre-drawing to form a mixed sliver, and then form the colored viscose fibe...

Embodiment 2

[0026] The preparation method of vortex spinning colored cotton yarn of the present invention, concrete steps are as follows:

[0027] (1) Material selection: Colored viscose fiber and flat polyester in red, yellow and blue colors are selected. The proportion of colored viscose fiber added is 94%, and the proportion of added flat polyester of each color is the same, 2%.

[0028] (2) Premixed strips: Mix the raw materials in step (1) into three mixed strips, two viscose fiber strips and two polyester strips to form a colored premixed strip. The specific mixing method is: first mix flat polyester with colored viscose The glue fiber is pre-mixed to form a mixed strip, and then the colored viscose fiber and flat polyester fiber are respectively formed into a viscose fiber strip and a polyester strip. Among them, in the pre-mixing, the mixing ratio of flat polyester and colored viscose fiber is 1:0.6, and the colored viscose fiber and flat polyester can be added to 85% of the total...

Embodiment 3

[0033] The preparation method of vortex spinning colored cotton yarn of the present invention, concrete steps are as follows:

[0034] (1) Material selection: Colored viscose fiber and flat polyester in red, yellow, and blue colors are selected. The proportion of colored viscose fiber added is 82%, and the proportion of added flat polyester of each color is the same, all 6%.

[0035] (2) Premixed strips: Mix the raw materials in step (1) into three mixed strips, two viscose fiber strips and two polyester strips to form a colored premixed strip. The specific mixing method is: first mix flat polyester with colored viscose The glue fiber is pre-mixed to form a mixed strip, and then the colored viscose fiber and flat polyester fiber are respectively formed into a viscose fiber strip and a polyester strip. Among them, in the pre-mixing, the mixing ratio of flat polyester and colored viscose fiber is 1:2, and the colored viscose fiber and flat polyester can be added to 80% of the to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production method of vortex spun colored silk yarns and belongs to the technical field of production of special yarns. The method includes: selecting materials, premixing slivers, pre-drawing, and performing vortex spinning. Colored viscose fiber and a plurality of flat polyester fibers different in color are pre-mixed; namely, the colored viscose fiber and the flat polyester fibers are alternately disposed in a disc grille of a cotton mixer, the fibers and the grille are fed into a carding machine after opening and are fed into a drawing frame for pre-drawing by the carding machine so as to obtain mixed slivers; the flat polyester fibers and the colored viscose fiber are made into polyester slivers and viscose slivers respectively before drawing and vortex spinning; the obtained fabric has the advantages of colorfulness, diversity, wear resistance and the like.

Description

technical field [0001] The invention relates to a preparation method of vortex spinning brocade yarn, which belongs to the technical field of preparation of special yarns. Background technique [0002] With the development of textile technology, different spinning forms can form different yarn styles due to different spinning principles. The vortex spinning process is short and the production rate is high. At the same time, it can save a lot of labor and is easy to operate. It is also relatively simple, and the strength and uniformity of the spun yarn are better than those of conventional technology. Not only can core-spun yarns be produced, but also double-structured yarns can be produced by using different fiber lengths and shrinkage degrees. Rich and colorful special yarn, so it is widely used. However, since vortex spinning yarns are generally pure viscose yarns and polyester-viscose blended yarns, the proportion of colored cotton or pure polyester yarns, pure cotton ya...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/34D02G3/04
Inventor 金国周金芳应萍俞诚陶华冠高水林郝首领赵中赵杨杰
Owner 绍兴国周针织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products