Manufacturing method for unidirectional electromagnetic steel sheet

An electromagnetic steel sheet and manufacturing method technology, applied in the direction of the magnetism of inorganic materials, can solve the problems of deviation in the length direction and width direction of the glass film or insulating film, and achieve the effect of suppressing defects and high quality

Active Publication Date: 2015-05-06
NIPPON STEEL CORP
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In addition, since grain-oriented electrical steel sheets are subjected to many heat treatments, the interface structure and thickness of the glass film or insulating film may vary in the longitudinal direction (rolling direction) and width direction of the steel sheet base metal.
Therefore, even if the laser irradiation conditions are adjusted, it may be difficult to reliably suppress the occurrence of flaws on the glass film on the entire steel sheet base metal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for unidirectional electromagnetic steel sheet
  • Manufacturing method for unidirectional electromagnetic steel sheet
  • Manufacturing method for unidirectional electromagnetic steel sheet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0057] Next, a confirmation experiment carried out to confirm the effects of the present invention will be described.

[0058] First, prepare a slab having the following composition: 3.0% by mass of Si, 0.05% by mass of C, 0.1% by mass of Mn, 0.02% by mass of acid-soluble Al, 0.01% by mass of N, and 0.01% by mass of S , P is 0.02% by mass, and the remainder contains Fe and unavoidable impurities.

[0059] This slab was hot-rolled at 1280° C. to produce a hot-rolled material with a thickness of 2.3 mm.

[0060] Next, the hot-rolled material was heat-treated under the condition of 1000° C.×1 minute. Pickling treatment was performed after the heat treatment, and cold rolling was performed to produce a cold-rolled material with a thickness of 0.23 mm.

[0061] This cold-rolled material was subjected to decarburization annealing under the conditions of 800° C.×2 minutes. Next, an annealing separation material mainly composed of magnesium oxide was coated on both surfaces of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The method for producing a grain-oriented electrical steel sheet according to the present invention has the following steps: a final annealing step (S07) of annealing the base metal of the steel sheet in a batch furnace in a coiled state, thereby forming the glass film on the surface of the steel plate base metal; an insulating film forming step (S08) of forming an insulating film on the glass film after the final annealing step (S07); and a laser irradiation step (S09) , which is a process of irradiating a laser beam from above the insulating film to control the magnetic domains, wherein in the laser irradiation process (S09), the radially outward surface of the roll during the final annealing process (S07) is Irradiate the laser beam.

Description

technical field [0001] The present invention relates to a method for producing a grain-oriented electrical steel sheet in which a glass film and an insulating film are formed on the surface of a steel sheet base metal and magnetic domains are controlled by irradiation with laser light. Background technique [0002] The aforementioned grain-oriented electrical steel sheets are being used as raw materials for iron cores constituting electrical equipment such as transformers and rotary machines. In such a grain-oriented electrical steel sheet, it is necessary to reduce energy loss (iron loss) during magnetization. Iron loss is classified into eddy current loss and hysteresis loss. Furthermore, eddy current loss is classified into classical eddy current loss and abnormal eddy current loss. [0003] Here, in order to reduce classical eddy current loss, a grain-oriented electrical steel sheet having a thin thickness with an insulating film formed on the surface of the sheet is p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D8/12H01F1/16C22C38/00C22C38/06
CPCC21D8/1222C21D8/1233C21D8/1255C21D8/1272C21D8/1283C21D8/1294C22C38/001C22C38/02C22C38/04C22C38/06H01F1/18
Inventor 坂井辰彦滨村秀行
Owner NIPPON STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com