Dual-curing composition

A dual-curing and composition technology, applied to light-curing compositions, can solve problems such as limited methods through the field of thermal curing, and achieve the effect of high strength and high hardness

Inactive Publication Date: 2014-02-12
甘春丽 +1
View PDF1 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For silicone rubber, in order to obtain higher strength and hardness, it is necessary to use reinforci...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dual-curing composition
  • Dual-curing composition
  • Dual-curing composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The dual curing composition of this example contains: 20 parts of vinyl-terminated divinyl silicone oil with a viscosity of 10000 mPa.S, 2 parts of active hydrogen-terminated hydroxyl-terminated silicone oil, 0.2 part of benzodiazepine, 0.01 part of 2,5- Dimethyl-2,5-bis(tert-butylperoxy)hexane, 5 parts of DPHA, 0.2 parts of 184, 0.15 parts of fluorosilicone defoamer.

[0043] The composition was heated and cured at 160° C. for 15 minutes, and then UV cured to obtain a dual-cured material, which had a rubber texture.

Embodiment 2

[0045] The dual curing composition of this embodiment comprises: 60 parts of vinyl-terminated divinyl silicone oil with a viscosity of 10000 mPa.S, 20 parts of active hydrogen-terminated hydroxyl-terminated silicone oil, 2 parts of ethynyl cyclohexanol, and 0.2 parts of chloroplatinic acid solution , 30 parts of 6145 (acrylate resin), 30 parts of DPHA, 7 parts of 184, 4 parts of fluorosilicone defoamer.

[0046] The composition was heat-cured at 160° C. for 15 minutes, and then UV-cured to obtain a dual-cure material.

Embodiment 3

[0048] The dual curing composition of this embodiment comprises: 10 parts of vinyl-terminated divinyl silicone oil with a viscosity of 850 mPa.S, 20 parts of vinyl-terminated divinyl silicone oil with a viscosity of 1000 mPa.S, 60 parts of vinyl-terminated divinyl silicone oil with a viscosity of 10000 mPa.S Vinyl-terminated divinyl silicone oil, 10 parts of vinyl-terminated divinyl silicone oil with a viscosity of 5,000,000mPa.S, 20 parts of active hydrogen-terminated hydroxyl-terminated silicone oil, 30 parts of active hydrogen-terminated and side chains also containing active hydrogen Hydrogen-containing silicone oil, 4 parts of diallyl maleate, 6 parts of ethynyl cyclohexanol, 0.6 parts of chloroplatinic acid solution, 0.4 parts of platinum-vinyl siloxane, 90 parts of CN2302 (acrylate resin), 10 parts Parts of methyl methacrylate, 7 parts of 184, 3 parts of TPO, 4.4 parts of fluorine-containing defoamer, 5 parts of fluorosilicon defoamer, 0.1 part of polymerization inhibito...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a dual-curing composition which comprises addition type silicone oil, hydrogen-containing silicone oil, an inhibitor, a catalyst, a (methyl) acrylic ester compound, a light initiator and an auxiliary, and selectively comprises silicon modified (methyl) acrylic ester, a filler, a reinforced silica resin and a solvent. Due to adoption of the composition disclosed by the invention, dual-curing of heating and ultraviolet light can be conveniently achieved, materials of different properties such as rubber and plastics can be prepared, and materials with different physical characteristics and different color effects can be prepared.

Description

technical field [0001] The present invention relates to dual-cure compositions, especially compositions curable by heat and light. Such compositions can be applied in the fields of dipping, 3D printing, molding, casting, spin coating, lamination, bonding, protection and the like. Background technique [0002] As a synthetic organic polymer with a special structure, silicone rubber has better high and low temperature resistance, ultraviolet resistance, radiation resistance, weather resistance, electrical insulation, hydrophobicity, flame retardancy, high air permeability, physiological inertia, etc. than other ordinary rubbers. Therefore, it is widely used in aerospace, aviation, electrical and electronic, light industry, machinery, construction, chemical industry, medical and health, daily necessities, etc., and has become an important and indispensable new polymer material in the national economy. For silicone rubber, in order to obtain higher strength and hardness, it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/07C08L83/05C08L33/08C08L33/10C08L83/04C08K13/06C08K9/06C08K3/36C08K5/3447C08K5/103C08K5/05C08K5/11C08L51/06C08L33/00C08J3/28C08J3/24
Inventor 廖张洁甘春丽
Owner 甘春丽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap