Textile subjected to water repellency treatment and production method for textile

A production method and textile technology, which are applied to water-repellent textiles and their production fields, can solve problems such as inability to meet, and achieve the effects of high safety, high water repellency, and low wettability

Inactive Publication Date: 2014-04-16
TORAY FIBER RES INST(CHINA) CO LTD
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, water-repellent clothing with PFOA and PFOS content less than 0.05 μg / g is basically treated with fluorine-based water-repellent agent or non-fluorine-based water-repellent agent alone, although these two methods have a good water-repellent effect , but it still cannot meet some garments with high requirements for water release performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Textile subjected to water repellency treatment and production method for textile
  • Textile subjected to water repellency treatment and production method for textile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Dye the woven gray fabric of CDP (sulfonic acid modified polyester), and then process it with the processing fluid of the following composition,

[0057] The pretreatment processing fluid consists of the following components:

[0058] Anionic pretreatment agent A 10%o.w.f.

[0059] pH regulator 1g / L

[0060] the rest is water

[0061] Water-repellent processing fluids consist of the following components:

[0062] Water repellent agent A 120g / L

[0063] Water repellent D 50g / L

[0064] Bridging agent A 3g / L

[0065] Penetrant 5g / L

[0066] the rest is water

[0067] Processing conditions: firstly treat in the pre-treatment processing liquid bath (bath ratio 1:20) for 30 minutes, the processing temperature is 90 degrees, and the processing pH value is 2-3; after drying, put it into the water-repellent processing liquid for padding, Then heat treatment at 130° C. for 2 minutes, then carry out setting finishing at 170° C., and obtain the textile of the present inven...

Embodiment 2

[0069] Dye the woven gray fabric of CDP (sulfonic acid modified polyester), and then process it with the processing fluid of the following composition,

[0070] The pretreatment processing fluid consists of the following components:

[0071] Anionic pretreatment agent A 5%o.w.f.

[0072] pH regulator 3g / L

[0073] the rest is water

[0074] Water-repellent processing fluids consist of the following components:

[0075] Water repellent agent B 100g / L

[0076] Water repellent agent E 50g / L

[0077] Bridging agent C 3g / L

[0078] Catalyst A (for bridging agent C) 3g / L

[0079] Penetrant 10g / L

[0080] the rest is water

[0081] Processing conditions: firstly treat in the pre-treatment processing liquid bath (bath ratio 1:20) for 30 minutes, the processing temperature is 90 degrees, and the processing pH value is 2-3; after drying, put it into the water-repellent processing liquid for padding, Then heat treatment at a temperature of 80-200°C for 10 minutes, and then carr...

Embodiment 3

[0083] Dye the knitted gray fabric formed by CDP (sulfonic acid modified polyester) / Lycra, and then process it with the processing fluid of the following composition,

[0084] The pretreatment processing fluid consists of the following components:

[0085] Anionic pretreatment agent A 10%o.w.f.

[0086] pH regulator 10g / L

[0087] the rest is water

[0088] Water-repellent processing fluids consist of the following components:

[0089] Water repellent C 70g / L

[0090] Water repellent F 90g / L

[0091] Bridging agent B 20g / L

[0092] Penetrant 20g / L

[0093] the rest is water

[0094] Processing conditions: firstly treat in the pre-treatment processing liquid bath (bath ratio 1:20) for 30 minutes, the processing temperature is 90 degrees, and the processing pH value is 2-3; after drying, put it into the water-repellent processing liquid for padding, Then heat treatment at 130° C. for 2 minutes, then carry out setting finishing at 170° C., and obtain the textile of the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a textile subjected to water repellency treatment and a production method for the textile. The textile mainly comprises cationic dye-dyeable modified polyester fibers and / or nylon fibers; the single fiber surface of the textile is at least covered with a resin film formed by water-repellent C6 fluororesin and water-repellent non-fluororesin; the surfaces of the cationic dye-dyeable modified polyester fibers and / or nylon fibers have anionic groups. The textile has durable washability and high water repellency.

Description

technical field [0001] The invention relates to a water repellent treated textile and a production method thereof. Background technique [0002] The common textiles with water-repellent function on the market are mainly products processed by water-repellent agents containing perfluorooctanoic acid ammonium compound (hereinafter referred to as PFOA) and perfluorooctane sulfonate compound (hereinafter referred to as PFOS). However, if the residual PFOA and PFOS in the body are higher than a certain concentration, it is harmful to the human body. PFOS is one of the most difficult to degrade organic pollutants found in the world, with high bioaccumulation and multiple toxicity. Among them, many kinds of toxicity are liver toxicity, male reproductive toxicity, variable genotoxicity, nerve damage toxicity, developmental delay toxicity and endocrine interference toxicity. It is 251mg / kg. PFOA is also difficult to degrade in the environment and has the characteristics of persiste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/256D06M15/643D06M13/02D06M15/00D06M101/32D06M101/34
Inventor 黄芸芸罗周荣清水壮夫
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com