Textile used for swimming suit and production method thereof

A production method and textile technology, applied in the field of swimwear textiles and its production, can solve the problems of low water-carrying performance maintenance, poor washing durability of polyester, etc., and achieve high safety, low wettability, and low water-carrying properties Effect

Inactive Publication Date: 2014-02-12
TORAY FIBER RES INST(CHINA) CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Patent Publication No. CN102134807A discloses a water-repellent-treated textile for swimwear. A similar method is used to obtain a water-repellent substance that does not contain PFOS and PFOA, but the sulfonic acid group-modified cationic dye can be dyed and modified The washing durability of polyester is poor, and the performance maintenance of low water carrying rate is also poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Textile used for swimming suit and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0164] It includes dyeing warp knitted fabric formed by CDP (sulfonic acid modified polyester) / Lycra, and then processing it with a processing fluid composed of the following:

[0165] The pretreatment processing fluid consists of the following components:

[0166] Anionic pretreatment agent A 10 %o.w.f.

[0167] pH adjustment solution 3g / L

[0168] the rest is water

[0169] Water-repellent processing fluids consist of the following components:

[0170] Water repellent agent A 100g / L

[0171] Bridging agent A 3g / L

[0172] Bridging agent B 2g / L

[0173] Bridging agent J 10g / L

[0174] Penetrant 10g / L

[0175] The rest is soft water

[0176] Processing conditions: firstly treat in the bath of the pre-treatment processing liquid (bath ratio 1:20) for 30 minutes, the processing temperature is 90 degrees, and the processing pH value is 3-4; after drying, put it into the water-repellent processing liquid for padding, Then heat treatment for 1-20 minutes at a temperature...

Embodiment 2

[0178] It includes dyeing warp knitted fabrics formed by CDP (sulfonic acid modified polyester) / Lycra / PTT, and then processing with the following processing fluid:

[0179] The pretreatment processing fluid consists of the following components:

[0180] Anionic pretreatment agent A 10 %o.w.f.

[0181] pH adjustment solution 3g / L

[0182] the rest is water

[0183] Water-repellent processing fluids consist of the following components:

[0184] Water repellent B 60g / L

[0185] Water repellent D 45g / L

[0186] Bridging agent G 10g / L

[0187] Penetrant 10g / L

[0188] The rest is soft water

[0189] Processing conditions: firstly treat in the bath of the pre-treatment processing liquid (bath ratio 1:20) for 30 minutes, the processing temperature is 90 degrees, and the processing pH value is 3-4; after drying, put it into the water-repellent processing liquid for padding, Then heat treatment for 1-20 minutes at a temperature of 80-200°C or dry at a temperature of 80-150°...

Embodiment 3

[0191] It includes dyeing the warp knitted fabric formed by CDP (sulfonic acid modified polyester) / PBT, and then processing it with the following processing fluid:

[0192] The pretreatment processing fluid consists of the following components:

[0193] Anionic pretreatment agent B 5%o.w.f.

[0194] the rest is water

[0195] Water-repellent processing fluids consist of the following components:

[0196] Water repellent agent A 55g / L

[0197] Water repellent K 30g / L

[0198] Bridging agent B 10g / L

[0199] Bridging agent C 3g / L

[0200] Catalyst A (for bridging agent C) 2g / L

[0201] Penetrant 10g / L

[0202] The rest is soft water

[0203] Processing conditions: firstly treat in the bath of the pretreatment processing liquid (bath ratio 1:10) for 20 minutes, the processing temperature is 80 degrees, and the pH value of the processing is 2 to 3; after drying, put it into the processing liquid for water-repellent padding, Then heat treatment for 1-20 minutes at a temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a textile used for a swimming suit and a production method thereof. The textile is mainly formed by elastic fiber, and polyester fiber surface of which is provided with anionic groups. The surface of single fiber in the textile is coated with a water-repellent resin film, wherein a fluorine element content of the water-repellent resin film is not less than 0 [mu]g / g and less than 6000 [mu]g / g; a residual amount of ammonium perfluorocaprylate is not more than 0.05 [mu]g / g, and a residual amount of perfluorooctane sulfonate is not more than 0.05 [mu]g / g. The textile is suitable for manufacturing functional swimming suit textile fabrics, and has excellent water repellency functions of low wettability, low water volume and durable rinsibility.

Description

technical field [0001] The invention relates to a textile for swimwear and a production method thereof. Background technique [0002] The common textiles with water-repellent function on the market are mainly products processed by water-repellent agents containing perfluorooctanoic acid ammonium compound (hereinafter referred to as PFOA) and perfluorooctane sulfonate compound (hereinafter referred to as PFOS). However, if the residual PFOA and PFOS in the body are higher than a certain concentration, it is harmful to the human body. PFOS is one of the most difficult to degrade organic pollutants found in the world, with high bioaccumulation and multiple toxicity. Among them, many kinds of toxicity are liver toxicity, male reproductive toxicity, variable genotoxicity, nerve damage toxicity, developmental delay toxicity and endocrine interference toxicity. It is 251 mg / kg. PFOA is also difficult to degrade in the environment and has the characteristics of persistent organic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/00D06M15/256D06P1/00D06P3/85D06P5/04A41D7/00D06M101/32
Inventor 符晔黄芸芸罗周荣清水壮夫
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com