Method for cleaning sticky wall of high pressure polyethylene tubular reactor
A technology of tubular reactor and high-pressure polyethylene, applied in cleaning methods and appliances, chemical instruments and methods, cleaning hollow objects, etc., can solve the problems of high molecular polymers that are difficult to clean, and achieve the effect of solving difficult cleaning
Active Publication Date: 2014-05-28
CHNA ENERGY INVESTMENT CORP LTD +1
View PDF4 Cites 5 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0007] The present invention aims to provide a method for cleaning the sticky wall of a high-pressure polyethylene tubular reactor to solve the problem that the high-molecular polymer adhered to the high-pressure polyethylene tubular reactor in the prior art is difficult to clean
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0018] The embodiments of the present invention will be described in detail below with reference to the accompanying drawings, but the present invention can be implemented in many different ways defined and covered by the claims.
[0019] The invention provides a method for cleaning the sticky wall of a high-pressure polyethylene tubular reactor, please refer to figure 1 The method comprises: feeding solvent oil into a reaction tube of a high-pressure polyethylene tubular reactor; heating the solvent oil in the reaction tube to a predetermined dissolution temperature and maintaining it for a predetermined time; discharging the solvent oil in the reaction tube.
[0020] In the present invention, the solvent oil is passed into the reaction tube of the high-pressure polyethylene tubular reactor, the solvent oil is heated to a predetermined temperature and maintained for a predetermined time, so that the high molecular polymer adhered to the inner wall of the reaction tube can be d...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a method for cleaning a sticky wall of a high pressure polyethylene tubular reactor. The method comprises the steps that solvent oil is added into a reaction pipe of the high pressure polyethylene tubular reactor; the solvent oil in the reaction pipe is heated to be at a preset solution temperature and maintained for a preset time period; the solvent oil in the reaction pipe is drained out. According to the method, the solvent oil is added into the reaction pipe of the high pressure polyethylene tubular reactor, the solvent oil in the reaction pipe is heated to be at the preset solution temperature and maintained for the preset time period, so that high-molecular polymers bonded on the inner wall of the reaction pipe are dissolved in the solvent oil, and finally the high-molecular polymers are drained out along with the solvent oil. The method conveniently solves the problem that the sticky wall of the high pressure polyethylene tubular reactor is difficult to clean.
Description
technical field [0001] The invention relates to a high-pressure polyethylene tubular reactor, and more particularly, to a method for cleaning the sticky wall of a high-pressure polyethylene tubular reactor. Background technique [0002] Polymers with relatively high molecular weight will be produced during the polymerization reaction. Because these polymers have high molecular weight and poor fluidity, they are easy to stick to the inner wall of the reaction tube of the high-pressure polyethylene tubular reactor. If the wall sticking is serious, it will not only reduce the production efficiency of the high-pressure polyethylene tubular reactor, but also cause the heat exchange efficiency of the reaction tube to drop sharply, so that the reaction heat cannot be removed in time, and the reaction temperature will rise sharply. Thereby increasing the probability of thermal decomposition. [0003] In addition, the sticky wall material is essentially a high-molecular-weight polye...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B08B9/08
CPCB08B9/027
Inventor 王会伦邓方文
Owner CHNA ENERGY INVESTMENT CORP LTD