Uvioresistant short fiber manufacturing method

A manufacturing method and short fiber technology, which is applied in the field of UV-resistant short fiber manufacturing, can solve the problems of losing the anti-ultraviolet effect and achieve the effect of increasing compatibility

Active Publication Date: 2015-02-25
NANTONG ANHENG CHEM FIBER CO LTD
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The anti-ultraviolet fibers currently available on the market are mainly made of ordinary fibers for surface anti-ultraviolet treatment, or polyester melt or polyester chips are added with anti-ult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Add cornstarch, polylactic acid, ethylene glycol, and aluminum coupling agent to the high-speed mixing mixer at a weight ratio of 80:10:8:2, with a rotation speed of 2500r / min and a mixing time of 30 minutes. The order is to add cornstarch and ethylene glycol first, then add surface treatment agent after stirring for 5 minutes, and then add polylactic acid after stirring for 10 minutes; Among them, the weight ratio of the three is 80:15:5, the rotating speed is 2500r / min, and the stirring and mixing time is 30min. Ester chips; (3) Mix the materials obtained in (1) and (2) in a high-speed mixer, keep stirring and raise the temperature to 180°C, then increase the speed to 4000r / min, continue stirring for 20min, then stop heating and continue stirring Mix until uniform, then cool and discharge; (4) Place the cooled and discharged material in a vacuum drum dryer and fully dry at 90°C for 15 hours; (5) Melt and extrude the dried material with a screw to obtain a melt , ...

Embodiment 2

[0030] (1) Add cornstarch, polylactic acid, ethylene glycol, and aluminum coupling agent into the high-speed mixing mixer at a weight ratio of 80:10:8:2, with a rotation speed of 2500r / min and a mixing time of 20 minutes. The order is to add cornstarch and ethylene glycol first, then add surface treatment agent after stirring for 5 minutes, and then add polylactic acid after stirring for 10 minutes; Among them, the weight ratio of the three is 80:15:5, the rotating speed is 2500r / min, and the stirring and mixing time is 30min. Ester chips; (3) Mix the materials obtained in (1) and (2) in a high-speed mixer, keep stirring and raise the temperature to 180°C, then increase the speed to 4000r / min, continue stirring for 30min, then stop heating and continue stirring Mix until uniform, then cool and discharge; (4) Place the cooled and discharged material in a vacuum drum dryer and fully dry at 100°C for 12 hours; (5) Melt and extrude the dried material with a screw to obtain a melt ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fiber denieraaaaaaaaaa
Breaking strengthaaaaaaaaaa
Average lengthaaaaaaaaaa
Login to view more

Abstract

A uvioresistant short fiber manufacturing method mainly includes that corn starch and polyesters are used as basic materials, and nano titanium dioxide is added to serve as a uvioresistant agent to make short fibers by melt spinning. The short fibers manufactured according to the method integrate advantages of corn fibers and polyester fibers and are excellent in uvioresistant effect.

Description

[0001] technical field [0002] The invention relates to the field of anti-ultraviolet fiber weaving, in particular to a method for manufacturing an anti-ultraviolet short fiber. [0003] Background technique [0004] The rapid development of the world's economy today has also brought about serious problems such as environmental pollution, especially the increasingly serious damage to the ozone layer. The intensity of ultraviolet rays reaching the ground has increased significantly, and the damage of ultraviolet rays to the human body has also increased. Long-term exposure to ultraviolet rays will cause Reduce the lifespan of organic molecules and reduce the immune function of the human body, which not only damages the skin and causes dermatitis, freckles, erythema and other diseases, but also promotes eye diseases, cataracts, and even skin cancer and other diseases. Therefore, how to solve the damage of ultraviolet rays has become an urgent problem to be solved. question. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/18D01F8/14D01F1/10D01D5/08D01D5/098
Inventor 耿云花
Owner NANTONG ANHENG CHEM FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap