Bitumen-impregnated type composite steel wire rope for railway and production method thereof

A production method and asphalt-impregnated technology, which is applied in the asphalt-impregnated composite steel wire rope used in railways and its production field, can solve the problems that the composite steel wire rope cannot meet the design requirements of high-speed railways, and can not meet the requirements, so as to ensure work efficiency and work safety , high tensile strength and high filling factor

Active Publication Date: 2015-05-13
江苏亚盛金属制品有限公司
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of high-speed railways in China and the world, more and more special steel wire ropes are used for electrified railways, and the requirements for their quality and performance are getting higher and higher. The requirements for the composite steel wire ropes used in railway compensation devices are also getting higher and higher. On the premise of considering the reasonable cooperation of the rope and the wheel and the small increase of the wheel groove of the overall device, the diameter of the composite steel wire rope basically does not increase, and higher requirements are put forward for the breaking force of the composite steel wire rope, and the composite steel wire rope is required to have a stronger In addition to fatigue resistance and fatigue resistance, the composite steel wire rope also needs to have a good electrical conductivity, but the existing composite steel wire rope cannot meet the design requirements of high-speed railways, and cannot meet the existing high standard requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bitumen-impregnated type composite steel wire rope for railway and production method thereof
  • Bitumen-impregnated type composite steel wire rope for railway and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Another aspect of the present invention provides a production method of asphalt-impregnated composite steel wire rope for railway, the structure of the asphalt-impregnated composite steel wire rope for railway is 12×26WS+12×7+1×36SFi, and the tensile strength of single-strand structure is greater than Equal to 2300Mpa, the knotting tension is greater than or equal to 55%, the number of torsion resistance is greater than or equal to 21, the tension of the inner strands is greater than or equal to 2300KN, and the tension of the outer strands is greater than or equal to 6000KN, which includes the following steps,

[0036] Step 1. For the wire rod, use SWRH72A with a diameter of 5.5 mm.

[0037] Step 2. Rough drawing. Use a straight wire drawing machine model 11 / 560 to draw a 5.5 mm diameter SWRH72A wire into a 2.0 mm SWRH72A. The drawing process is 5.5-4.9-4.4-4.0-3.7-3.4- 3.1-2.8-2.5-2.2-2.0.

[0038] Step 3, heat treatment, choose a gas-fired type 32 electric heating fu...

Embodiment 2

[0048] Another aspect of the present invention provides a production method of asphalt-impregnated composite steel wire rope for railway, the structure of the asphalt-impregnated composite steel wire rope for railway is 12×26WS+12×7+1×36SFi, and the tensile strength of single-strand structure is greater than Equal to 2300Mpa, the knotting tension is greater than or equal to 55%, the number of torsion resistance is greater than or equal to 21, the tension of the inner strands is greater than or equal to 2300KN, and the tension of the outer strands is greater than or equal to 6000KN, which includes the following steps,

[0049] Step 1. For the wire rod, use SWRH72A with a diameter of 5.5 mm.

[0050] Step 2. Rough drawing. Use a straight wire drawing machine model 11 / 560 to draw a 5.5 mm diameter SWRH72A wire into a 2.0 mm SWRH72A. The drawing process is 5.5-4.9-4.4-4.0-3.7-3.4- 3.1-2.8-2.5-2.2-2.0.

[0051] Step 3, heat treatment, choose a gas-fired type 32 electric heating fu...

Embodiment 3

[0062] Another aspect of the present invention provides a production method of asphalt-impregnated composite steel wire rope for railway, the structure of the asphalt-impregnated composite steel wire rope for railway is 12×26WS+12×7+1×36SFi, and the tensile strength of single-strand structure is greater than Equal to 2300Mpa, the knotting tension is greater than or equal to 55%, the number of torsion resistance is greater than or equal to 21, the tension of the inner strands is greater than or equal to 2300KN, and the tension of the outer strands is greater than or equal to 6000KN, which includes the following steps,

[0063] Step 1. For the wire rod, use SWRH72A with a diameter of 5.5 mm.

[0064] Step 2. Rough drawing. Use a straight wire drawing machine model 11 / 560 to draw a 5.5 mm diameter SWRH72A wire into a 2.0 mm SWRH72A. The drawing process is 5.5-4.9-4.4-4.0-3.7-3.4- 3.1-2.8-2.5-2.2-2.0.

[0065] Step 3, heat treatment, choose a gas-fired type 32 electric heating fu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of steel wire rope application and particularly discloses a bitumen-impregnated type composite steel wire rope for a railway and a production method thereof. The bitumen-impregnated type composite steel wire rope is composed of a center strand, twelve inner layer strands and twelve outer layer strands, wherein the inner layer strands are arranged on the periphery of the center strand and arranged with the center strand in a dodecagon shape, and the outer layer strands are arranged on the periphery of the inner layer strands and arranged with the inner layer strands in a dodecagon shape. The center stand makes point contact with the inner layer strands, and the inner layer strands make point contact with the outer layer strands. The bitumen-impregnated type composite steel wire rope is simple in structure, low in production cost, high in extension strength, fatigue resistance, corrosion resistance and abrasive resistance and long in service life; through repeated calculation, tests, designs and stimulation tests, the high-strength and high-fatigue-resistance steel wire rope special for the electric railway is produced; compared with a conventional steel wire rope, the filling coefficient is high, contact layer steel wires are thickened, and therefore the steel wire rope has the advantages of being high in strength, fatigue resistance and conductive performance.

Description

technical field [0001] The invention belongs to the technical field of steel wire rope applications, and in particular relates to an asphalt-soaked composite steel wire rope for railways and a production method thereof. Background technique [0002] With the development of high-speed railways in China and the world, more and more special steel wire ropes are used for electrified railways, and the requirements for their quality and performance are getting higher and higher. The requirements for the composite steel wire ropes used in railway compensation devices are also getting higher and higher. On the premise of considering the reasonable cooperation of the rope and the wheel and the small increase of the wheel groove of the overall device, the diameter of the composite steel wire rope basically does not increase, and higher requirements are put forward for the breaking force of the composite steel wire rope, and the composite steel wire rope is required to have a stronger ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D07B1/06B21C1/02B21C9/00C23C2/06C23C2/38D07B7/14
CPCC21D8/065C23C2/06C23C2/38D07B1/068D07B1/0686D07B7/145B21C1/02B21C9/00D07B2201/1044D07B2201/1036D07B2201/2024D07B2201/2012D07B2201/2011D07B2205/00D07B2201/2037D07B2201/2061D07B2201/2087D07B2205/3025D07B2205/3071D07B2801/18D07B2801/10D07B2801/24D07B1/165D07B1/147
Inventor 蒋东华蒋红俊周江赵洪章
Owner 江苏亚盛金属制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap