Wear resistant surfacing alloy material and preparing method thereof

A technology of alloy materials and surfacing materials, applied in welding/cutting media/materials, welding equipment, metal processing equipment, etc., can solve the problems of decreased safety of surfacing layers, poor wear resistance of surfacing layers, and strong toughness of surfacing layers Low-level problems, to achieve the effect of improving the shape of the hard phase, good wear resistance, and improving wear resistance

CN104625473AActive Publication Date: 2015-05-20美光(江苏)三维科技有限公司
14 Cites 8 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2015-05-20
Patent Text Reader

Abstract

The invention discloses a wear resistant surfacing alloy material which comprises, by weight, the components of 4.8%-5.0% of C, 3.3%-3.5% of B, 28%-30% of Cr, 8.0%-8.5% of V, 2.0%-2.5% of Nb, 0.9%-1.0% of K, 1.2%-1.5% of Ce, 1.2%-1.5% of Bi, 0.50%-0.65% of Ca, less than 1.2% of Si, less than 0.5% of Mn, less than 0.05% of S, less than 0.05% of P and the balance of Fe. Compared with the prior art, the material has the advantages of being high in hardness, good in abrasion resistance and the like, the material is used for flour mill grinding roller surfacing, and wear resistance is improved by 130%-160% compared with a common high-chromium cast iron surfacing material.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of surface treatment, and in particular relates to a wear-resistant surfacing alloy material. Background technique

[0002] Material wear is one of the important characteristics of the failure of engineering materials. The wear of materials has caused the reduction of the service life of parts and the reduction of equipment operation rate. Therefore, the development of new surface treatment methods and surface strengthening of wear-resistant parts are the key to improving the wear resistance of materials. The common surface treatment methods include electroplating, spraying, surfacing welding, etc. Among them, surfacing welding has the characteristics of easy operation and flexible application, and has been widely used in industrial production.

[0003] Chinese invention patent CN103785967A discloses a slag-free self-shielding flux-cored welding wire for vanadium-niobium composite strengthened wear-resistant...

Examples

Embodiment Construction

[0012] Below in conjunction with embodiment the present invention will be further described.

[0013] Material of the present invention is made respectively surfacing electrode (seeing embodiment 1), flux cored welding wire (seeing embodiment 2), bulk surfacing material (seeing embodiment 3) and powder surfacing material (seeing embodiment 4), Its chemical composition is shown in Table 1, and it is respectively used for the surfacing welding of the grinding roller of the coal mill. ) and 72.0HRC (see Example 4), after testing, its wear resistance is improved by 130-160% compared with common high-chromium cast iron surfacing materials.

[0014] Table 1 Chemical composition of wear-resistant surfacing materials (mass fraction, %)

[0015] the element

[0016] The above is only a preferred embodiment of the present invention, it should be pointed out that for those of ordinary skill in the art, without departing from the principle of the present invention, some improve...