Preparation process of first coat material with moisture permeable function

A kind of primer material and preparation technology, applied in the field of textile fabrics, can solve the problems that it is difficult to break through 3500MMH2O, the surface toughness of the coating film is not enough, and the rate of finished product A is low, so as to improve the moisture permeability, proper permeability and activity long time effect

Active Publication Date: 2015-06-03
KUNSHAN HUAYANG NEW MATERIAL
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) The pores of the primer layer formed by the primer slurry are easy to overlap, and the water pressure is relatively low, so it is difficult to break through 3500MMH2O;
[0004] (2) The surface toughness of the microporous coating film formed by the existing primer slurry is not enough, not scratch-resistant, and not resistant to film;
[0005] (3) The grade A rate of the finished product of the microporous coating formed by the existing primer slurry is low, and the failure rate reaches more than 30%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of first coat material with moisture permeable function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] Embodiment: a kind of primer material preparation process with moisture permeability function, comprising:

[0022] Step 1. Mix methyl ethyl ketone, water and polyurethane resin according to the mass ratio of 66~68:3~5:29~31 to form the main resin solution. Note: the mixing ratio of Example 1 is 66:3:31, Example 2 The mixing ratio is 67:5:29, and the mixing ratio of Example 3 is 68:4:30;

[0023] Step 2, adding N-methylethanolamine as an accelerator in the main resin solution of step 1, the mass ratio of the main resin solution and the accelerator is 100:2.5 or 3 or 3.5;

[0024] Step 3: Slowly put the mixture of methyl ethyl ketone and toluene into the main resin solution in step 2 and stir evenly to form a main resin mixed solution. The mass ratio of this mixed solution to the main resin solution is 100:43 or 44 or 45, so Butanone and toluene form the mixed solution according to the mass ratio of 1:2 or 1:1;

[0025] Step 4. Stir the mixed solution of hexahexanediis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of a first coat material with the moisture permeable function. The process comprises the following steps: uniformly mixing butanone, water and polyurethane resin in mass ratio of (66-68) to (3-5) to (29-31) to obtain a main resin solution; agitating and uniformly mixing 1,6-diisocyanatohexane and the main resin mixed solution obtained in step 3 in mass ratio of 100 to (1.5-2.5) at the rotating speed of 1000rpm and under the temperature of 25 to 35 DEG C to obtain the regulated main resin mixed solution; filtering the regulated main resin mixing solution through a nylon mesh with 100 to 200 meshes to obtain the filtered main resin mixed solution; standing the filtered main resin mixing solution for at least 2 hours and defoaming, wherein the standing is performed in a vacuum condition for 2 hours. According to the preparation process, the weakness that the first coat material is easily expanded in water is overcome, the moisture permeable performance of a fabric body can be improved, so that the fabric is high in service performance, and the wear resistance is greatly improved.

Description

technical field [0001] The invention relates to a preparation process of a primer material with a moisture-permeable function, and belongs to the technical field of textile fabrics. Background technique [0002] The hydrophilic non-porous PU moisture-permeable raw material currently used in the market, this method is to apply the hydrophilic non-porous PU moisture-permeable raw material to the surface of the base fabric through a coating machine, and then pass it through the coating machine oven. Hot air drying, solvent volatilization, and film formation. Make the fabric waterproof and moisture-permeable. The moisture-permeable principle is that the moisture-permeable raw materials contain hydrophilic substances, which have the functions of moisture absorption-diffusion-desorption. The moisture-permeable fabric processed by this process will swell when it encounters water, resulting in a decrease in the abrasion resistance of the film, and the moisture-permeable performance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M13/368
Inventor 张子睿
Owner KUNSHAN HUAYANG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com