A kind of organophosphine molybdenum complex, preparation method and application

An organophosphine and complex technology, which is applied in the field of preparation of organophosphine-molybdenum complexes, can solve the problems of insolubility, low catalytic efficiency, inability to meet high-efficiency production and the like, achieves low cost, high catalytic efficiency, and is suitable for large-scale industrialization production effect

Active Publication Date: 2017-08-04
张玉清
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of compound cannot be dissolved in dicyclopentadiene monomer, and the heterogeneous system formed during catalysis makes the catalytic efficiency low and cannot meet the requirements of high-efficiency production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of organophosphine molybdenum complex, preparation method and application
  • A kind of organophosphine molybdenum complex, preparation method and application
  • A kind of organophosphine molybdenum complex, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] The organophosphine molybdenum complex of this embodiment is a propyl diphenylphosphine molybdenum complex, which has the following molecular formula:

[0043] Mo[P(Ph) 2 CH 2 CH 2 CH 3 ] 2 Cl 5 Formula I-1;

[0044] In Formula I-1, P(Ph) 2 CH 2 CH 2 CH 3 For propyl diphenyl phosphine.

[0045]The preparation method of the organophosphine-molybdenum complex of this embodiment is to add 273.2g (1mol) of molybdenum pentachloride into 500ml of dry chloroform under nitrogen protection, stirring and 30°C, and wait until the molybdenum pentachloride is completely dissolved. Finally, the chloroform solution of molybdenum pentachloride is obtained; the chloroform solution of the propyl diphenylphosphine that is dissolved in 456.38g (2mol) is added dropwise in the chloroform solution of molybdenum pentachloride, 30 ℃ of insulation reaction 5h, obtain the concentration of 1mol / L chloroform solution of propyl diphenylphosphine molybdenum complex.

[0046] The chlorofo...

Embodiment 2

[0052] The organophosphine-molybdenum complex of this embodiment is a hexyldiphenylphosphine-molybdenum complex, which has the following molecular formula:

[0053] Mo[P(Ph) 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 3 ] 2 Cl 5 Formula I-2;

[0054] In formula I-2, P(Ph) 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 3 For hexyl diphenyl phosphine.

[0055] The preparation method of the organophosphine-molybdenum complex of the present embodiment is to add 218.56 g (0.8 mol) of molybdenum pentachloride into 500 ml of dry toluene under nitrogen protection, stirring and 50° C., and wait until the molybdenum pentachloride is completely After dissolving, the toluene solution of molybdenum pentachloride was obtained; the toluene solution dissolved with 432.3g (1.6mol) of hexyldiphenylphosphine was added dropwise to the toluene solution of molybdenum pentachloride, and the temperature was kept at 50°C for 4h to obtain the concentration It is a toluene solution of 0.8mol / L hexyl diphenylphosphin...

Embodiment 3

[0062] The organophosphine-molybdenum complex of this embodiment is an octyldiphenylphosphine-molybdenum complex, which has the following molecular formula:

[0063] Mo[P(Ph) 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 3 ] 2 Cl 5 Formula I-3;

[0064] In formula I-3, P(Ph) 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 2 CH 3 For octyl diphenyl phosphine.

[0065] The preparation method of the organophosphine-molybdenum complex of the present embodiment is to add 136.6 g (0.5 mol) of molybdenum pentachloride into 500 ml of dry ethylbenzene under nitrogen protection, stirring and 60° C. After molybdenum was completely dissolved, the ethylbenzene solution of molybdenum pentachloride was obtained; the ethylbenzene solution of octyldiphenylphosphine that was dissolved in 298.19g (1mol) was added dropwise in the ethylbenzene solution of molybdenum pentachloride, The reaction was carried out at 60°C for 3 hours to obtain an ethylbenzene solution of octyl diphenylphosphine moly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an organic phosphine-molybdenum complex, a preparation method and an application. The organic phosphine-molybdenum complex has the following general formula: Mo[P(Ph) 2 R] 2 Cl 5 ; where, P(Ph) 2 R is an alkyl diphenylphosphine, wherein R is a linear alkyl group with 3 to 10 carbon atoms. The organophosphine-molybdenum complex of the present invention, the ligand is an alkyl diphenylphosphine, and the organophosphine-molybdenum complex can be dissolved in dicyclopentadiene, and when used as a main catalyst to catalyze the ring-opening polymerization of dicyclopentadiene, it can be combined with bicyclopentadiene Pentadiene forms a homogeneous system, which greatly improves the catalytic efficiency, thereby improving the production efficiency of polydicyclopentadiene; it has high catalytic activity, and the quality of polydicyclopentadiene products prepared by it as the main catalyst is high. The organic phosphine-molybdenum complex has good mechanical properties such as tensile strength and impact strength; the organic phosphine-molybdenum complex has high chemical stability, is insensitive to air and water vapor, is simple to prepare, and has low cost, and is suitable for popularization and application.

Description

technical field [0001] The invention belongs to the technical field of organic synthesis, and specifically relates to an organic phosphine-molybdenum complex, and also relates to a preparation method of the organic phosphine-molybdenum complex and the application of the above-mentioned organic phosphine-molybdenum complex in catalyzing the ring-opening polymerization of dicyclopentadiene . Background technique [0002] Polydicyclopentadiene (PDCPD) is a thermosetting engineering plastic with a three-dimensional network structure obtained by ring-opening metathesis catalyst and reaction injection molding process. It is a homopolymer or copolymer of dicyclopentadiene (DCPD). Its good comprehensive mechanical properties and high-efficiency and energy-saving process characteristics can be used to manufacture various thin-walled large-scale parts with high performance and complex shapes, and are widely used in transportation, machinery manufacturing, chemical industry, civil engi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More