Waterproof pulverized coal and preparation method thereof
A technology of pulverized coal and stearic acid, applied in the field of pulverized coal, can solve the problems of limited storage time, transportation mode and application field of pulverized coal, affecting the use of coal-water slurry, shortening the storage time, etc. Good performance and waterproof performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0016] Example 1 A waterproof coal powder and its preparation method
[0017] 1. A waterproof coal powder composed of the following components by weight: CaCO 3 10 parts, 1 part stearic acid, 89 parts coal powder with a particle size of 90 mesh.
[0018] 2. A preparation method of waterproof coal powder:
[0019] 1) Weigh the raw materials according to the above formula;
[0020] 2) After the above weighed raw materials are mixed and stirred uniformly, they are added to the drum heating reactor, and after the temperature is raised to 110°C, the rolling heating is maintained for 20 minutes to obtain the waterproof coal powder; wherein the temperature rise rate of the temperature rise is 2°C / min.
[0021] According to the method of DB51 / 172-1993, the performance test of the above-mentioned waterproof coal powder prepared in this embodiment shows that the water-resistant coal powder prepared in this embodiment has a hydrophobicity rate of 99%. Under 700mm water column pressure, 4 days wit...
Example Embodiment
[0022] Example 2 A waterproof coal powder and its preparation method
[0023] 1. A waterproof coal powder composed of the following components by weight: CaCO 3 10 parts, 1 part stearic acid, 89 parts coal powder with a particle size of 90 mesh, and 0.5 parts paraffin wax;
[0024] 2. A preparation method of waterproof coal powder:
[0025] 1) Weigh the raw materials according to the above formula;
[0026] 2) After the above weighed raw materials are mixed and stirred uniformly, they are added to the drum heating reactor, and after the temperature is raised to 110°C, the rolling heating is maintained for 20 minutes to obtain the waterproof coal powder; wherein the temperature rise rate of the temperature rise is 2°C / min.
[0027] According to the method of DB51 / 172-1993, the above-mentioned waterproof coal powder prepared in this embodiment was tested for performance, and the results showed that the water-resistant coal powder prepared in this embodiment had a water repellency rate o...
Example Embodiment
[0028] Example 3 A waterproof coal powder and its preparation method
[0029] 1. A waterproof coal powder consisting of the following parts by weight: 5 parts CaCO 3 , 5 parts of calcium stearate, 60 parts of coal powder with a particle size of 60 mesh and 1 part of paraffin wax.
[0030] 2. A preparation method of waterproof coal powder:
[0031] 1) Weigh the raw materials according to the above formula;
[0032] 2) After the above weighed raw materials are mixed and stirred uniformly, they are added to the rolling heating reactor, and after the temperature is raised to 130°C, the rolling heating is maintained for 40 minutes to obtain the waterproof coal powder; wherein the heating rate of the heating is 1°C / min.
[0033] According to the method of DB51 / 172-1993, the above-mentioned waterproof coal powder prepared in this embodiment was tested for performance, and the result showed that the water-repellent coal powder prepared in this embodiment had a water repellency rate of 98.5%. ...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap