Positive lead plaster containing superconducting material additive for lead storage battery

A technology of superconducting materials and lead-acid batteries, which is applied to lead-acid batteries, battery electrodes, circuits, etc., can solve the problems of large self-discharge, low stability, and poor low-temperature performance of batteries, so as to improve charging and receiving capabilities, hinder deposition, Effect of improving electrical conductivity and microstructure

Inactive Publication Date: 2016-04-06
JIANGSU HUAFU STORAGE NEW TECH DEV
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the battery has poor corrosion resistance, low stability, and large self-discharge, so the service life of the battery is short
At the same time, the low temperature performance of the battery is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention also discloses a preparation method of lead storage battery negative electrode paste containing superconducting material additives, comprising the following steps:

[0014] 1), weigh each component according to claim 1 weight component;

[0015] 2) Mix lead powder, superconducting material and short fiber evenly to obtain a mixed material for use; mix 50%-60% water and sulfuric acid evenly to obtain a mixed solution for use;

[0016] 3) Within 30 minutes, add the mixed solution while stirring the mixed material, add the remaining water after the mixed solution is completely added, and stir evenly to obtain a lead battery positive paste containing superconducting material additives.

[0017] The preparation method of the lead storage battery positive paste containing the superconducting material additive of the present invention is simple and convenient, the step design is reasonable, and the lead storage battery positive paste containing the superconductin...

Embodiment 1

[0020] First, according to 80 parts of lead powder, 10 parts of water, 9.8 parts of sulfuric acid, niobium trigermanium (Nb 3 Ge) 0.1 parts by weight of powder, 0.1 parts by weight of short fibers Weigh each component.

[0021] Secondly, the lead powder and niobium germanium (Nb 3 Ge) The superconducting material and the short fiber are fully mixed and set aside; 5 parts of water and sulfuric acid are mixed to form a uniform mixed solution.

[0022] Finally, add the mixed solution while stirring the solid mixed material within 30 minutes, add 5 parts of water after the mixed solution is completely added, and stir evenly to obtain a lead storage battery positive electrode paste with superconducting materials added. The lead paste can be used for subsequent production of batteries by mechanical or manual coating.

[0023] After testing, the conductivity of the positive plate is better, the battery charge acceptance ability is 1-2 times higher than that of the existing technolo...

Embodiment 2

[0025] First, according to 83 parts of lead powder, 10 parts of water, 6.3 parts of sulfuric acid, niobium trialuminum (Ne 3 Al) 0.5 parts by weight of powder, 0.2 parts by weight of short fibers Weigh each component.

[0026] Secondly, the lead powder, the niobium-tri-aluminum superconducting material and the short fiber are fully mixed and used for later use; 6 parts of water and sulfuric acid are mixed to form a uniform mixed solution.

[0027] Finally, add the mixed solution while stirring the solid mixed material within 30 minutes, add 4 parts of water after the mixed solution is completely added, and stir evenly to obtain the positive lead paste of the lead storage battery with the superconducting material added. The lead paste can be used for subsequent production of batteries by mechanical or manual coating.

[0028] After testing, the conductivity of the positive plate is better, the battery charge acceptance ability is 1-2 times higher than that of the existing tech...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a positive lead plaster containing a superconducting material additive for a lead storage battery. The positive lead plaster comprises the following components in parts by weight: 80-83 parts of lead powder, 10-15 parts of water, 4-10 parts of sulfuric acid, 0.1-0.5 part of a superconducting material and 0.1-0.2 part of a staple fiber. According to the positive lead plaster containing the superconducting material additive for the lead storage battery disclosed by the invention, with the superconducting material as the additive of the positive lead plaster for the lead storage battery, the superconducting material can be well fused with active materials of the lead plaster; the conductivity and the microstructure of a positive plate can be effectively improved; deposition of mass sulfate in a discharge process is hindered; the charge acceptance of the battery is improved; and the positive lead plaster can be widely applicable to various lead-acid storage battery products.

Description

technical field [0001] The invention belongs to the field of materials related to chemical power sources, and in particular relates to a positive electrode paste formula that can be used for lead storage batteries. Background technique [0002] Lead-acid batteries are widely used in power, energy storage, electric power, communication and other fields, with various types. The basic components involved in the electrochemical reaction in lead-acid batteries are positive electrode paste, negative electrode paste and electrolyte. Positive electrode paste is an important part that determines the overall capacity and performance of the battery. When preparing positive lead paste, conductive substances such as expanded graphite are generally added to improve the conductivity of the lead paste and increase the utilization rate of active materials. However, the corrosion resistance of the battery is poor, the stability is low, and the self-discharge is large, so the service life of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/57H01M4/62H01M10/06
CPCH01M4/57H01M4/624H01M4/626H01M4/628H01M10/06Y02E60/10
Inventor 吴战宇顾立贞李一平黄毅周寿斌王兴锋于尊奎
Owner JIANGSU HUAFU STORAGE NEW TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com