Method for preparing oligochitosan through self-resonating cavitation

A chitosan oligosaccharide and self-vibration cavitation technology, which is applied in the preparation field of chitosan oligosaccharides, can solve problems such as difficult to achieve efficient energy utilization, and achieve the effects of increased degradation rate, high efficiency, and low energy consumption

Active Publication Date: 2016-04-27
GUANGXI UNIVERSITY OF TECHNOLOGY
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cavitation bubble collapses quickly and cannot be fully grown before collapsing, so it is difficult to realize efficient utilization of energy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing oligochitosan through self-resonating cavitation
  • Method for preparing oligochitosan through self-resonating cavitation
  • Method for preparing oligochitosan through self-resonating cavitation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0030] Example: A method for preparing oligochitosan by self-vibration cavitation, including the following steps:

[0031] The first step: Chitosan dissolution: Add high molecular weight chitosan to a solvent to dissolve it to prepare a chitosan solution. The solvent is one of an inorganic acid aqueous solution, an organic acid aqueous solution or a slightly acidic buffer solution. Wherein, the mass concentration of the inorganic acid aqueous solution or the organic acid aqueous solution is 1%-13%, the pH of the buffer solution is 3-5, and the mass concentration of the chitosan solution is 0.5g / L- 5g / L, the relative molecular mass of the high molecular weight chitosan is greater than 2×10 6 , The degree of deacetylation is greater than 60%; the inorganic acid is hydrochloric acid, the organic acid is formic acid, acetic acid, lactic acid or citric acid, and the buffer solution is acetic acid-sodium acetate or citric acid-sodium citrate;

[0032] Step 2: Self-vibration cavitation de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of deacetylationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing oligochitosan through self-resonating cavitation. The method is characterized in that self-resonating cavitation degradation is adopted, that is, a chitosan solution is subjected to self-resonating cavitation degradation treatment in a self-resonating cavitation device; the self-resonating cavitation device comprises a thermostatic water-bath circulation water tank, a storage tank, a pump, a self-resonating cavitation device, a pipeline for conveying the chitosan solution, a pressure gauge and a valve; the technological process of self-resonating cavitation degradation is as follows: the chitosan solution is stored in the storage tank, subjected to thermostatic treatment by the circulation water tank and conveyed by the pump to the self-resonating cavitation device for cavitation degradation, the pressure of an inlet is adjusted by the valve, the pressure is monitored by the pressure gauge, and the chitosan solution subjected to cavitation degradation flows back to the storage tank. The degradation rate by using the method is at least 40% higher than that by using a hydrodynamic cavitation device (venturi tube) to prepare oligochitosan at present, and the method has the characteristics of simplicity, easiness, low energy consumption, high efficiency and the like and has the advantage of mass industrial application.

Description

Technical field [0001] The invention relates to a method for preparing oligochitosan, in particular to a method for preparing oligochitosan by self-vibration cavitation. Background technique [0002] Generally, chitosan prepared by deacetylation of chitin has a large molecular weight and a compact crystal structure. It is insoluble in common solvents and can only be dissolved in certain acidic media. This makes the application of chitosan greatly affected. limit. In addition, studies have shown that the properties of chitosan with different relative molecular masses are very different, and sometimes even show diametrically opposite characteristics. Many specific functions of chitosan can only be manifested when the relative molecular mass is reduced to a certain extent. The oligomeric water-soluble chitosan obtained by the degradation of chitosan has unique and superior physiological activity and physical and chemical properties, and has a wide range of application fields and de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08B37/08
CPCC08B37/003
Inventor 黄永春杨锋李利军许佳丽任仙娥黄承都黄琼谢清若张昆明
Owner GUANGXI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com