Antioxidant composition, modified polyformaldehyde resin composition and modified polyformaldehyde resin and preparation method thereof

A technology of polyoxymethylene resin and composition, which is applied in the field of modified polyoxymethylene resin, and can solve the problems of high price of antioxidant and impact on POM production cost, etc.

Active Publication Date: 2016-08-24
CHNA ENERGY INVESTMENT CORP LTD +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to achieve a better anti-thermal oxygen effect, a large amount of antioxidant is usually required, and the price of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antioxidant composition, modified polyformaldehyde resin composition and modified polyformaldehyde resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The preparation method of the modified polyoxymethylene resin provided by the present invention comprises melting, extruding and granulating the above-mentioned modified polyoxymethylene resin composition at 180-225° C., and then drying.

[0024] According to the preparation method of the modified polyoxymethylene resin provided by the present invention, the method also preferably includes mixing the components in the modified resin composition uniformly before melt extrusion granulation, which is more conducive to the Improvement of thermal stability of polyoxymethylene resin. The step of melt extrusion granulation can usually be carried out in an existing single-screw extruder or twin-screw extruder. In addition, the drying conditions generally include that the drying temperature may be 50-100° C., and the drying time may be 1-10 hours.

[0025] The present invention also provides the modified polyoxymethylene resin prepared by the above method.

Embodiment 1

[0028] This example is used to illustrate the antioxidant composition, the modified polyoxymethylene resin composition, the modified polyoxymethylene resin and the preparation method thereof provided by the present invention.

[0029] 100 parts by weight of polyoxymethylene resin (purchased from Shenhua Ningxia Coal Group Coal Chemical Branch, brand name is MC90G, the same below), 0.5 parts by weight of diphenylmethane-4,4'-diisocyanate (MDI) (Alfa Aesar company, The same below), 1 part by weight of 2,2,6,6-tetramethylpiperidine-nitrogen-oxide (TEMPO), 0.5 part by weight of antioxidant triethylene glycol bis[β-(3-tert-butyl Base-4-hydroxyl-5-methylphenyl) propionate] (antioxidant 245), 0.5 parts by weight of melamine, 0.5 parts by weight of magnesium hydroxide are uniformly mixed and then melted and extruded by a vented twin-screw extruder For granulation, the extrusion temperature is 180°C-225°C, the screw speed is 100 rpm, and after granulation, it is dried at 80°C for 2 hou...

Embodiment 2

[0031] This example is used to illustrate the antioxidant composition, the modified polyoxymethylene resin composition, the modified polyoxymethylene resin and the preparation method thereof provided by the present invention.

[0032] 100 parts by weight of polyoxymethylene resin, 2 parts by weight of diphenylmethane-4,4'-diisocyanate (MDI), 1 part by weight of 2,2,6,6-tetramethylpiperidine-nitrogen-oxide (TEMPO ), 1 part by weight of polyamide PA6 / 12 (purchased from EMS Swiss Chemical Co., Ltd., the brand is Grilamid, the same below), 0.5 parts by weight of antioxidant tetrakis[β-(3,5-di-tert-butyl-4-hydroxy Phenyl) propionic acid] pentaerythritol ester (antioxidant 1010), 0.5 parts by weight of melamine, and 0.5 parts by weight of magnesium hydroxide are evenly mixed and then melted and extruded to granulate with a vented twin-screw extruder at an extrusion temperature of 180°C -225°C, the screw speed is 100 rpm, and after granulation, it is dried at 80°C for 2 hours to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an antioxidant composition, a modified polyformaldehyde resin composition and modified polyformaldehyde resin and a preparation method thereof. The antioxidant composition is prepared from, by weight, 0.5-2 parts of an isocyanate compound, 0.5-1 part of a free radical capturing agent and 0.5-1.3 parts of a formaldehyde absorbent, wherein the free radical capturing agent is selected from at least one of 2,2,6,6-tetramethylpiperidine-nitrogen-oxide, 2,2-diphenyl-1-trinitrophenylhydrazine, p-benzoquinone, tetramethyl-benzoquinone, N-tert-butyl-alpha-phenylnitrone and 3-2-(2-bromoacetyl amino)acetamide-2,2,5,5-tetramethyl-1-pyrrolidyl oxide, and polyamide can be adopted as the formaldehyde absorbent. When polyformaldehyde resin is modified by the antioxidant composition, the heat stability of the polyformaldehyde resin can be very significantly improved.

Description

technical field [0001] The present invention relates to an antioxidant composition, a modified polyoxymethylene resin composition containing the antioxidant composition, a preparation method of modified polyoxymethylene resin and a modified polyoxymethylene resin prepared by the method. Formaldehyde resin. Background technique [0002] Polyoxymethylene (POM) has poor thermal stability due to its special molecular structure, so the thermal stabilization of POM is the most important and basic key technology in its synthesis, processing and application. POM is prone to thermal action and oxygen action during the melting process. Once its molecules generate free radicals, they will undergo chain scission, and then a continuous formaldehyde removal reaction will occur. The formaldehyde and the trace amount of formic acid generated by the oxidation of formaldehyde will promote the thermal decomposition process and greatly accelerate the formaldehyde removal reaction until the mac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L59/00C08L77/02C08L77/06C08K13/02C08K5/3492C08K3/22C08K5/098C08K5/3435C08K5/521C08K5/134C08K5/29
Inventor 孙小杰梁文斌马伊张寅灵赖世燿
Owner CHNA ENERGY INVESTMENT CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap