Nanometer anion function material for wallpaper and preparation method thereof
A nano-anion and functional material technology, which is applied in the field of nano-anion functional materials for wallpaper and its preparation, can solve the problems of difficulty in developing negative-ion wallpapers and limited research, and achieve excellent air purification effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A nano-anion functional material for wallpaper, made of the following raw materials by weight (kg): hydromica 20, magnetic wave stone 18, palygorskite 10, black tourmaline 14, montmorillonite 15, titanium dioxide 5, Huangshan ball stone 21 , porous powder quartz 10, heavy calcium powder 5.
[0017] A preparation method of nano anion functional material for wallpaper, comprising the following steps:
[0018] (1) Mix hydromica, magnetic wave stone, palygorskite, black tourmaline, montmorillonite, and Huangshan ballstone, calcinate at 410°C for 4h, cool to room temperature, crush into particles with a particle size of 30μm, and add an appropriate amount of Stir with water to make a suspension with a concentration of 50%, then adjust the pH of the suspension to 8.5 with a 15% sodium hydroxide solution, treat with microwaves for 1.5 hours, microwave power is 350W, magnetically oscillate for 2 hours, and the oscillation frequency is 300Hz. Adjust the pH of the suspension to ...
Embodiment 2
[0022] A nano-anion functional material for wallpaper, made of the following raw materials by weight (kg): hydromica 25, magnetic wave stone 22, palygorskite 15, black tourmaline 18, montmorillonite 20, titanium dioxide 8, Huangshan ball stone 26 , Porous powder quartz 12, heavy calcium powder 7.
[0023] A preparation method of nano anion functional material for wallpaper, comprising the following steps:
[0024] (1) Mix hydromica, magnetic wave stone, palygorskite, black tourmaline, montmorillonite, and Huangshan ballstone, calcinate at 440°C for 3.5h, cool to room temperature, crush into particles with a particle size of 40μm, and add appropriate amount of Stir with water to make a suspension with a concentration of 52%, then adjust the pH of the suspension to 8.8 with a 15% sodium hydroxide solution, treat with microwaves for 2 hours, microwave power is 300W, magnetic oscillation is 2.5 hours, and the oscillation frequency is 250Hz. The pH of the suspension was adjusted t...
Embodiment 3
[0028] A nano-anion functional material for wallpaper, made of the following raw materials by weight (kg): hydromica 30, magnetic wave stone 26, palygorskite 20, black tourmaline 22, montmorillonite 25, titanium dioxide 10, Huangshan ball stone 29 , Porous powder quartz 15, heavy calcium powder 10.
[0029] A preparation method of nano anion functional material for wallpaper, comprising the following steps:
[0030] (1) Mix hydromica, magnetic wave stone, palygorskite, black tourmaline, montmorillonite, and Huangshan ballstone, calcinate at 460°C for 3h, cool to room temperature, crush into particles with a particle size of 60μm, and add an appropriate amount of Stir with water to make a suspension with a concentration of 55%, then adjust the pH of the suspension to 9 with a sodium hydroxide solution with a concentration of 15%, treat with microwaves for 2.5 hours, the microwave power is 250W, magnetic oscillation is 3 hours, and the oscillation frequency is 150Hz. Adjust the...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
clearance rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com