A self-leveling type II polymer cement waterproof mortar

A waterproof mortar and polymer technology, applied in the field of waterproof mortar, can solve the problems of poor impermeability and durability, and achieve the effects of increasing the setting and hardening speed, shortening the final setting time, and high construction efficiency

Active Publication Date: 2019-08-13
SHANDONG YINGCAI UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Solve the durability problem of ordinary self-leveling mortar due to the high content of high-alumina cement components resulting in poor long-term waterproof and impermeable performance, and realize the self-leveling construction of polymer cement waterproof mortar, which can be applied to various building waterproofing projects, such as toilets and kitchens , roofs, swimming pools, underground structures, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A self-leveling type II polymer cement waterproof mortar
  • A self-leveling type II polymer cement waterproof mortar
  • A self-leveling type II polymer cement waterproof mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A self-leveling type II polymer cement waterproof mortar, the formula is as follows: 85 parts of ordinary portland cement, 15 parts of composite hardening accelerator, 12 parts of fly ash, 0.8 parts of polycarboxylate superplasticizer powder, organic silicon hydrophobic 0.6 parts of agent, 0.3 parts of hydroxypropyl methylcellulose ether, 2 parts of VAE redispersible latex powder, 0.3 parts of defoamer, 90 parts of fine quartz sand, and 45 parts of water.

[0040] Among them, the composition of the composite hardening accelerator: 5 parts of quicklime, 4 parts of sodium sulfate, and 6 parts of aluminate cement.

[0041] Preparation method: Mix quicklime, sodium sulfate, and aluminate cement evenly to obtain a composite hardening accelerator;

[0042] Portland cement, composite hardening accelerator, fly ash, polycarboxylate superplasticizer powder, silicone water repellent, hydroxypropyl methylcellulose ether, VAE redispersible latex powder, defoamer, Mix fine quartz s...

Embodiment 2

[0047] A self-leveling type II polymer cement waterproof mortar, the formula is as follows: 80 parts of ordinary Portland cement, 15 parts of composite hardening accelerator, 10 parts of fly ash, 0.5 parts of polycarboxylate superplasticizer powder, organic silicon hydrophobic 0.4 parts of agent, 0.2 parts of hydroxypropyl methylcellulose ether, 1 part of VAE redispersible latex powder, 0.2 parts of defoamer, 80 parts of fine quartz sand, and 40 parts of water.

[0048] Among them, the composition of the composite hardening accelerator: 3 parts of quicklime, 2 parts of sodium sulfate, and 5 parts of aluminate cement.

[0049] Preparation method: Mix quicklime, sodium sulfate, and aluminate cement evenly to obtain a composite hardening accelerator;

[0050]Portland cement, composite hardening accelerator, fly ash, polycarboxylate superplasticizer powder, silicone water repellent, hydroxypropyl methylcellulose ether, VAE redispersible latex powder, defoamer, Mix fine quartz san...

Embodiment 3

[0053] A self-leveling type II polymer cement waterproof mortar, the formula is as follows: 85 parts of ordinary Portland cement, 20 parts of composite hardening accelerator, 15 parts of fly ash, 1 part of polycarboxylate superplasticizer powder, organic silicon hydrophobic 0.8 parts of agent, 0.4 parts of hydroxypropyl methylcellulose ether, 3 parts of VAE redispersible latex powder, 0.4 parts of defoamer, 100 parts of fine quartz sand, and 50 parts of water.

[0054] Among them, the composition of the composite hardening accelerator: 6 parts of quicklime, 5 parts of sodium sulfate, and 10 parts of aluminate cement.

[0055] Preparation method: Mix quicklime, sodium sulfate, and aluminate cement evenly to obtain a composite hardening accelerator;

[0056] Portland cement, composite hardening accelerator, fly ash, polycarboxylate superplasticizer powder, silicone water repellent, hydroxypropyl methylcellulose ether, VAE redispersible latex powder, defoamer, Mix fine quartz sa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a self-leveling type II polymer cement waterproof mortar. The mortar includes: Portland cement, composite hardening agent, aggregate, water, polymer, and other additives, wherein the composite hardening agent is composed of the following raw materials in parts by weight: quicklime 3-6 parts, sodium sulfate 2 ‑5 parts, 5‑10 parts of aluminate cement. Solve the durability problem of ordinary self-leveling mortar due to the high content of high-alumina cement components resulting in poor long-term waterproof and impermeable performance, and realize the self-leveling construction of polymer cement waterproof mortar, which can be applied to various building waterproofing projects, such as toilets and kitchens , roofs, swimming pools, underground structures, etc.

Description

technical field [0001] The invention belongs to the field of waterproof mortar, in particular to a self-leveling type II polymer cement waterproof mortar. Background technique [0002] At present, the polymer cement waterproof mortar still adopts the complicated construction method of layering and batching. There are many defects in this construction method: poor flatness, difficulty in guaranteeing construction quality, long construction period, high construction intensity, and low labor efficiency. In addition, the bonding between the mortar surface and the concrete base is poor, and cracks are prone to occur, which reduces the overall impermeability of the structure. [0003] In order to change the traditional construction method and promote the improvement of construction technology and construction quality, it is necessary to introduce self-leveling technology into the preparation and construction of waterproof mortar. However, in order to obtain rapid hardening and e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B111/60C04B111/62
CPCC04B28/06C04B2111/60C04B2111/62C04B7/02C04B22/147C04B22/064C04B18/08C04B2103/302C04B24/42C04B24/383C04B2103/0057C04B2103/50C04B14/06C04B24/045
Inventor 丰曙霞
Owner SHANDONG YINGCAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap