A method for implanting a sound-absorbing diaphragm of an embedded sound-absorbing honeycomb and an implanting tool

An embedded, honeycomb technology, applied in chemical instruments and methods, lamination devices, transportation and packaging, etc., can solve the problems of difficult implantation operations, increase the overall weight of the honeycomb, reduce the overall weight and facilitate the implantation operation. Effect

Active Publication Date: 2019-03-19
AVIC BASIC TECH RES INST
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method has the following problems: First, most membrane materials are difficult to maintain the flanging state for a long time without external constraints, and often quickly develop into a planar shape after the external constraints are removed, making it difficult to plant. Second, in order to fix the diaphragm, the entire honeycomb needs to be immersed in the glue tank to re-dip the glue, which increases the overall weight of the honeycomb

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for implanting a sound-absorbing diaphragm of an embedded sound-absorbing honeycomb and an implanting tool
  • A method for implanting a sound-absorbing diaphragm of an embedded sound-absorbing honeycomb and an implanting tool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1. Choose NH-1-5.5-48 honeycomb produced by AVIC Composite Materials, and process a piece of aramid paper honeycomb with a thickness of 30mm and a cell size of 5.5mm, and reserve it;

[0027] 2. Manufacture the blank of the muffler diaphragm:

[0028] 2.1. Choose a piece of Sefa 75-25BHY acoustic mesh;

[0029] 2.2. Select the SY-24C epoxy resin film produced by Beijing Institute of Aeronautical Materials, and print regular hexagonal hollow patterns on the acoustic cloth. The regular hexagonal pattern is the hollow part, and the rest is the film. The side length of the regular hexagon is 5.5mm, and the distance between the centers of adjacent regular hexagons is 18mm;

[0030] 2.3. Cut the acoustic cloth into a square piece with a side length of 18mm;

[0031] 3. Implantation of anechoic diaphragm blank:

[0032] 3.1. Using the implant tool, insert the cut acoustic diaphragm blank into the honeycomb unit at a height of 15mm, and pull out the implant tool after stayin...

Embodiment 2

[0035] 1. Select the aluminum honeycomb with the brand name LF2Y-5-0.06-49 produced by AVIC Composite Materials, and process a piece of aluminum honeycomb with a thickness of 30mm and a cell size of 5mm for spare;

[0036] 2. Manufacture the blank of the muffler diaphragm:

[0037] 2.1. Choose a piece of Sefa 145-27BHY acoustic mesh;

[0038] 2.1. Choose a piece of Sefa 75-25BHY acoustic mesh;

[0039] 2.2. Select the SY-24C epoxy resin film produced by Beijing Institute of Aeronautical Materials, and print regular hexagonal hollow patterns on the acoustic cloth. The regular hexagonal pattern is the hollow part, and the rest is the film. The side length of the regular hexagon is 5.5mm, and the distance between the centers of adjacent regular hexagons is 18mm;

[0040] 2.3. Cut the acoustic cloth into a square piece with a side length of 18mm;

[0041] 3. Implant the blank of the sound-absorbing diaphragm 2:

[0042] 3.1. Using the implant tool, insert the cut acoustic diap...

Embodiment 3

[0045]1. Choose NH-1-4.5-60 honeycomb produced by AVIC Composite Materials, and process a piece of aramid paper honeycomb with a thickness of 20mm and a cell size of 4.5mm, and reserve it;

[0046] 2. Manufacture the blank of the muffler diaphragm:

[0047] 2.1. Choose a piece of Sefa 145-27BHY acoustic mesh;

[0048] 2.2. Select the SY-24C epoxy resin film produced by Beijing Institute of Aeronautical Materials, and print regular hexagonal hollow patterns on the acoustic cloth. The regular hexagonal pattern is the hollow part, and the rest is the film. The side length of the regular hexagon is 5.5mm, and the distance between the centers of adjacent regular hexagons is 15mm;

[0049] 2.3. Cut the acoustic cloth into circular pieces with a diameter of 15mm;

[0050] 3. Implant the blank of the sound-absorbing diaphragm 2:

[0051] 3.1. Using the implant tool, insert the cut acoustic diaphragm blank into the honeycomb unit at a height of 15mm, and pull out the implant tool af...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to a functional honeycomb manufacturing technology and relates to a manufacturing method and an implanting tool of an embedded anechoic honeycomb. An anechoic diaphragm comprises the following implanting steps: selecting a honeycomb substrate; determining the position of an anechoic diaphragm (2) on the uppermost layer; gumming the honeycomb; manufacturing an anechoic diaphragm blank board; implanting the anechoic diaphragm (2). The invention provides the manufacturing method and the implanting tool of the embedded anechoic honeycomb, which have the advantages that the processes are simplified, the manufacturing efficiency is improved, and the manufacturing cost is reduced.

Description

technical field [0001] The invention belongs to the functional honeycomb manufacturing technology, and relates to a method for implanting a sound-absorbing diaphragm of a built-in sound-absorbing honeycomb and an implanting tool. Background technique [0002] The embedded sound-absorbing honeycomb was first proposed by Hexcel Corporation of the United States, and has been successfully applied in the sound-absorbing liners of aircraft engines such as A380. In this structure, because the sound-absorbing diaphragm in each honeycomb unit divides the air layer into multiple closed sub-cavities, this kind of embedded sound-absorbing honeycomb is implanted with micro-perforated partitions or partitions at a certain height of the honeycomb space. The diaphragm not only achieves the purpose of the multi-degree-of-freedom sound-absorbing structure, but also avoids a series of shortcomings of the traditional multi-degree-of-freedom sound-absorbing structure. U.S. Patent No. 7,434,659B...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B3/12B32B1/06B32B37/14
CPCB32B3/085B32B3/12B32B37/146B32B2305/024B32B2305/028B32B2307/102B32B2605/18
Inventor 纪双英史湘宁王芙蓉许健翔刘杰
Owner AVIC BASIC TECH RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap