Process for separating lead and bismuth from high bismuth lead alloy

A bismuth-lead alloy and a technology for separating lead, which can be applied in photography technology, photography auxiliary technology, improvement of process efficiency, etc., can solve the problems of easy dispersion of gold and silver, difficulty in separation, complicated process, etc.

Active Publication Date: 2017-09-19
YIYANG SHENGLI CHEM IND
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These methods avoid smoke and dust pollution in the fire process and improve working conditions, but there are still disadvantages such as complicated procedures, easy dispersion of gold and silver in the oxidation leaching process, large consumption of reagents, and difficult separation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for separating lead and bismuth from high bismuth lead alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The composition of the high-bismuth-lead anode alloy cast from high-bismuth-lead anode slime provided by a company in Hunan is: Bi40.1%, Cu 1.9%, Pb 51.4%, Sb 4.5%, Ag 1.9%.

[0032]The high bismuth-lead alloy was used as the anode (length 12cm×width 8cm×thickness 2cm), graphite was used as the cathode for pulse chlorination electrolysis in the HCl-NaCl system, and the anode was placed in a canvas anode bag. The pulse frequency of the pulsed electric field during electrolysis is 500Hz, the duty cycle is 60%, and the pulse average current density is 700A / m 2 , the temperature is 60°C, the distance between cathode and anode is 6cm, the volume of electrolyte is 1L, the concentration of HCl in the electrolyte is 3mol / L, and the concentration of NaCl is 100g / L. Under these conditions, the reaction was stopped after 10 hours of electrolysis, the liquid and solid were separated, the cathode sponge bismuth powder was rinsed twice with 50 ml of hot water and then dried, and the ...

Embodiment 2

[0035] The composition of the high-bismuth-lead anode alloy cast from high-bismuth-lead anode slime provided by a company in Yunnan is: Bi38.3%, Cu 2.3%, Pb 52.7%, Sb 5.1%, Ag 1.3%.

[0036] This high bismuth lead alloy is used as the anode (length 18cm×width 10cm×thickness 2cm), and the titanium plate is used as the cathode in HCl-NH 4 Pulse chlorination electrolysis was carried out in the Cl system, and the anode was placed in a canvas anode bag. The pulse frequency of the pulse electric field is 1200Hz, the duty cycle is 70%, and the pulse average current density is 600A / m 2 , the temperature is 70°C, the distance between cathode and anode is 7cm, the volume of electrolyte is 1.5L, the concentration of HCl in the electrolyte is 4mol / L, NH 4 Cl concentration is 80g / L. Under these conditions, the reaction was terminated after 18 hours of electrolysis, and the liquid and solid were separated. The cathode sponge bismuth powder was washed twice with 100 ml of hydrochloric acid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a process for separating lead and bismuth from a high bismuth lead alloy; and the process uses an alloy formed by casting high bismuth lead anode mud as an anode; and the alloy is fed in an anode bag for pulse chlorination electrolysis in a hydrochloric acid-chlorine salt system. Insoluble matters of the anode fall into the anode bag to form anode mud during electrolyzing; lead is dissolved in solution in a lead-chlorine complex form; and bismuth is separated out from a cathode in a rough bismuth powder form. The anode mud, lead chloride complex solution and rough bismuth powder are respectively obtained after electrolysis. The lead chloride solution is cooled for crystallization to obtain lead chloride; and crystallization mother liquor is returned to prepare electrolyte. The oxidation leaching is performed on the rough bismuth powder by adopting methane sulfonic acid to respectively obtain leaching liquid and leaching slag enriched with antimony and silver. The leaching liquid is replaced and purified for pulse electrodeposition to obtain electric bismuth; and electrodeposition back liquid is returned to leaching of the rough bismuth powder. The process can perform classified extraction on lead and bismuth in the high bismuth lead alloy; silver is enriched; the closed cycle of the technological process is realized; and the process has the advantages of simple technological process, high yield of valuable elements, cleanness and environmental protection.

Description

technical field [0001] The invention belongs to the field of hydrometallurgy, and in particular relates to a process for separating lead and bismuth from a high-bismuth-lead alloy. Background technique [0002] During the electrolytic refining of crude lead, because the standard electrode potential of Sb, As, Bi, Cu, Ag, Au and other metals is more positive than that of Pb, these metals are rarely dissolved into the electrolyte but adhere to the surface of the anode in solid form or fall off the electrolytic tank Anode slime is formed in the anode slime, because it is enriched with 5-30% bismuth, 5-45% antimony, 1-10% copper, 1-20% bismuth, 10-1500g / t gold, 1-20% Silver and 5-30% lead, 0.1-30% arsenic and other elements, so it is of great significance to realize its clean treatment and efficient recycling. Especially in recent years, the proportion of high-bismuth lead raw materials has gradually increased, and the bismuth content in the anode slime obtained during the elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25C5/02C25B1/26C25C1/22C22B30/06C22B7/00C22B30/02C22B11/00C22B15/00
CPCC22B7/007C22B11/042C22B15/0091C22B30/02C22B30/06C25B1/26C25C1/22C25C5/02Y02P10/20
Inventor 杨建广南天翔丁龙杨建英李树超陈冰
Owner YIYANG SHENGLI CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap