Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A Stirring Head Power Supply Assisted Composite Biaxial Friction Stir Welding Method

A friction welding and biaxial stirring technology, applied in welding equipment, non-electric welding equipment, metal processing equipment, etc., can solve the problems of low welding speed, wear of stirring head, heavy equipment, etc., to improve welding speed, increase strength, reduce Effects of Welding Defects

Active Publication Date: 2019-07-02
XI AN JIAOTONG UNIV
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in the special high temperature environment of friction stir welding, when welding metal materials with high melting point, the wear of the stirring head is serious, and the equipment is generally heavy and complicated.
In addition, when welding materials with high melting point and large thickness, the welding speed is often low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Stirring Head Power Supply Assisted Composite Biaxial Friction Stir Welding Method
  • A Stirring Head Power Supply Assisted Composite Biaxial Friction Stir Welding Method
  • A Stirring Head Power Supply Assisted Composite Biaxial Friction Stir Welding Method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be described in detail below in conjunction with the accompanying drawings.

[0020] refer to figure 1 , figure 2 , image 3 with Figure 4 , a composite biaxial friction stir welding method powered by a stirring head, comprising the following steps:

[0021] 1) Clamping and fixing the first workpiece 1 to be welded and the second workpiece 2 to be welded on the welding workbench, the seam gap between the first workpiece 1 to be welded and the second workpiece 2 to be welded is 0-0.6 mm; The welding workbench and workpiece fixture need to be insulated to prevent the danger of equipment leakage; before clamping, it is necessary to clean the joint surface of the first workpiece 1 to be welded and the second workpiece 2 to be welded to remove oil. Remove oxide film;

[0022] 2) The first workpiece 1 to be welded, the second workpiece 2 to be welded, the first stirring head 3, and the second stirring head 4 are connected by the first stirrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stirring head power supply-assisted composite double-shaft friction stir welding method. The method comprises the steps that stirring friction heads are adopted as electrodes of a resistor heat source, high-density currents are provided for the interior of a to-be-welded workpiece through a direct-current switch power supply, and the resistor-assisted heat source is provided for the stirring heads rotating at a high speed in the friction stir welding process; the stirring heads rotating at the high speed are inserted into the two sides of a joint, and upsetting pressure is exerted to metal at the joint through a shaft shoulder, so that the metal material at the joint is softened; the metal structure at the joint achieves a plasticizing state under the stirring effect through the stirring heads, and meanwhile micro-forging treatment is conducted on the plasticized metal by adopting an ultrasonic vibration exciter, so that metal structure crystalline grains at the joint are refined; the stirring heads do forward feeding motion in the direction of the joint, a cavity formed after a stirring needle moves is continuously filled with the plasticized metal under the stirring and extruding effect of the stirring heads, and the plasticized metal is gradually cooled and solidified to form a welding joint. According to the method, wear of the stirring heads is reduced, the welding thickness is increased, the welding speed is increased, and welding defects are reduced.

Description

technical field [0001] The invention belongs to the technical field of friction stir welding and forming, and in particular relates to a composite biaxial friction stir welding method powered by a stirring head. Background technique [0002] Friction stir welding (FSW) is a solid phase welding technology, originally used for the connection of low melting point metals (such as aluminum alloys and magnesium alloys, etc.), because there is no melting of materials in the FSW process, so this technology can avoid traditional fusion welding Common problems such as cracks, pores and deformation, and have low requirements for operation and equipment. Although the research on friction stir welding technology has been more and more in-depth, but there are still deficiencies in this technology. [0003] Friction stir welding mainly stirs the workpiece through the stirring head, and relies on frictional heat to heat the metal around the joint of the workpiece to a plastic state to real...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K20/12B23K20/26
CPCB23K20/123B23K20/1245B23K20/26
Inventor 赵升吨张鹏李靖祥董渊哲董朋
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com