Ultra-light anti-adhesion release film preparation method

A release film and anti-adhesion technology, applied in the pulp raw material addition process, coating, paper coating and other directions, can solve the problem that the customer's requirements for ultra-light release film cannot be met, the ultra-light requirements cannot be met, and the film is sticky. and other problems, to achieve the effect of equalizing pressure, improving drying efficiency, and smoothing the film surface

Active Publication Date: 2017-11-10
江阴华美光电科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main problem of ordinary PET release film is that the peeling force is above 10g, which cannot meet the ultra-light requirement. If the peeling force is below 5g, the film will stick to the surface, which cannot meet the customer's requirements for ultra-light release film. membrane requirements
Several major technical problems that need to be solved for ultra-light anti-adhesion release film are: 1. Stability of peeling force: range of release force; Obvious rainbow pattern; 3. Problems such as stickiness of the film surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-light anti-adhesion release film preparation method
  • Ultra-light anti-adhesion release film preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Step 1, the first coating process

[0034] 1. Coating configuration: Mix 3 parts of D120 solvent oil, 3 parts of D30 solvent oil, 4 parts of butanone and 1 part of isopropanol as solvent, add 1 part of 7458 silicone oil main agent, 0.1 part of 7672 crosslinking agent, 297 anchoring agent 0.02 parts and 0.05 parts of 4000 catalysts, stirred at 1200 rpm for 30 minutes, filtered through a 200-mesh filter, and used within 3 hours;

[0035] 2. Original film treatment: the corona value is greater than 50 during corona treatment, and the gap between any two points is guaranteed not to exceed 5; thereby enhancing the adhesion of the film surface; dust removal treatment uses a double-sided dust removal device to effectively reduce the original film Floating dust on the surface greatly improves the cleanliness of the product;

[0036] 3. Precise coating: apply the configured coating on the surface of the original film through the coating machine, the coating method is reverse co...

Embodiment 2

[0048] Step 1, the first coating process

[0049] 1. Coating configuration: Mix 4 parts of D120 solvent oil, 4 parts of D30 solvent oil, 5 parts of butanone and 1.5 parts of isopropanol as solvent, add 1.2 parts of 7458 silicone oil main agent, 0.2 parts of 7672 crosslinking agent, 297 anchoring agent 0.03 parts and 0.06 parts of 4000 catalysts, stirred at 1300 rpm for 40 minutes, filtered through a 230-mesh filter, and used within 3.5 hours;

[0050] 2. Original film treatment: the corona value is greater than 50 during corona treatment, and the gap between any two points is guaranteed not to exceed 5; thereby enhancing the adhesion of the film surface; dust removal treatment uses a double-sided dust removal device to effectively reduce the original film Floating dust on the surface greatly improves the cleanliness of the product;

[0051] 3. Precise coating: apply the configured coating on the surface of the original film through the coating machine, the coating method is rev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
hazeaaaaaaaaaa
Login to View More

Abstract

The present invention discloses an ultra-light anti-adhesion release film preparation method, which comprises: 1, mixing 3-4 parts of D120 solvent oil, 3-4 parts of D30 solvent oil, 4-5 parts of butanone, and 1-1.5 parts of isopropanol to obtain a mixture as a solvent, adding 1-1.2 parts of a 7458 silicone oil main agent, 0.1-0.2 part of a 7672 cross-linking agent, 0.02-0.03 part of a 297 anchoring agent, and 0.05-0.06 part of a 4000 catalyst, stirring for 30-40 min at a speed of 1200-1300 rotation / min, filtering with a 200-230 mesh filtration screen, using within 3-3.5 h, carrying out raw film treatment, precisely coating, carrying out drying curing, and carrying out material receiving winding; 2, mixing 2-2.5 parts of D120 solvent oil, 2-2.5 parts of D30 solvent oil, 2.5-3 parts of butanone and 0.8-1.2 parts of isopropanol to obtain a mixture as a solvent, adding 0.8-1 part of a 9106 silicone oil main agent, 0.1-0.2 part of a 7672 cross-linking agent, 0.02-0.03 part of a 297 anchoring agent, and 0.06 part of a 4000 catalyst, stirring for 30-40 min at a speed of 1200-1300 rotation / min, filtering with a 200-230 mesh filtration screen, using within 3-3.5 h, carrying out raw film treatment, precisely coating, carrying out drying curing, and carrying out material receiving winding; and 3, carrying out post-curing treatment. According to the present invention, the produced release film has the light transmittance of more than 88%, has the mist degree of less than 3, and has the peel force stability (normal temperature) of 3-5 g.

Description

technical field [0001] The invention relates to the technical field of film coating, in particular to a preparation method of an ultra-light anti-adhesion release film. Background technique [0002] Release paper, also known as release paper and anti-adhesive paper, is mainly used to stick the adhesive layer on the surface of the tape to protect the surface of the tape. The existing release paper is generally coated with a film layer (the material used is mainly polyethylene) on the surface of the bottom paper layer of the release paper, and then coated with a layer of release agent coating on the surface of the film layer (The material used is mainly silicone oil) to form a release film to obtain a release paper. The main problem of ordinary PET release film is that the peeling force is above 10g, which cannot meet the ultra-light requirement. If the peeling force is below 5g, the film will stick to the surface, which cannot meet the customer's requirements for ultra-light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/46D21H23/56D21H23/46D21H27/00
CPCD21H19/46D21H23/46D21H23/56D21H27/00
Inventor 王上丹吴祥赵伟达
Owner 江阴华美光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com