Aluminum alloy welding wire for automobile fuel tank and preparation method of aluminum alloy welding wire

A technology of aluminum alloy welding wire and automobile fuel tank, which is applied in the direction of welding equipment, metal processing equipment, welding medium, etc., and can solve the problems of damage to the weld, impact resistance of the weld of the fuel tank, low fatigue resistance, oil leakage, etc.

Inactive Publication Date: 2017-12-01
安徽飞弧焊业股份有限公司
View PDF7 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of the automobile industry, people have higher and higher requirements for the lightness of automobiles. Replacing steel fuel tanks with aluminum alloy fuel tanks can reduce the weight of automobiles. How

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy welding wire for automobile fuel tank and preparation method of aluminum alloy welding wire

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1

[0015] An aluminum alloy welding wire for automobile fuel tanks. Its raw materials include Mg: 6.5%, Mn: 0.65%, Ti: 0.17%, Be: 0.003%, Fe: 0.3%, B: 0.045%, and Cr: 0.235% by weight. , Si: 0.35%, Zr: 0.2%, V: 0.175%, Sc: 0.25%, Cu≤0.1%, Zn≤0.2%, individual content of other impurity elements≤0.05%, total content of other impurity elements≤0.1%, remaining The amount is Al.

[0016] The method for preparing aluminum alloy welding wire for automobile fuel tanks includes the following steps: melting the aluminum ingot, adding the remaining raw materials, smelting, refining, and casting to obtain a round ingot meeting the above composition range; homogenizing, extruding, and Annealing and drawing treatments obtain aluminum alloy welding wire for automobile fuel tank.

Example Embodiment

[0017] Example 2

[0018] An aluminum alloy welding wire for automobile fuel tanks. Its raw materials include Mg: 6.3%, Mn: 0.8%, Ti: 0.16%, Be: 0.005%, Fe: 0.2%, B: 0.08%, and Cr: 0.22% by weight. , Si: 0.4%, Zr: 0.16%, V: 0.2%, Sc: 0.2%, Cu≤0.1%, Zn≤0.2%, single content of other impurity elements≤0.05%, total content of other impurity elements≤0.1%, remaining The amount is Al.

[0019] The method for preparing aluminum alloy welding wire for automobile fuel tanks includes the following steps: melting the aluminum ingot, adding the remaining raw materials, smelting, refining, and casting to obtain a round ingot meeting the above composition range; homogenizing, extruding, and Annealing and drawing treatments obtain aluminum alloy welding wire for automobile fuel tank, wherein the homogenization temperature is 475℃, homogenization temperature is 24h, extrusion temperature is 440℃, extrusion ratio is 40, annealing temperature is 460℃, annealing time For 2h.

Example Embodiment

[0020] Example 3

[0021] An aluminum alloy welding wire for automobile fuel tanks. Its raw materials include Mg: 6.7%, Mn: 0.5%, Ti: 0.18%, Be: 0.0001%, Fe: 0.4%, B: 0.01%, Cr: 0.25% by weight percentage. , Si: 0.3%, Zr: 0.25%, V: 0.15%, Sc: 0.3%, Cu≤0.1%, Zn≤0.2%, individual content of other impurity elements≤0.05%, total content of other impurity elements≤0.1%, remaining The amount is Al.

[0022] The method for preparing aluminum alloy welding wire for automobile fuel tanks includes the following steps: melting the aluminum ingot, adding the remaining raw materials, smelting, refining, and casting to obtain a round ingot meeting the above composition range; homogenizing, extruding, and Annealing and drawing treatments obtain aluminum alloy welding wire for automobile fuel tank. The homogenization temperature is 455℃, the homogenization temperature is 36h, the extrusion temperature is 430℃, the extrusion ratio is 45, the annealing temperature is 440℃, and the annealing time Fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum alloy welding wire for an automobile fuel tank. The raw materials of the aluminum alloy welding wire comprise, by weight, 6.3-6.7% of Mg, 0.5-0.8% of Mn, 0.16-0.18% of Ti, 0.0001-0.005% of Be, 0.2-0.4% of Fe, 0.01-0.08% of B, 0.22-0.25% of Cr, 0.3-0.4% of Si, 0.16-0.25% of Zr, 0.15-0.2% of V, 0.2-0.3% of Sc, less than or equal to 0.1% of Cu, less than or equal to 0.2% of Zn, less than or equal to 0.05% of the single content of other impurity elements, less than or equal to 0.1% of the total content of other impurity elements and the balance Al. The invention further discloses a preparation method of the aluminum alloy welding wire for the automobile fuel tank. The aluminum alloy welding wire for the automobile fuel tank is compact in welding joint tissue, good in impact resistance, toughness and tension strength, good in crack resistance, and good in fatigue resistant property.

Description

technical field [0001] The invention relates to the field of welding wire technology, in particular to an aluminum alloy welding wire for an automobile fuel tank and a preparation method thereof. Background technique [0002] With the rapid development of the automobile industry, people have higher and higher requirements for the lightness of automobiles. Replacing steel fuel tanks with aluminum alloy fuel tanks can reduce the weight of automobiles. However, due to the low impact resistance and fatigue resistance of the fuel tank welds, Long-term turbulence and the impact of oil solvents often cause damage to the welding joints, resulting in oil leakage and potential safety hazards. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes an aluminum alloy welding wire for automobile fuel tanks and a preparation method thereof. The present invention has fine weld structure, good impact resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/28B23K35/40
CPCB23K35/0261B23K35/288B23K35/40
Inventor 卢齐元
Owner 安徽飞弧焊业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap