Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anti-corrosion coating and synthetic method thereof

A technology of polyvinylidene chloride and vinylidene chloride, which is applied in the direction of anti-corrosion coatings, etc., can solve the problems of poor adhesion and high crystallinity of vinylidene chloride resin, and achieve the effect of enhancing toughness and increasing toughness

Inactive Publication Date: 2018-03-06
摩田材料科技(昆山)有限公司
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to improve the problems of high crystallinity and poor adhesion of vinylidene chloride resin, the invention provides a polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anticorrosion coating and its synthesis method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anti-corrosion coatings is composed of the following raw materials by weight: 1) 40 parts of mixed monomers: 15% acrylate, 5% acrylic acid and 80% partial dichloride Ethylene; 2) 0.2 parts of initiator: potassium persulfate; 3) 0.4 parts of emulsifier: 20% sodium lauryl sulfate and 80% sodium 1-propenyl-2-hydroxyalkanesulfonate.

Embodiment 2

[0024] Polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anti-corrosion coatings is composed of the following raw materials by weight: 1) 50 parts of mixed monomers: 15% acrylate, 5% acrylic acid and 80% partial dichloride Ethylene; 2) 0.25 parts of initiator: potassium persulfate; 3) 0.5 parts of emulsifier: 20% sodium lauryl sulfate and 80% sodium 1-propenyl-2-hydroxyalkanesulfonate.

Embodiment 3

[0026] Polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anti-corrosion coatings is composed of the following raw materials by weight: 1) 42 parts of mixed monomers: 15% isooctyl acrylate, 5% acrylic acid and 80% partial Dichloroethylene; 2) 0.22 parts of initiator: potassium persulfate; 3) 0.42 parts of emulsifier: 20% sodium lauryl sulfate and 80% sodium 1-propenyl-2-hydroxyalkanesulfonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Minimum film forming temperatureaaaaaaaaaa
Minimum film forming temperatureaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a polyvinylidene chloride-acrylate copolymer emulsion for a water-based metal anti-corrosion coating and a synthetic method thereof. The copolymer emulsion is prepared from, byweight, 40-50 parts of mixed monomer, 0.2-0.25 part of an initiator and 0.4-0.5 part of emulsifier, wherein the mixed monomer is prepared from 15% of acrylic ester, 5% of acrylic acid and 80% of vinylidene chloride, the initiator is prepared from potassium persulfate, and the emulsifier is prepared from 20% of sodium lauryl sulfate and 80% of 1-allyl-2-sodium hydroxy alkanesulfonate. The preparedpolyvinylidene chloride-acrylate copolymer emulsion for the water-based metal anti-corrosion coating is high in toughness and adhesive force, and good in storage stability, salt spray resistance, corrosion resistance and other comprehensive performance.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and relates to a metal anti-corrosion coating, in particular to a polyvinylidene chloride-acrylate copolymer emulsion for water-based metal anti-corrosion coatings and a synthesis method thereof. Background technique [0002] Water-based coatings were first widely used in the field of construction, and then gradually promoted for industrial corrosion protection of steel structures including marine engineering. Compared with traditional coatings, water-based anti-corrosion coatings have high production efficiency and excellent material properties, and have achieved "sustainable development and zero emissions", which has become one of the development directions of the coatings industry today. Water-based coatings use water as a solvent or thinner, are non-toxic, odorless, non-flammable, have no danger of fire and explosion, and are not harmful to human health. [0003] In recent ye...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F214/08C08F220/18C08F220/06C08F2/26C09D127/08C09D5/08
CPCC09D127/08C08F2/26C08F214/08C09D5/08C08F220/1808C08F220/06C08F220/18
Inventor 王以元咸曦晨李洪霞
Owner 摩田材料科技(昆山)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com