Pea-green Ru porcelain glaze and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of green glaze and porcelain bean, which is applied in the field of ceramics, can solve the problems of agate entering the glaze and natural kiln turning into bean green, and achieve the effect of soft luster
Inactive Publication Date: 2018-06-22
马聚魁
View PDF1 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] The purpose of the present invention is to provide a kind of Ru porcelain bean green glaze, in order to solve the ancient glaze color of the bean green glaze in the prior art, and solve the problem that agate enters the glaze, and the natural kiln becomes bean green; the purpose of the present invention is also To provide a preparation method of Ru porcelain bean green glaze
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] A Ru porcelain bean green glaze, comprising the following components in parts by weight: 13 parts of agate stone, 7 parts of purple gold soil, 35 parts of feldspar powder, 8 parts of quartz powder, 1.6 parts of bone ash, 10 parts of wood ash, 16 parts of calcite, red 5 parts of iron ore, 7 parts of porphyrin, 10 parts of local glazed soil (local glazed soil in Baofeng, Henan), and 14 parts of self-made medicine.
[0026] The preparation method of Ru porcelain bean green glaze comprises the following steps:
[0027] 1) Refining, washing and crushing agate, calcite, hematite and porphyrin respectively into granules or powder;
[0028] 2) Mix purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local glazed soil, self-made this medicine and the stone materials treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.85 of the glaze. times, the ball milling time is 20 hours, and the glaze slurry is...
Embodiment 2
[0035] A Ru porcelain bean green glaze, comprising the following components in parts by weight: 19 parts of agate stone, 10 parts of purple gold soil, 45 parts of feldspar powder, 12 parts of quartz powder, 2.5 parts of bone ash, 15 parts of wood ash, 19 parts of calcite, red 9 parts of iron ore, 10 parts of porphyrin, 15 parts of local glazed soil (local glazed soil in Baofeng, Henan), and 19 parts of self-made medicine.
[0036] The preparation method of Ru porcelain bean green glaze comprises the following steps:
[0037] 1) Refining, washing and crushing agate, calcite, hematite and porphyrin respectively into granules or powder;
[0038] 2) Mix purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local glazed soil, self-made medicine and the stones treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.90 of the glaze. times, the ball milling time is 60 hours, and the glaze slurry is obtained; ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a pea-green Ru porcelain glaze and a preparation method thereof. The glaze comprises, by weight, 13-19 parts of agate, 7-10 parts of violet gold earth, 35-45 parts of feldsparpowder, 8-12 parts of quartz powder, 1.6-2.5 parts of bone ash, 10-15 parts of wood ash, 16-19 parts of calcite, 5-9 parts of hematite, 7-10 parts of spotted tone, 10-15 parts of local glazed earth and 14-19 homemade medicine. According to the pea-green Ru porcelain glaze and the preparation method thereof, the problem of unique color of pea-green Ru porcelain glazes is mainly solved; the problemof adding the agate into the glaze is solved; pea green is presented after natural furnace transmutation; the glaze is pea green, simple and elegant, smooth and delicate; the color changes with light;the glaze is jade, unique, milky, icy, green and elegant and rich in water color; a glaze layer is pure and delicate, the color is like jade, green and elegant, the texture is beautiful, and the luster is soft; the surface of the glaze has the unique advantages of having dense cracks, fish-scale cracks, cicada wing-like cracks, crab claw-like cracks, ice cracks and sesame flower-like cracks.
Description
technical field [0001] The invention relates to the technical field of ceramics, in particular to a Ru porcelain bean green glaze and a preparation method thereof. Background technique [0002] Ru porcelain was listed as the first of the five famous porcelains (Ru, Guan, Jun, Ge, Ding) in the Song Dynasty of our country, and was designated as royal porcelain at that time. The clay of Ru porcelain is fine, the fetal bone is hard, the glaze color is moist, and the shape is simple and generous. The characteristics of "sesame flower" are called "like jade but not jade but better than jade" by the world. Ru porcelain began in the late Northern Song Dynasty and got its name because the kiln site was in Ruzhou (now Ruzhou and Baofeng, Henan). Due to historical reasons, Ru Kiln flourished for only 20 years. Due to the short firing time, there are less than 100 pieces of treasures handed down to this day, which are very precious. [0003] The traditional ceramic glaze is a kind of...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more