Archaistic environment-friendly high-viscosity weather-resistant paint and preparation method thereof
A weather-resistant coating and high-viscosity technology, applied in the field of coatings, can solve the problems of weak decoration and color difference, and achieve the effect of increasing the sense of simplicity, strong antique effect, and good bactericidal effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0038] A kind of antique environment-friendly high-viscosity weather-resistant paint of the present embodiment comprises the following raw materials in parts by weight:
[0039] 70 parts of water-based mixed emulsion, 8 parts of dimethyl hydroxy silicone oil, 7 parts of polyacrylamide, 6 parts of modified filler, 3 parts of coupling agent, 7 parts of antique pigment, 3 parts of modified graphene, 2 parts of nano additives , 5 parts of additives.
[0040] The water-based mixture emulsion in this embodiment is a mixture of water-based fluorocarbon emulsion, water-based epoxy resin, and water-based acrylic resin in a weight ratio of 3:5:2.
[0041]The modified and added filler in this example is: calcining shell powder, attapulgite, fly ash, and diatomaceous earth at a temperature of 600°C for 1 hour according to the weight ratio of 3:4:1:2, and after cooling, ball milling 100 mesh sieves to obtain the mixture, add silane coupling agent KH550, 2% sorbitan monooleate, 2% triethyl...
Embodiment 2
[0053] A kind of antique environment-friendly high-viscosity weather-resistant paint of the present embodiment comprises the following raw materials in parts by weight:
[0054] 90 parts of water-based mixed emulsion, 10 parts of dimethyl hydroxy silicone oil, 9 parts of polyacrylamide, 10 parts of modified filler, 5 parts of coupling agent, 11 parts of antique pigment, 7 parts of modified graphene, 4 parts of nano additives , 9 parts of additives.
[0055] The water-based mixture emulsion in this embodiment is a mixture of water-based fluorocarbon emulsion, water-based epoxy resin, and water-based acrylic resin in a weight ratio of 3:5:2.
[0056] The modified and added fillers in this example are as follows: shell powder, attapulgite, fly ash, and diatomaceous earth are calcined at a temperature of 700°C for 2 hours in a weight ratio of 3:4:1:2, and after cooling, ball milling 200 mesh sieves to obtain the mixture, add silane coupling agent KH550, 4% sorbitan monooleate, 4%...
Embodiment 3
[0068] A kind of antique environment-friendly high-viscosity weather-resistant paint of the present embodiment comprises the following raw materials in parts by weight:
[0069] 80 parts of water-based mixed emulsion, 9 parts of dimethyl hydroxy silicone oil, 8 parts of polyacrylamide, 8 parts of modified filler, 4 parts of coupling agent, 9 parts of antique pigment, 5 parts of modified graphene, and 3 parts of nano additives , 7 parts of additives.
[0070] The water-based mixture emulsion in this embodiment is a mixture of water-based fluorocarbon emulsion, water-based epoxy resin, and water-based acrylic resin in a weight ratio of 3:5:2.
[0071] The modified and added filler in this example is: calcining shell powder, attapulgite, fly ash, and diatomaceous earth at a temperature of 650°C for 1.5h at a weight ratio of 3:4:1:2, and after cooling, ball mill Pass through a 100-200 mesh sieve to get the mixture, add 4% silane coupling agent KH550, 3% sorbitan monooleate, 3% tr...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com