A kind of preparation method of porous dandelion-like PD nanodendrite and its obtained material and application

A dandelion-like nano-technology, which is applied in nanotechnology, transportation and packaging, metal processing equipment, etc., can solve problems such as technical limitations and complex synthetic routes, and achieve a clear mechanism of the preparation process, a simple preparation method, and large-scale production. Effect

Active Publication Date: 2019-11-12
NANJING NORMAL UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are certain technical limitations in the preparation of hollow nanostructures in noble metal-based alloys by displacement reactions.
At the same time, the synthesis route of the sacrificial template method is relatively complicated, and the construction of porous structures using a more convenient method still needs further exploration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of porous dandelion-like PD nanodendrite and its obtained material and application
  • A kind of preparation method of porous dandelion-like PD nanodendrite and its obtained material and application
  • A kind of preparation method of porous dandelion-like PD nanodendrite and its obtained material and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0030] 1) Preparation of reaction solution: Accurately weigh 0.038mg N,N'-methylenebisacrylamide (MBAA), add 9.5mL H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0031] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

Embodiment 2

[0033] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0034] 1) Preparation of reaction solution: Accurately weigh 50 mg of N, N'-methylenebisacrylamide (MBAA), add 9.5 mL of H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0035] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

Embodiment 3

[0037] A preparation method of porous dandelion-like Pd nano dendrites, comprising the following steps:

[0038] 1) Preparation of reaction solution: Accurately weigh 385.43 mg N, N'-methylenebisacrylamide (MBAA), add 9.5 mL H 2 O, make it fully dissolved, add 0.5mL 0.05M K 2 PdCl 4 Solution, fully ultrasonicated to make it evenly mixed.

[0039] 2) Preparation of porous dandelion-like Pd nanodendrites: the reaction solution was allowed to stand at room temperature (25°C) for 10 min to obtain a black precipitate. The black precipitate is centrifuged, washed, and dried to obtain the porous dandelion-like Pd nanodendrite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing porous dandelion-like Pd nanodendrites, the obtained material and its application as an oxygen reduction cathode catalyst. The method uses N,N'-methylenebisacrylamide (MBAA) as a complex Agents, structure-directing agents and reducing agents, the metal precursors were quickly reduced into porous dandelion-like Pd nanodendrites by one-step static reduction method. The porous dandelion-like Pd nanodendrite prepared by the method of the invention has the advantages of regular shape, ultra-fine particle size, high electrocatalytic activity, etc., and exhibits high catalytic activity and stability as an oxygen reduction cathode catalyst. The preparation method of the invention is simple, efficient and universal.

Description

technical field [0001] The invention relates to a method for preparing porous dandelion-like Pd nano dendrites and the obtained materials and applications thereof, belonging to the technical field of Pd nano dendrites. Background technique [0002] Facing the problems of energy shortage and environmental pollution, a large number of scientific researchers are devoted to the development and development of clean energy technology. Unlike other energy conversion devices, fuel cells can directly convert chemical energy into electrical energy, and have the advantages of no pollution, zero emissions, high efficiency, wide application, and diversified fuels. It is expected to become the most potential energy supply device in the future. However, there are still some urgent problems to be solved on the road to commercialization of fuel cells, the most prominent of which is the design and synthesis of low-platinum or non-platinum electrocatalysts with high catalytic activity and good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F1/00B22F9/24B82Y40/00
CPCB82Y40/00B22F9/24B22F2009/245B22F1/0553B22F1/07B22F1/054
Inventor 唐亚文江娴黄祯娜邓思辉孙境泽付更涛徐林孙冬梅
Owner NANJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap