Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cold patching and road technology, applied in the field of road paving, can solve the problems that the cold patching material cannot quickly form strength, the joints of the pit interface fall off, and the cohesion of the cold patching material is poor, so as to improve the strength and shear resistance Strength, the effect of increasing the degree of cross-linking
Active Publication Date: 2018-09-21
ZHEJIANG XIUSHAN GARDEN CONSTR CO LTD
View PDF26 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In order to meet the storage performance and ease of construction of asphalt cold patching materials, cold patching materials often cannot quickly develop strength, and the cohesion of the above-mentioned cold patching materials is poor, so it is e
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] Example 1, a regenerative road cold patch material, the raw material components are shown in Table 1 in parts by weight. Wherein, the cold patch is prepared through the following steps:
[0033] Step 1: Heat base asphalt and planing and milling material to 120-140°C, add kerosene and stir for 20-30 minutes, then add cold patching additives and keep warm to 100°C to obtain diluted asphalt;
[0034] Step 2, the polyurethane prepolymer, water-based epoxy resin and octadecyltrimethylammonium chloride are dropped into the diluted asphalt and stirred evenly to obtain the mixture;
[0035] Step 3, putting styrene-butadiene-styrene block copolymer and dicumyl peroxide into the cold repair mixture and stirring evenly to obtain the modified mixture;
[0036] In step 4, limestone is put into the modified mixture for mixing and stirring to obtain cold patching material.
Embodiment 2
[0037] Embodiment 2 differs from Embodiment 1 in that, in parts by weight, the raw material components are as shown in Table 1.
Embodiment 3
[0038] Example 3, a regenerative road cold patch material, the raw material components are shown in Table 1 in parts by weight. Wherein, the cold patch is prepared through the following steps:
[0039]Step 1: Heat base asphalt and planing and milling material to 120-140°C, add kerosene and stir for 20-30 minutes, then add cold patching additives and keep warm to 100°C to obtain diluted asphalt;
[0040] Step 2, putting the polyurethane prepolymer and octadecyltrimethylammonium chloride into the diluted asphalt and stirring evenly to obtain the mixture;
[0041] Step 3, putting styrene-butadiene-styrene block copolymer and dicumyl peroxide into the cold repair mixture and stirring evenly to obtain the modified mixture;
[0042] In step 4, limestone is put into the modified mixture for mixing and stirring to obtain cold patching material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a regenerative road cold filling material, and relates to the technical field of road paving. The regenerative road cold filling material is prepared from, by weight, 80-120 parts of matrix asphalt, 80-120 parts of milling material, 1-5 parts of cold filling addictive, 10-25 parts of separant, 20-40 parts aggregate and 20-30 parts of polyurethane prepolymer. The milling material is a waste asphalt mixture, the cold filling material is prepared by using the milling material, and the milling material is fully recycled. The polyurethane prepolymer can improve the adhesiveaggregation performance of the cold filling material, so that the cold filling material and a pit slot interface can form a stronger bonding effect, thereby preventing the asphalt mixture from loosening too early or preventing an interface seam of the pit slot from being damaged the pit slot is filled, and then the durability of the cold filling material is improved. After the polyurethane prepolymer and liquid asphalt are fully mixed and solidified, the asphalt is evenly distributed in a spatial net-shaped structure formed by the polyurethane prepolymer, not only is the strength of the cold filling material improved, but also the cold filling material cannot become sticky and soft at a high temperature.
Description
technical field [0001] The invention relates to the technical field of road paving, and more specifically, relates to a regenerative cold patch material for roads. Background technique [0002] Cold patch is a road repair material that can be used around the clock and is suitable for repairing various types of road surfaces in any weather and environment, such as asphalt concrete roads, cement concrete roads, parking lots, airport runways, etc. [0003] The Chinese patent with the notification number CN101008172B discloses a regenerative road cold patching material, which includes the following components in weight percentage: milling material 56-87%; cold patching additive 0.08-0.34%; diesel oil 0.87% -1.6%; the rest is new stone, among which the milling material is composed of Type I milling material with a particle size of 10-19mm and 4 / 6 of the total amount of milling material with a particle size of 5-10mm. The milling material and 1 / 6 of the three-type milling materia...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.