A kind of magnetic porous adsorbent and preparation method thereof

A porous adsorbent and adsorbent technology, applied in chemical instruments and methods, adsorbed water/sewage treatment, other chemical processes, etc., can solve the problems of complex preparation process, high cost of adsorbent, inconvenient separation, etc., and achieve environmental applicability Wide range of properties, simple process, quick magnetic separation effect

Active Publication Date: 2021-07-27
FUZHOU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these adsorbents still have disadvantages such as high cost, complicated preparation process, inconvenient separation during application, and some even cause secondary pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magnetic porous adsorbent and preparation method thereof
  • A kind of magnetic porous adsorbent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Disperse 1.0 g of melamine resin, 5.0 g of cetyltrimethylammonium bromide, and 1.0 g of ferric oxide in deionized water, add 0.1 mL of formic acid, mix well, and react at 40°C for 10 min to prepare Obtain a mixed solution containing magnetic complexes;

[0024] (2) Add 60.0 mL of 1 wt% hydrochloric acid solution containing 0.5 g chitosan to the mixed solution containing the magnetic complex obtained in step (1), and mix well;

[0025] (3) Add 2.0 mL of ammonia water and 2.0 mL of formaldehyde to the mixture obtained in step (2), and stop the reaction after cross-linking reaction at 40°C for 0.5 h to form a cross-linked porous composite;

[0026] (4) Adjust the pH of the solution obtained in step (3) to neutral, separate the product with a magnetic field, wash it repeatedly with deionized water and dry it, and then reflux with absolute ethanol to remove excess cetyl trimethyl bromide ammonium to obtain a magnetic porous adsorbent.

[0027] 40 mg of adsorbent was ad...

Embodiment 2

[0029] (1) Disperse 3.0 g of melamine resin, 25.0 g of hexadecyltrimethylammonium bromide and 2.5 g of ferric oxide in deionized water, add 0.8 mL of formic acid, mix well, and react at 60°C for 40 min to prepare Obtain a mixed solution containing magnetic complexes;

[0030] (2) Add 60.0 mL of 1 wt% hydrochloric acid solution containing 3.0 g chitosan to the mixed solution containing the magnetic complex obtained in step (1), and mix well;

[0031] (3) Add 10.0 mL of ammonia water and 1.0 mL of epichlorohydrin to the mixture obtained in step (2), and stop the reaction after cross-linking reaction at 60°C for 1.0 h to form a cross-linked porous composite;

[0032] (4) Adjust the pH of the solution obtained in step (3) to neutral, separate the product with a magnetic field, wash it repeatedly with deionized water and dry it, and then reflux with absolute ethanol to remove excess cetyl trimethyl bromide ammonium to obtain a magnetic porous adsorbent.

[0033] 40 mg of adsorben...

Embodiment 3

[0035] (1) Disperse 1.0 g of melamine resin, 40.0 g of cetyltrimethylammonium bromide and 4.0 g of ferric oxide in deionized water, add 1.5 mL of formic acid, mix well, and react at 70°C for 90 min to prepare Obtain a mixed solution containing magnetic complexes;

[0036] (2) Add 60.0 mL of 1 wt% hydrochloric acid solution containing 5.0 g of chitosan to the mixed solution containing the magnetic complex obtained in step (1), and mix well;

[0037] (3) Add 25.0 mL of ammonia water, 3.0 mL of formaldehyde and 5.0 mL of epichlorohydrin to the mixture obtained in step (2), stop the reaction after 3.0 hours of cross-linking reaction at 80°C, and generate a cross-linked porous composite;

[0038] (4) Adjust the pH of the solution obtained in step (3) to neutral, separate the product with a magnetic field, wash it repeatedly with deionized water and dry it, and then reflux with absolute ethanol to remove excess cetyl trimethyl bromide ammonium to obtain a magnetic porous adsorbent....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
clearance rateaaaaaaaaaa
clearance rateaaaaaaaaaa
clearance rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a magnetic porous polymer adsorbent and a preparation method thereof. The main raw materials are melamine resin, cetyltrimethylammonium bromide, chitosan and iron tetroxide. Amine resin, cetyltrimethylammonium bromide and iron ferric oxide are cross-linked under acidic conditions to prepare magnetic functional composites, and then chitosan and cross-linking agent are added to it for deep cross-linking reaction to form cross-linking The porous composite is then dried and ethanol refluxed to obtain a chitosan-modified melamine resin magnetic porous adsorbent. The adsorbent has a good adsorption effect, and the removal rate of new carmine dye in wastewater can reach 99%, and it has a simple and fast magnetic separation function, which is beneficial to simplify the time-consuming and energy-consuming centrifugation, The sedimentation process has a good application prospect in the field of sewage treatment.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to a magnetic porous adhesive and a preparation method thereof. Background technique [0002] With the rapid development of modern industry, the massive discharge of industrial wastewater and domestic wastewater has caused water pollution and seriously affected people's healthy life. Therefore, water body governance and water environment protection have become one of the hot issues in today's society. Research on economical and efficient water treatment methods is the focus of the current government and people. At present, wastewater treatment technologies mainly include photocatalytic oxidation, chemical coagulation, biosorption and other technologies, among which biosorption is a simple, effective and economical method with broad application prospects. [0003] Adsorbent is the key core of biosorption. The current adsorbents mainly include porous carbon, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/22B01J20/30B01J20/28C02F1/28C02F101/30
CPCB01J20/06B01J20/22B01J20/24B01J20/28009B01J2220/46B01J2220/4806B01J2220/4812B01J2220/4825C02F1/281C02F1/285C02F1/286C02F2101/308
Inventor 游力军鲁菲菲许珂丁冠军张其清
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap