A technology of high magnetic induction orientation and silicon steel, applied in the direction of contour control, metal rolling, etc., can solve the problem of high occurrence rate of "biscuit brittle" defects

Active Publication Date: 2019-04-09
武汉钢铁有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a method for hot-rolling production of low-temperature high-magnetic-induction oriented silicon steel to solve or partially solve the technical problem of high occurrence rate of "biscuit brittle" defects at the edge of strip steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot-rolled edge quality control method for low-temperature and high-magnetic-inductance oriented silicon steel
  • Hot-rolled edge quality control method for low-temperature and high-magnetic-inductance oriented silicon steel
  • Hot-rolled edge quality control method for low-temperature and high-magnetic-inductance oriented silicon steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] In order to enable those skilled in the technical field to which the application belongs to understand the application more clearly, the technical solutions of the application will be described in detail below through specific embodiments in conjunction with the accompanying drawings.

[0034] The natural edge of normal hot-rolled low-temperature high-magnetic-induction oriented silicon steel strip should be smooth, and there should be no obvious cracks, jagged cracks, rough burrs, and unevenly deformed small nodules after the edge is plastically deformed. quality typical photo see figure 1 . "Biscuit brittle" is a shape defect such as microcracks, jagged cracks, or small nodules with rough and burr-like uneven deformation on the natural edge of hot-rolled low-temperature, high-magnetic-induction oriented silicon steel strip steel. The typical photo of the edge biscuit brittle defect is shown in Figure 2-Figure 3 .

[0035] In order to solve the technical problem of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hot-rolled edge quality control method for low-temperature and high-magnetic-inductance oriented silicon steel. The control method comprises the steps of in the process of heating the low-temperature and high-magnetic-inductance oriented silicon steel by a heating furnace high-temperature section, controlling an air-fuel ratio of an upper secondary heating section to an upper soaking section of the low-temperature and high-magnetic-inductance oriented silicon steel to be less than or equal to a first preset value, and controlling an air-fuel ratio of a lower secondaryheating section to a lower soaking section of the low-temperature high-magnetic-inductance oriented silicon steel to be less than or equal to a second preset value, wherein the first preset value isgreater than the second preset value; reducing the temperature of the heating furnace high-temperature section by 10-20 DEGC; and performing three pass of rough rolling on the low-temperature and high-magnetic-inductance oriented silicon steel by a first vertical roll and a second vertical roll, wherein the rolling speed in each pass in rough rolling is controlled at 2.6-4.8 m / s, and the best slope matching speed and backward slip coefficient between the vertical rollers E2 and R2 in each pass. The hot-rolled edge quality control method solves the technical problem of high occurrence rate of 'cake brittleness' defect at the edge of the strip.

Description

technical field [0001] The present application relates to the field of grain-oriented silicon steel manufacturing, and in particular to a method for controlling the quality of hot-rolled edges of low-temperature high-magnetic-inductive grain-oriented silicon steel. Background technique [0002] Low temperature and high magnetic induction oriented silicon steel has poor material processing performance, resulting in poor quality of hot-rolled side edges, which are prone to edge cracks and delamination. In the cold rolling process, normalized pickling machines are usually used to trim the edges to 40-60mm. The Sendzimir 20-high rolling mill with wide bottom feed is produced. The Sendzimir rolling mill adopts an uncoiler for the first pass of coiling production. The entry side platen is always closed to provide auxiliary back tension, and the side guide roll is aligned with the position where the steel strip enters the roll gap. [0003] With the optimization and improvement of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B37/44B21B3/02
CPCB21B3/02B21B37/44B21B2201/06
Inventor 胡伟东陈一峰蔡延擘蔡海斌吴健鹏黄东郑晓强向云盼王伍洲杨皓
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap