Anti-seismic and fireproof steel for high-strength building structure and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-strength technology for building structures, applied in the field of structural steel for construction, can solve the problems of high cost, impact, and high composition, and achieve the effects of improving corrosion resistance, wide process window, and excellent application prospects
Active Publication Date: 2019-04-16
UNIV OF SCI & TECH BEIJING
View PDF8 Cites 25 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This steel alloy is added with W and Zr, which has high composition and high cost; in order to improve the strength, the Mn content is relatively high, so its welding performance is affected to a certain extent. Under severe temperature, its impact toughness needs to be further verified
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0034] The present invention will be further described through specific examples below, and the examples are only for the purpose of explanation, and the protection scope of the present invention is not limited to the examples.
[0035] The present invention is further described below:
[0036] Table 1 is the chemical composition and weight percentage content list of each embodiment of the present invention and comparative example;
[0037] Table 2 is the value list of the rolling main process parameters of each embodiment of the present invention and comparative examples;
[0038] Table 3 is the value list of the isothermal heat treatment main process parameters of each embodiment of the present invention and comparative examples;
[0039] Table 4 is a list of the mechanical and fire resistance test results of the various embodiments of the present invention and comparative examples.
[0040] Each embodiment of the present invention is produced according to the following pr...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
Login to view more
Abstract
The invention provides anti-seismic and fireproof steel for a high-strength building structure and a preparation method thereof, and belongs to the field of building steel. The preparation method comprises, 0.04-0.08% of C, 1.0-1.5% of Mn, 0.15-0.60% of Si, 0.2-0.7% of Cr, 0.10-0.60% of Mo, less than or equal to 0.35 of Ti+V+Nb, 0.01-0.05% of Al, 0.1-0.6% of Cu, 0.1-0.6% of Ni, less than or equalto 0.008% of P, less than or equal to 0.002% of S, and the balance iron and inevitable trace chemical elements. Continuous casting is adopted for smelting through a converter or an electric furnace, amedium-thickness plate rolling machine is adopted for rolling, and after rolling is carried out, a steel plate is subjected to heat preservation, quenching and tempering heat treatment processes in an alpha+gamma phase region, and the strength and the yield ratio of a material are controlled by regulating the tissue proportion of bainite, martensite and ferrite; the yield strength is larger thanor equal to 690 MPa, the tensile strength is 850-950 MPa, the elongation at break is larger than or equal to 85%, the percentage elongation after fracture is larger than or equal to 20%, -40 DEG C KV2larger than or equal to 150 J, and the yield strength after heat preservation at 600 DEG C for 3 hours is greater two thirds than the yield strength at room temperature. The preparation method can bewidely applied to high-rise and super-high-rise building steel simultaneously with high-strength, anti-seismic and fireproof requirements and the like.
Description
technical field [0001] The invention belongs to the field of structural steel for construction, in particular to an anti-seismic fire-resistant steel for high-strength building structure and a preparation method thereof. Background technique [0002] At present, domestic and international high-rise steel structure buildings are constantly emerging, not only the number has increased sharply, but also the height has been continuously increased. The board has entered the stage of general application and promotion. It has become a development trend to focus on high-strength, high-performance, large-scale, and functional steel for construction. Considering the safety of buildings and the actual life cycle, higher requirements are put forward for the earthquake resistance and fire resistance of construction steel. [0003] In recent years, earthquakes have occurred frequently, and the seismic performance of steel has attracted much attention. As the ratio of yield strength to ten...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.