Medical conductive pressure-sensitive adhesive, preparation method thereof and electrode plate

A conductive voltage and obtained technology, applied in the field of conductive adhesive, can solve the problems of poor skin adhesion and easy falling off, and achieve the effects of enhancing moisturizing function, large adhesion, and improving stability.

Active Publication Date: 2019-08-23
QINGDAO BRIGHT MEDICAL MFG
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a medical conductive pressure-sensitive adhesive, its preparation method and the obtained electrode sheet, which solves the problem that the conductive pressure-sensitive adhesive made of water-soluble acrylate has poor adhesion to skin and is easy to fall off in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical conductive pressure-sensitive adhesive, preparation method thereof and electrode plate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] A kind of preparation method of medical conductive pressure-sensitive adhesive of the present invention, comprises the following steps:

[0028] 1) Take 0.05-0.15 parts by weight of cross-linking agent, 0.10-0.20 parts by weight of dispersant and 1.00-2.00 parts by weight of solubilizer, mix well, add 2.00-4.00 parts by weight of water, stir and dissolve to obtain the first mixture ,spare;

[0029] 2) Take 30.00-40.00 parts by weight of photocurable monomer, 6.00-8.00 parts by weight of water and 18.00-26.00 parts by weight of solubilizer, mix and stir evenly to obtain the second mixture and set aside;

[0030] 3) Take 12.00-16.00 parts by weight of water, 10.00-25.00 parts by weight of neutralizing agent, the second mixture obtained in step 2), 1.00-3.00 parts by weight of acrylic acid, the first mixture obtained in step 1), 0.50-3.00 parts by weight The conductive agent in parts by weight is mixed sequentially, the reaction temperature is controlled to be less than 3...

Embodiment 1

[0037] A kind of preparation method of medical conductive pressure-sensitive adhesive of the present invention, comprises the following steps:

[0038] 1) In the first side reactor, add 0.08 parts of N,N-methylenebisacrylamide, 0.13 parts of polyvinylpyrrolidone, and 1.00 parts of 1,2-propylene glycol, mix well, make a paste, and then add water 2.00 parts, at 500r / min, stir for 2h, wait until it is fully dissolved, to obtain the first mixture, set aside;

[0039] 2) In the second side reactor, add 30.00 parts of AMPS, 4.56 parts of β-CEA, 24.64 parts of 1,2-propanediol, 1.36 parts of polyethylene glycol 400, 6.00 parts of water, mix, and at 100r / min, Stir evenly to get the second mixture, set aside;

[0040] 3) In the main reactor, add 16.00 parts of water, stir evenly at 100r / min, and cool to the temperature <30°C, and enter the next step;

[0041] 4) In the main reactor obtained in step 3), add 10.70 parts of sodium carbonate, stir evenly at 100r / min, and cool to a tempera...

Embodiment 2

[0051] A kind of preparation method of medical conductive pressure-sensitive adhesive of the present invention, comprises the following steps:

[0052] 1) In the first side reactor, add 0.11 parts of N,N-methylenebisacrylamide, 0.18 parts of polyethylene glycol-60000, and 1.00 parts of 1,2-propylene glycol, mix well, make a paste, and then Add 2.94 parts of water, stir at 500r / min for 2h, and wait until it is fully dissolved to obtain the first mixture, which is set aside;

[0053] 2) In the second side reactor, add 30.00 parts of β-CEA, 7.00 parts of water, 24.86 parts of 1,2-propylene glycol, and 1.14 parts of polyethylene glycol 400, and stir evenly at 200 r / min to obtain the second mixture, spare;

[0054] 3) In the main reactor, add 12.00 parts of water, stir evenly at 200r / min, and cool to the temperature <30°C, enter the next step;

[0055] 4) In the main reactor obtained in step 3), add 11.78 parts of sodium carbonate, stir evenly at 200r / min, and cool to a temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medical conductive pressure-sensitive adhesive, a preparation method thereof and an electrode plate. The medical conductive pressure-sensitive adhesive comprises the following components: in parts by weight, 30.00-40.00 parts of water-soluble photocurable monomers, 20.00-30.00 parts of a solubilizer, 20.00-28.00 parts of water, 10.00-25.00 parts of a neutralizer, 1.00-3.00 parts of acrylic acid, 0.50-3.00 parts of a conductive agent, 0.01-0.50 part of a photoinitiator, 0.05-0.15 parts of a cross-linking agent, 0.10-0.20 part of a dispersing agent, 0.05-10.00 parts ofa polymerizable quaternary ammonium salt and 0.10-5.00 parts of a humectant. The invention also provides preparation methods of the conductive pressure-sensitive adhesive and electrode plate. The glass transition temperature of copolymer can be regulated, the adhesion of the obtained electrode plate to the skin is increased, and the obtained electrode plate has good affinity to the human skin, nostimulation and excellent electrical conductivity.

Description

technical field [0001] The invention belongs to the technical field of conductive adhesives, in particular to a medical conductive pressure-sensitive adhesive, a preparation method thereof, and an obtained electrode sheet. Background technique [0002] In the electrocardiogram, electroencephalogram, defibrillator, myoelectric instrument, transcutaneous electrical nerve stimulation therapy, neuromuscular electrical stimulation therapy and other medical examinations and electrotherapy processes, it is necessary to frequently replace disposable electrodes. And its adhesion to the skin is directly related to the inspection results; in addition, since the electrode pads are in direct contact with the skin, the material of the electrode pads is required to be non-irritating, non-cytotoxic, and non-sensitizing to the skin. At present, disposable medical electrode sheets are mainly composed of substrate carrier film, Ag / AgCl conductive paste printing layer, conductive pressure-sensi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/24C09J133/14C09J7/38C09J7/50C09J9/02C08F220/58C08F220/28C08F222/38C08F220/06C08F226/02C08F220/34C08F2/48
CPCC09J133/24C09J133/14C09J7/385C09J7/50C09J9/02C08F220/58C08F220/28C08F2/48C08F220/283C08F220/585C09J2301/314C09J2301/122C09J2301/302C08F222/385C08F220/06C08F226/02C08F220/34C08F226/06
Inventor 范延超赵德政
Owner QINGDAO BRIGHT MEDICAL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com