Carbon fiber structure reinforcement method

A technology of carbon fiber and carbon fiber cloth, which is applied in the field of structural damage detection and reinforcement, can solve the problems that the strength, stiffness, stability and durability of structures and components cannot be improved well, and achieve simple and rapid construction and high axial tensile strength. High, long-term effect

Inactive Publication Date: 2019-09-10
王伟
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a carbon fiber structure reinforcement method to solve the problem that the existing technology cannot improve the strength, rigidity, stability and durability of the structure and components in the above-mentioned background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber structure reinforcement method
  • Carbon fiber structure reinforcement method
  • Carbon fiber structure reinforcement method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0026] This embodiment: as figure 1 As shown, a carbon fiber structure reinforcement method, the method includes using a special structural glue to paste the carbon fiber cloth on the structure to be reinforced.

[0027] Before pasting the carbon fiber cloth, pre-soak the carbon fiber cloth with epoxy resin solution S1.

[0028] Paste the soaked carbon fiber cloth on the concrete crack surface S2 with epoxy resin adhesive.

[0029] The carbon fiber cloth is pasted along the direction of tension or perpendicular to the crack direction.

[0030] Since a carbon fiber structure reinforcement method is adopted, the method includes pasting the carbon fiber cloth on the structure to be reinforced with a special structural adhesive, pre-soaking the carbon fiber cloth with an epoxy resin solution before pasting the carbon fiber cloth, and soaking the carbon fiber cloth The cloth is pasted on the concrete crack surface with epoxy resin adhesive, and the carbon fiber cloth is pasted a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of structural damage detection and reinforcement, and particularly relates to a carbon fiber structure reinforcement method. Before pasting a carbon fibercloth, the carbon fiber cloth is pre-soaked with an epoxy resin solution, the carbon fiber cloth after immersion is pasted on the surface of a concrete crack with an epoxy resin adhesive, and the carbon fiber cloth is pasted in the direction of the tension or in the direction perpendicular to the cracks. The carbon fiber structure reinforcement method solves the problem that in the prior art, thestrength, rigidity, stability and durability of a structure and a member cannot be well improved in the prior art, and has the beneficial technical effects of improving the strength, rigidity, crack resistance and elongation of the structure and being good in anti-seismic effect and better in reinforcement effect.

Description

technical field [0001] The invention belongs to the technical field of structure damage detection and reinforcement, and in particular relates to a carbon fiber structure reinforcement method. Background technique [0002] At present, the widely used methods for structural damage detection and reinforcement are mainly artificial neural network technology based on neural network, in addition to the use of genetic algorithm for structural damage diagnosis research, etc. The basic method of neural network for damage identification is: according to the structure Corresponding to different damage degrees of different damage parts in different states, through feature extraction, select parameters that are more sensitive to structural damage as the input vector of the network, and the damage state of the structure as the output, establish a damage classification training sample set, and then train the network , after the training is completed, it is classified into the closest cate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04G23/02
CPCE04G23/0203
Inventor 王伟张森林王琪
Owner 王伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap