Glass/aluminum-base composite material support roller

An aluminum-based composite material, glass technology, applied in the direction of rollers, conveyors, conveyor objects, etc., to achieve low density, avoid explosion accidents, and reduce mold wear

Inactive Publication Date: 2011-05-04
上海华威环保技术有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, how to use glass / aluminum-based composite materials to replace seamless steel pipes, rubber and plastics to manufacture idlers with good comprehensive performance, light weight, good electrical conductivity, wear resistance and durability, has not yet been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass/aluminum-base composite material support roller
  • Glass/aluminum-base composite material support roller
  • Glass/aluminum-base composite material support roller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The glass / aluminum matrix composite idler roller described in this embodiment is composed of two circlips, two retaining rings, two sealing rings, two bearings, two bearing housings, a roller and a shaft assembly. Among them: circlips, retaining rings, sealing rings, and bearings are all standard parts, which can be purchased directly; the shaft is made of 45 # Steel is machined; housings and rollers are fabricated from glass / aluminum matrix composite.

[0021] The glass / aluminum matrix composite material is mainly composed of waste glass and waste aluminum, and its composition and weight percentage of each composition are: 18.5% of waste glass, 77% of waste aluminum, and 4.5% of crystalline silicon.

[0022] The waste glass is obtained by cleaning, drying, ball milling and screening the waste glass products, and the waste glass products come from cullet in domestic waste, glass bottles or glass doors and windows in construction waste.

[0023] The waste aluminum is ob...

Embodiment 2

[0058] The material composition and the weight percentage of each composition for preparing the glass / aluminum matrix composite idler bearing housing and roller of this embodiment are: 7% waste glass, 90% waste aluminum, and 3% crystalline silicon.

[0059] The rest of the content and preparation process are the same as those described in Example 1.

[0060] The properties of the glass / aluminum-based composite material for preparing the roller and the bearing housing in this embodiment are as follows:

[0061]Density 2.53g / cm 3

[0062] Resistivity 21.4μΩ·cm

[0063] Linear expansion coefficient 19.9×10 -6 / °C

[0064] Softening temperature 570℃

[0065] Compressive strength 266.4Mpa

[0066] Compression modulus of elasticity 55.3Gpa

[0067] Hardness HB50

[0068] The material properties of the roller and bearing seat processed by the above hot extrusion preparation process are as follows:

[0069] Compressive strength 288Mpa

[0070] Compression modulus of elastici...

Embodiment 3

[0079] The material composition and the weight percentage of each composition of the glass / aluminum matrix composite idler bearing seat and roller of this embodiment are: 30% of waste glass, 64% of waste aluminum, and 6% of crystalline silicon.

[0080] The rest of the content and preparation process are the same as those described in Example 1.

[0081] The properties of the glass / aluminum-based composite material for preparing the roller and the bearing housing in this embodiment are as follows:

[0082] Density 2.57g / cm 3

[0083] Resistivity 17.4μΩ·cm

[0084] Linear expansion coefficient 18.6×10 -6 / °C

[0085] Softening temperature 582℃

[0086] Compressive strength 285Mpa

[0087] Compression modulus of elasticity 66.3Gpa

[0088] Hardness HB55

[0089] The material properties of the roller and bearing seat processed by the above hot extrusion preparation process are as follows:

[0090] Compressive strength 310Mpa

[0091] Compression modulus of elasticity 67...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a idler roller prepared by glass / aluminum matrix composite, comprising two bearings, two bearing chocks, a roller and an axis, the bearing chock and the roller are prepared by glass / aluminum matrix composite, the components of the glass / aluminum matrix composite and the weight percentage of each component are that: glass 7-30%, Aluminum 64-90%, crystal silicon 3-6%, the sum of the three is 100%. The glass / aluminum matrix composite idler roller, which is processed by the preparation technology of secondary hot extrusion and drawing, has the advantages of good comprehensive properties, i.e. low density, good conductivity, higher intensity and stiffness than rubber and plastic idler rollers and good anti-wear properties, more wear-resistance than the rubber and plastic idler rollers, not only greatly saving the energy consumption, reducing the cost, but also avoiding the occurrence of safety accident.

Description

technical field [0001] The present invention relates to an idler roller, in particular to an idler roller made of glass / aluminum matrix composite material and its preparation process, especially to a glass / aluminum matrix composite material mainly composed of waste glass and waste aluminum Rollers made of material. Background technique [0002] Idler rollers are the main accessories and consumables of belt conveyors, which are required to be wear-resistant, light in weight and conductive. The existing idlers are made of seamless steel pipe, rubber or plastic, and the main disadvantages are as follows: 1) The steel idler consumes a lot of steel, and the weight of the steel idler is large, and the power consumption of the motor is large ;2) Rubber or plastic idlers, because these materials are insulated, the static charge generated by the long-term friction between the conveyor belt and the idler cannot be introduced into the ground, and sparks will be generated when the char...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B65G39/02B65G39/18B65G23/04
Inventor 李如燕孙可伟赵炎宋平
Owner 上海华威环保技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap