Two-component compound synergistic inorganic fireproof glue and preparation method thereof

A fire-resistant adhesive, a two-component technology, applied in the direction of inorganic adhesives, adhesives, non-polymer adhesive additives, etc., can solve the problems of fire-resistant performance barriers, achieve increased gloss and leveling, and excellent solubilization , Improve the effect of storage stability

Active Publication Date: 2019-09-17
滁州圣好材料科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, a large amount of organic solvents are used in the above-mentioned fireproof liquid, and the organic solvents have a hindering effect on the improvement of the fireproof performance. Therefore, the fireproof performance needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of dispersing aid, adopts following steps to prepare:

[0045] (1) Ingredients: In parts by weight, weigh 10 parts of sodium tripolyphosphate, 1 part of industrial aluminum sulfate, 3 parts of sodium dodecylsulfonate, 5 parts of polycarboxylate ammonium salt dispersant and 3 parts of rosin resin;

[0046] (2) Put the polycarboxylate ammonium salt dispersant in the agitator, and adjust the speed to 85r / min;

[0047] (3) Increase the speed to 145r / min, continue to add sodium tripolyphosphate and industrial aluminum sulfate for stirring;

[0048] (4) Increase the speed to 170r / min, add rosin resin and sodium dodecylsulfonate and stir for 2h.

Embodiment 2

[0050] A kind of dispersing aid, adopts following steps to prepare:

[0051] (1) Ingredients: In parts by weight, weigh 12 parts of sodium tripolyphosphate, 1 part of industrial aluminum sulfate, 3 parts of sodium dodecylsulfonate, 6 parts of polycarboxylate ammonium salt dispersant and 3 parts of rosin resin;

[0052] (2) Put the polycarboxylate ammonium salt dispersant in the agitator, and adjust the speed to 87r / min;

[0053] (3) Increase the speed to 147r / min, continue to add sodium tripolyphosphate and industrial aluminum sulfate for stirring;

[0054] (4) Increase the speed to 170r / min, add rosin resin and sodium dodecylsulfonate and stir for 3h.

Embodiment 3

[0056] A kind of dispersing aid, adopts following steps to prepare:

[0057] (1) Ingredients: In parts by weight, weigh 15 parts of sodium tripolyphosphate, 2 parts of industrial aluminum sulfate, 4 parts of sodium dodecylsulfonate, 7 parts of polycarboxylate ammonium salt dispersant and 3 parts of rosin resin;

[0058] (2) Put the polycarboxylate ammonium salt dispersant in the mixer, and adjust the rotation speed to 88r / min;

[0059] (3) Increase the speed to 148r / min, continue to add sodium tripolyphosphate and industrial aluminum sulfate for stirring;

[0060] (4) Increase the speed to 175r / min, add rosin resin and sodium dodecylsulfonate and stir for 4h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to two-component compound synergistic inorganic fireproof glue and a preparation method thereof, the two-component compound synergistic inorganic fireproof glue comprises a material A and a material B, the material A comprises the following components in parts by weight: 50 parts of water, 12-18 parts of polyacrylamide and 1-5 parts of a dispersing aid, and the material B comprises 50 parts of water, 15-25 parts of urea, 20-30 parts of borax, 3-10 parts of a silica gel binder and 35-45 parts of polyphosphate. The fireproof glue is divided into two parts, wherein the material A is a master batch and the material B is a curing agent, and the material B is added into the material A to perform curing reaction to form the fireproof glue, and most of the components of the fireproof glue are inorganic substances, so that the fireproof glue can resist long-term flame combustion.

Description

technical field [0001] The invention relates to a fireproof adhesive, in particular to a two-component composite synergistic inorganic fireproof adhesive and a preparation method thereof. Background technique [0002] On May 1, 2015, the country promulgated and implemented GB50016-2014 "Code for Fire Protection in Building Design", which contains detailed regulations on the room design specifications for high-rise buildings. For residential buildings, when the height of the building is greater than 54m, each household must have a refuge room, which must meet the following requirements: 1. It should be installed against the outer wall, and should be equipped with openable outer windows; 2. The inner and outer walls The fire resistance limit of the room should not be lower than 1h, the door of the room should be a Class B fire door, and the exterior window should be a fire window with a fire resistance integrity of not less than 1h; The fire-resistant integrity of upper doors...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J1/00C09J11/04C09J11/06C09J11/08C09J9/00
CPCC09J1/00C09J9/00C09J11/04C09J11/06C09J11/08
Inventor 唐正良
Owner 滁州圣好材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap