A multi-dimensional decorative original edge wood grain ceramic tile and its preparation method

A multi-dimensional, ceramic tile technology, applied in the production of ceramic materials, clay products, other household appliances, etc., can solve the problems of low wood grain unevenness and high surface gloss, reduce gloss, simplify the process flow, and achieve a delicate touch. Effect

Active Publication Date: 2022-05-20
DONGGUAN CITY WONDERFUL CERAMICS IND PARK +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the deficiencies in the prior art above, the purpose of the present invention is to provide a multi-dimensional decorative original wood-grain ceramic tile and its preparation method, aiming to solve the problem that the surface gloss of the existing imitation wood-grain ceramic tile is too high and the wood grain concave-convex feeling is too low. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A multi-dimensional decorative original edge wood grain ceramic tile and its preparation method
  • A multi-dimensional decorative original edge wood grain ceramic tile and its preparation method
  • A multi-dimensional decorative original edge wood grain ceramic tile and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] see figure 1 , a method for preparing multi-dimensional decorative original edge wood grain ceramic tiles, comprising:

[0077] Step S11, pressing the blank into shape, and placing it in a roller kiln for drying to form a ceramic tile body;

[0078] Step S12, applying a matte glaze on the ceramic tile body to form a matte glaze layer;

[0079]Step S13, performing inkjet printing on the matte glaze layer and applying deep ink to form a composite layer of pattern decoration and deep ink;

[0080] Step S14, applying a matte transparent glaze on the pattern decoration and deep ink composite layer to form a matte transparent glaze layer;

[0081] Step S15a, applying dry granular glaze on the matte transparent glaze layer to form a dry granular glaze layer;

[0082] Step S16, firing in a kiln to obtain multi-dimensional decorative original edge wood grain ceramic tiles.

[0083] The ceramic tile body obtained in step 11 has a top surface and a side surface, and the joint ...

Embodiment 2

[0095] A method for preparing multi-dimensional decorative original edge wood grain ceramic tiles, comprising:

[0096] Step S11, pressing the blank into shape, and placing it in a roller kiln for drying to form a ceramic tile body;

[0097] Step S12, applying a matte glaze on the ceramic tile body to form a matte glaze layer;

[0098] Step S13, performing inkjet printing on the matte glaze layer and applying deep ink to form a composite layer of pattern decoration and deep ink;

[0099] Step S14, applying a matte transparent glaze on the pattern decoration and deep ink composite layer to form a matte transparent glaze layer;

[0100] Step S15b, applying a convex glaze on the matte transparent glaze layer to form a convex glaze layer;

[0101] Step S16, firing in a kiln to obtain multi-dimensional decorative original edge wood grain ceramic tiles.

[0102] The ceramic tile body obtained in step 11 has a top surface and a side surface, and the joint between the top surface a...

Embodiment 3

[0115] A multi-dimensional decorative original wood-grain ceramic tile, wherein the multi-dimensional decorative original wood-grain ceramic brick is prepared by the preparation method of the multi-dimensional decorative original wood-grain ceramic brick in the above-mentioned embodiment of the present invention;

[0116] The multi-dimensional decorative original wood-grain ceramic tiles include from bottom to top: ceramic tile body, matte surface glaze layer, pattern decoration and deep ink composite layer, matte glaze transparent layer and dry glaze layer.

[0117] It can be understood that by setting a matte glaze layer on the surface of the ceramic tile body, on the one hand, the flatness of the ceramic tile body surface is effectively improved, and on the other hand, the gloss of the multi-dimensional decorative original wood grain ceramic tile is effectively reduced. degree; by synchronously setting pattern decorative ink and deep ink composite layer on the matte surface ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
depthaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multi-dimensional decorative original edge wood grain ceramic brick and a preparation method thereof. The method comprises: A. pressing and forming a blank, and placing it in a roller kiln for drying to form a ceramic brick body; B. Matte surface glaze is applied on the brick body to form a matte surface glaze layer; C. Inkjet printing is performed on the matte surface glaze layer and deep ink is applied to form a composite layer of pattern decoration and deep ink; D. After pattern decoration and deep ink A matte transparent glaze is applied on the ink composite layer to form a matte transparent glaze layer; E 1 1. Apply dry glaze on the matte transparent glaze layer to form a dry glaze layer; F. Put it into a kiln for firing and molding to obtain multi-dimensional decorative original edge wood grain ceramic tiles. The flatness of the surface of the ceramic tile body is improved, which ensures the effects of pattern decoration, concave-convex texture, layering, and surface texture. At the same time, the product feels delicate, and has matte, non-slip, wear-resistant and anti-pollution effects.

Description

technical field [0001] The invention relates to the field of building ceramics production, in particular to a multi-dimensional decorative original edge wood grain ceramic brick and a preparation method thereof. Background technique [0002] With the development of architectural ceramic technology, the decorative technology level of ceramic tiles is getting higher and higher, which can imitate and decorate the surface color and texture of various natural materials such as imitation stone, imitation wood, imitation leather, imitation cloth, imitation metal, imitation cement, etc. Texture, the degree of imitation is becoming more and more realistic. At present, imitation wood-grain ceramic tile products are used in the living room, study, balcony, corridor and other spaces and walls of home decoration. The use of wood-grain brick products can give people a comfortable, warm and quiet feeling, and is also highly praised by designers. favored by consumers. The characteristics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C04B35/622C03C8/00
CPCC04B41/52C04B41/89C04B41/009C04B35/622C03C8/00C04B35/00C04B33/00C04B41/4543C04B41/5022C04B41/4545C04B41/0072Y02P40/60
Inventor 欧志勇盛正强李琳曹端旭陈展豪
Owner DONGGUAN CITY WONDERFUL CERAMICS IND PARK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com