High-zinc low-copper aluminum alloy excellent in corrosion resistance and preparation method thereof

A copper-aluminum alloy, corrosion-resistant technology, applied in the field of alloy materials, can solve problems such as lack of mature theory

Active Publication Date: 2020-01-17
JIANGXI UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is still a lack of mature theories to explain the corrosion performance theoretically.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-zinc low-copper aluminum alloy excellent in corrosion resistance and preparation method thereof
  • High-zinc low-copper aluminum alloy excellent in corrosion resistance and preparation method thereof
  • High-zinc low-copper aluminum alloy excellent in corrosion resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0019] This embodiment is only used to illustrate the effects of the present invention. The smelting method in this example is a special small-batch smelting method adopted in the laboratory. The smelting is carried out under the protection of argon gas, and the degassing and other processes in actual production are omitted. In actual production, it can be smelted according to the degassing and refining method of 7 series aluminum alloys, which can further improve the quality and performance of ingots, such as strength, plasticity, and porosity.

[0020] Carry out batching according to Table 1 with weight percentage. The metal blocks of Al, Zn, Mg, Cr and Y have a purity greater than 99.9% and a total weight of 20g. In order to supplement the volatilization loss of Zn during smelting, the excess weight of Zn is 3%.

[0021] serial number Zn(g) Mg(g) Cu(g) Al-Cr(g,10%Cr) Y(g) Al(g) ① 2.266 0.4330 0.34 0.14 0.0000 16.90 ② 2.266 0.4326 0.3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-zinc low-copper aluminum alloy excellent in corrosion resistance and a preparation method thereof, and belongs to the technical field of aluminum alloy materials. The alloy material is prepared from, by mass part, 10-11wt% of Zn, 1.8-2.0wt% of Mg, 0.97-1.0wt% of Cu, 0.08-0.1wt% of Cr, 1.4-2.0wt% of Y and the balance Al. Corrosion of the grain boundary phase of the alloy is greatly inhibited, and the corrosion resistance is greatly improved and is close to the level of pure aluminum. At the grain size of 30 micrometers, the hardness of the alloy can reach about 195 N / mm<2>, and it is equivalent that the tensile strength is about 630 MPa.

Description

technical field [0001] The invention belongs to the technical field of alloy materials, and in particular relates to a corrosion-resistant aluminum alloy composition and a processing method thereof. Background technique [0002] Aluminum alloy is the most widely used non-ferrous metal structural material in industry, and has important applications in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industry. Among them, the 7 series Al-Zn-Mg(Cu) aluminum alloy is characterized by low density, high strength and hardness, and is especially suitable for the aerospace industry. However, low stress brittle fracture often occurs in such high-strength aluminum alloys. Under the joint action of stress and environmental medium, this failure stress is far lower than the failure stress (ie tensile strength) of the material itself. Therefore, in aircraft structural materials, corrosion-resistant aluminum alloys have always been an important research ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/10C22C1/03C22F1/053
CPCC22C1/026C22C1/03C22C21/10C22F1/002C22F1/053
Inventor 杨育奇严平司恒刚王磊肖绮周晨曦张志勇方嘉文
Owner JIANGXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com