Method for preparing high-purity superfine aluminum hydroxide flame retardant by decomposition method

An ultra-fine aluminum hydroxide, aluminum hydroxide technology, applied in chemical instruments and methods, alkali metal aluminate/alumina/aluminum hydroxide preparation, inorganic chemistry and other directions, can solve the complex preparation process of ultra-fine crystal seeds, Industrial production is difficult to control and other problems, to achieve the effect of low cost, simple method and high whiteness

Inactive Publication Date: 2020-05-12
HEFEI ZHONGKE FLAME RETARDANT NEW MATERIAL
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Above-mentioned two kinds of ultrafine aluminum hydroxide production methods, the preparation process of its ultrafine seed crystal is more complicated, and industrial production is difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Embodiment 1 provides a kind of decomposition method and prepares the method for high-purity superfine aluminum hydroxide flame retardant, and production process comprises the following steps:

[0057] (1) Preparation of aluminum hydroxide seed crystals: the caustic ratio αk of sodium aluminate refining solution by sintering method is 1.6, the alumina content is 90g / L, cool to 25°C through a plate heat exchanger, add white mud washing solution until refined The caustic ratio αk of the liquid is 1.4, and the alumina content is 60g / L. Then, paddle stirring is used in the carbon separation tank, and CO with a concentration of 25% is introduced. 2 gas, the decomposition time is 40min, and finally a gelatinous aluminum hydroxide slurry with a pH of 9 is obtained.

[0058] (2) Decomposition method to prepare aluminum hydroxide slurry: adding the gelatinous aluminum hydroxide glue solution prepared in step (1) to caustic ratio αk is 1.6, and alumina content is sintering method...

Embodiment 2

[0064] Embodiment 2 provides a method for preparing high-purity ultrafine aluminum hydroxide flame retardant by decomposition method, and the production process includes the following steps:

[0065] (1) Preparation of aluminum hydroxide seed crystals: the caustic ratio αk of the sodium aluminate refining solution by sintering method is 1.4, the alumina content is 80g / L, cool to 50°C through a plate heat exchanger, add white mud washing solution until refined The caustic ratio αk of the liquid is 1.3, the alumina content is 40g / L, and then a paddle-type stirring is used in the carbon separation tank, and CO with a concentration of 10% is introduced. 2 gas, the decomposition time was 30min, and finally a gelatinous aluminum hydroxide slurry with a pH of 8.5 was obtained.

[0066] (2) Preparation of aluminum hydroxide slurry by decomposition method: the gelatinous aluminum hydroxide glue solution prepared in step (1) is added to a caustic ratio α k of 1.4, and the sintering meth...

Embodiment 3

[0072] Embodiment 3 provides a method for preparing high-purity ultrafine aluminum hydroxide flame retardant by decomposition method, and the production process includes the following steps:

[0073] (1) Preparation of aluminum hydroxide seed crystals: the caustic ratio αk of sodium aluminate refining solution by sintering method is 1.7, the alumina content is 120g / L, cool to 10°C through a plate heat exchanger, add white mud washing solution until refined The caustic ratio αk of the liquid is 1.5, the alumina content is 80g / L, and then a paddle-type stirring is used in the carbon separation tank, and CO with a concentration of 40% is introduced. 2 gas, the decomposition time is 50min, and finally a gelatinous aluminum hydroxide slurry with a pH of 10.5 is obtained.

[0074] (2) Decomposition method to prepare aluminum hydroxide slurry: adding the gelatinous aluminum hydroxide glue solution prepared in step (1) to caustic ratio α k is 1.7, and the sintering method sodium alumi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
whitenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation methods of aluminum hydroxide flame retardants, in particular to a method for preparing a high-purity superfine aluminum hydroxide flame retardant by a decomposition method. The production process of the aluminum hydroxide flame retardant comprises the following steps: (1) preparation of an aluminum hydroxide seed crystal: cooling a Bayerprocess or sintering process sodium aluminate refined solution, and carrying out carbon decomposition in a carbon decomposition tank to form a gel-like aluminum hydroxide gel slurry; (2) preparationof aluminum hydroxide slurry through decomposition: adding the gelatinous aluminum hydroxide glue solution prepared in the step (1) into a Bayer process or sintering process sodium aluminate refined solution, and stirring and decomposing the mixture in a seed precipitation tank to obtain ultrafine aluminum hydroxide slurry; (3) solid-liquid separation on the aluminum hydroxide slurry: separating the superfine strong aluminum oxide glue solution prepared in the step (2) through a filter to obtain a filter cake; and (4) drying: carrying out paddle type drying and rotary flash evaporation drying.The purity of the aluminum hydroxide flame retardant prepared by the preparation method is not lower than 99%, the whiteness is not lower than 98%, and the average particle size is 1-2 [mu] m.

Description

technical field [0001] The invention relates to the technical field of preparation methods of aluminum hydroxide flame retardants, in particular to a method for preparing high-purity ultrafine aluminum hydroxide flame retardants by decomposition. Background technique [0002] Due to the good thermal stability of ultra-fine aluminum hydroxide and no secondary pollution during combustion, it is a green flame retardant product. In recent years, the demand for flame retardant ultra-fine aluminum hydroxide has increased sharply at home and abroad, and the research and development cost is low. The ultra-fine aluminum hydroxide flame retardant has broad market application prospects and economic benefits. At present, the preparation of ultra-fine aluminum hydroxide mainly includes mechanical pulverization and chemical methods. In order to reverse the aggregation of ultra-fine aluminum hydroxide, dispersant is often added to the ultra-fine aluminum hydroxide before drying to prevent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01F7/14C09K21/02
CPCC01F7/14C01F7/142C01F7/148C01P2004/61C01P2006/60C01P2006/80C09K21/02
Inventor 王周王立贵
Owner HEFEI ZHONGKE FLAME RETARDANT NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap