Gel cement, associated polymer and preparation method

A technology of associating polymers and cement, applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of poor construction safety, large amount of plugging grout, and insufficient temperature resistance, etc., to achieve good anti-corrosion Water dilution ability, high temperature resistance and high temperature gelation ability, fast dissolution effect

Pending Publication Date: 2020-06-12
SICHUAN GUANGYA POLYMER CHEM +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing plugging materials mainly include: 1) polymers, resins, and sediments, which have the problems of low strength and insufficient temperature resistance after the plugging slurry is consolidated; 2) cement plugging, which is easily damaged by water Flush release, poor water intrusion resistance, and poor construction safety are technical difficulties; the plugging agent cannot effectively stay in the plugging layer, and the plugging agent has been replaced to the target layer before it is solidified and is lost, resulting in plugging slurry injection Disadvantages of large quantity and long construction time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gel cement, associated polymer and preparation method
  • Gel cement, associated polymer and preparation method
  • Gel cement, associated polymer and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A gel cement:

[0039] It includes: 2.6g of associative polymer and 200g of cement; the cement is Sichuan Jiahua superfine cement with a particle size of 20 microns.

[0040] The aforementioned associative polymers:

[0041] In mole percent, the associative polymer consists of 35% acrylamide, 15% sodium acrylate, 12% N-vinylpyrrolidone, 30% 2-acrylamido-2-methylpropanesulfonic acid and 8 hydrophobic monomers. The reaction monomer polymerization reaction of % composition is obtained; Described hydrophobic monomer is the compound shown in formula I;

[0042]

[0043] Among them, n=11; X - for chloride ions.

[0044] The preparation method of above-mentioned gel cement:

[0045] It comprises: adding the associative polymer and the cement into a mixer and fully stirring, and mixing evenly to prepare the obtained product.

[0046] The preparation method of above-mentioned associative polymer:

[0047] include:

[0048] The sodium hydroxide adjustment system adjusts t...

Embodiment 2

[0054] The difference between this embodiment and embodiment 1 is only:

[0055] A gel cement:

[0056] Comprising: 2.2g of associative polymer and 200g of cement; the cement is Sichuan Jiahua superfine cement (commercially available) with a particle size of 20 microns.

Embodiment 3

[0058] The difference between this embodiment and embodiment 1 is only:

[0059] A gel cement:

[0060] Comprising: 3g of associative polymer and 200g of cement; the cement is Sichuan Jiahua G grade oil well cement (commercially available).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses gel cement, an associated polymer and a preparation method. The gel cement comprises the following components in parts by weight: 0.6-2 parts of associated polymer and 100 parts of cement; wherein the associated polymer is prepared by carrying out polymerization reaction on reaction monomers consisting of 10 to 50 percent of acrylamide, 10 to 20 percent of sodium acrylate,10 to 20 percent of N-vinyl-2-pyrrolidone, 20 to 50 percent of 2-acrylamido-2-methylpropanesulfonic acid and 5 to 10 percent of a hydrophobic monomer in percentage by mole; the gel cement has high-temperature-resistant gelling capacity, the high-temperature gelling phenomenon can be effectively eliminated, and after the gel cement is prepared into cement paste, the paste is high in structural force and has excellent anti-flushing capacity and residence capacity.

Description

technical field [0001] The invention relates to the technical field of chemical engineering, in particular to a gel cement, an association polymer and a preparation method. Background technique [0002] Lost circulation refers to the leakage of various working fluids, including mud, cement slurry, completion fluid and other liquids, into the formation under the action of pressure difference during special downhole operations such as drilling, cementing, testing or workover. A downhole complex situation is one of the most common technical problems in downhole engineering. [0003] In order to solve the problem of well leakage, the main idea in the existing technology is to inject a plugging material into the leaky layer to seal the leaky layer, thereby solving the plugging problem. At present, the existing plugging materials mainly include: 1) polymers, resins, and sediments, which have the problems of low strength and insufficient temperature resistance after the plugging s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B28/04C04B12/00C09K8/467C08F220/56C08F220/06C08F226/10C08F220/58C04B111/72
CPCC04B12/00C04B28/02C04B28/04C04B2111/72C04B2201/20C04B2201/50C08F220/56C08F220/58C09K8/467C04B24/2688
Inventor 郭拥军罗平亚罗勇金诚胡俊
Owner SICHUAN GUANGYA POLYMER CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com