A kind of black finishing varnish for automobile and its preparation method and application

A technology for finishing varnishes and automobiles, applied in the field of varnishes, can solve problems such as insufficient blackness of paint films, achieve high gloss, prevent excessive oven temperature, and have excellent appearance

Active Publication Date: 2022-03-22
NIPPON PAINT GUANGZHOU
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] An object of the present invention is to provide a black finish varnish for automobiles, which is suitable for matching with water-based and oil-based paints, can effectively improve the blackness of the vehicle body, make the vehicle body visually blacker and bluer, and has a sag limit and needle High pore limit, good appearance, good adhesion for high temperature recoating, excellent acid resistance and weather resistance, etc., which solves the problem of insufficient blackness of the paint film in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of black finishing varnish for automobile and its preparation method and application
  • A kind of black finishing varnish for automobile and its preparation method and application
  • A kind of black finishing varnish for automobile and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] In a specific embodiment, the preparation method of the above-mentioned automotive yellowing-resistant varnish for sealing strips includes:

[0046] (1) Mix 0.5-1.0 parts of ultraviolet absorber, 0.4-1.0 parts of light stabilizer and 4-8 parts of mixed solvent to obtain the first mixture; 3-6 parts of reactive microgel, 2-5 parts Mix 1-2 parts of butyl etherified amino resin with 4-10 parts of mixed solvent to obtain the second mixture; mix 1-2 parts of xylene with 0.1-0.5 parts of degassing agent to obtain the third mixture; mix 40-60 parts of thermosetting acrylic resin , 15-25 parts of butylated amino resin, 4-10 parts of epoxy modified thermosetting acrylic resin, 0.1-0.5 parts of antioxidant additives, 0.1-1 parts of leveling agent, 0.1-1.0 parts of defoamer, 0.4- 0.8 parts of black pulp were mixed evenly to obtain the fourth mixture;

[0047] (2) Add the first mixture, the second mixture, and the third mixture to the fourth mixture in turn under stirring, and aft...

Embodiment 1

[0066] A kind of black finishing varnish for automobile, formula as shown in table 1

[0067] The formula of varnish in table 1 embodiment 1

[0068] serial number components number of copies 1 S-150 solvent oil 5 2 THASORB UV-234 0.9 3 RIASORB UV-292 0.45 4 S-150 solvent oil 2 5 Butanol 2 6 Trimethyl orthoacetate 1 7 AZS-1230 5 8 CYMEL 1158 2.5 9 Xylene 1 10 GK-19 0.2 11 Setalux 1766VB-64 54 12 CYMEL 1158 17.5 13 ACS-1284 6 14 BYK 355 0.5 15 BYK-323 0.1 16 BYK 051 0.3 17 SP M-350-1(T)9904A BLACK UDP 0.4 18 BYK ES80 0.15 19 S-100# solvent oil 1

[0069] The preparation method of the black finish varnish for automobile of the present embodiment may further comprise the steps:

[0070] The first step is to take a steam jacketed cylinder, add component 1 and ground the container for 5 minutes, add component 2 to the container, start...

Embodiment 2

[0076] A kind of black finishing varnish for automobile, formula as shown in table 2.

[0077] The formula of varnish in table 2 embodiment 2

[0078] serial number components number of copies 1 S-150 solvent oil 4 2 CHISORB 234 0.9 3 TINUVIN 292 0.5 4 S-150 solvent oil 1.8 5 Butanol 1.8 6 Trimethyl orthoacetate 1.1 7 AZS-617 3 8 UVAN 20SE-60 3 9 Xylene 1.2 10 Benzoin GK-19 0.25 11 Setalux 1766VB-64 50 12 UVAN 20SE-60 23.5 13 ACS-1017 5 14 TEGO FLOW 370 0.45 15 TEGO FLOW 425 0.2 16 DISPARLON OX-750 0.15 17 SP M-70(T)BLACK FW-200P(10PWC) 0.5 18 Methanol 2.5 19 S-100# solvent oil 0.15

[0079] The preparation method of the black finish varnish for automobile of the present embodiment may further comprise the steps:

[0080] The first step is to take a steam jacketed cylinder, add component 1 and ground the container for 5 minutes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
particle diameteraaaaaaaaaa
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses a black finish varnish for automobiles, which comprises, in parts by weight: 40-60 parts of thermosetting acrylic resin, 15-30 parts of butylated amino resin, and 4-10 parts of epoxy-modified thermosetting acrylic resin , 3-6 parts of reactive microgel, 0.1-0.5 parts of antioxidant additives, 0.5-1.0 parts of UV absorbers, 0.4-1.0 parts of light stabilizers, 0.1-1.0 parts of leveling agents, 0.1-0.5 parts of Air agent, 0.1-1.0 parts of defoamer, 0.1-2.5 parts of conductive agent, 0.4-0.8 parts of black paste, 1-2 parts of xylene, 10-20 parts of mixed solvent. The varnish can effectively improve the blackness of the car body and has an excellent appearance. It is also suitable for water-based and oil-based paint systems to meet the needs of upgrading automotive color consumption; and the varnish has a higher pinhole limit, sagging limit and good Excellent high temperature repeated adhesion; in addition, it also has excellent acid resistance and weather resistance.

Description

technical field [0001] The present invention relates to the field of varnishes. More specifically, it relates to a black finish varnish for automobiles and its preparation method and application. Background technique [0002] According to the "BASF Automotive Original Paint Color Report" released by BASF's Coatings Division, the color distribution of the global automotive market in 2018 was analyzed. From a global perspective, achromatic colors such as white, black, gray and silver are still the main colors on the road, and vehicles using these colors account for 80% of the entire car production. Among them, black, as a traditional color, gives people a feeling of solemnity, dignity and seriousness, and has always been the most popular color for official vehicles. For cars, the more high-end the car, the more monotonous the color, and most of them are black. The black color is solemn and full of style, which can highlight the identity. The higher the blackness, the higher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D161/32
CPCC09D133/04C08L2205/035C08L2205/025C08L61/32C08L33/04
Inventor 林业伟夏天渊郭峻峰董明琪张睿
Owner NIPPON PAINT GUANGZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap